- W102768809 abstract "This study evaluated the tensile bond strength of repaired amalgams and compared the degree of microleakage. Amalgam (Cavex avalloy) was condensed into plastic tubes (3 mm in diameter, 10 mm in height) to the half-length. After storage in water at 37 degrees C for two days, the remaining parts of tubes were filled with amalgam (A), cavity varnish (CV)+A, Liner Bond 2V (LB2V)+A, 3M Opal Luting Cement (3MOLC)+A, Panavia F(PF)+A, Metabond(MB)+A, Fuji BondLC(FB)+A, HytacOSB(HOSB)+Hytac Aplitip (H), Liner Bond2V+Clearfil AP-X(CAP). The bond strengths for 15 samples of each restoration group were determined. For the microleakage study, MOD cavities of 90 extracted human premolars were used. The distal half of cavities were filled with amalgam. After storage in water at 37 degrees C for two days, the mesial half of the cavities were filled to simulate a clinical repair. The repair was placed using the procedures applied in the bond strength study. The teeth were stained with basic fuchsine (0.5%), sectioned and evaluated for dye penetration. In both parts of study, the data were analyzed by ANOVA and Duncan's multiple range tests. Bond strength values (MPa) were: A+PF+A 3.84+/-1.08, A+LB2V+A 3.15+/-0.97, A+LB2V+CAP 3.05+/-0.53, A+MB+A 2.86+/-0.88, A+HOSB+H 2.58+/-0.51, A+3MOLC+A 2.11+/-0.75, A+FB+A 0.68+/-0.59. The repaired A+A and A+CV+A groups were separated before testing. The A+PF+A group showed the highest bond strength (p<0.05). Microleakage in the cervical margins of repaired restorations was lower in the amalgam groups than microleakage in the resin composite and compomer groups. PF, MB, 3MOLC and FB performed better at the amalgam repair interface. The A+LB2V+A group showed no microleakage at both the occlusal and gingival test regions." @default.
- W102768809 created "2016-06-24" @default.
- W102768809 creator A5017346990 @default.
- W102768809 creator A5051490466 @default.
- W102768809 creator A5052125968 @default.
- W102768809 creator A5065345274 @default.
- W102768809 date "2002-04-05" @default.
- W102768809 modified "2023-10-17" @default.
- W102768809 title "Amalgam repair: evaluation of bond strength and microleakage." @default.
- W102768809 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/11931139" @default.
- W102768809 hasPublicationYear "2002" @default.
- W102768809 type Work @default.
- W102768809 sameAs 102768809 @default.
- W102768809 citedByCount "10" @default.
- W102768809 countsByYear W1027688092012 @default.
- W102768809 countsByYear W1027688092013 @default.
- W102768809 countsByYear W1027688092016 @default.
- W102768809 countsByYear W1027688092019 @default.
- W102768809 crossrefType "journal-article" @default.
- W102768809 hasAuthorship W102768809A5017346990 @default.
- W102768809 hasAuthorship W102768809A5051490466 @default.
- W102768809 hasAuthorship W102768809A5052125968 @default.
- W102768809 hasAuthorship W102768809A5065345274 @default.
- W102768809 hasConcept C112950240 @default.
- W102768809 hasConcept C147789679 @default.
- W102768809 hasConcept C159096172 @default.
- W102768809 hasConcept C159985019 @default.
- W102768809 hasConcept C17525397 @default.
- W102768809 hasConcept C185592680 @default.
- W102768809 hasConcept C192562407 @default.
- W102768809 hasConcept C199343813 @default.
- W102768809 hasConcept C2779227376 @default.
- W102768809 hasConcept C2781448156 @default.
- W102768809 hasConcept C28667232 @default.
- W102768809 hasConcept C51795115 @default.
- W102768809 hasConcept C68928338 @default.
- W102768809 hasConcept C71924100 @default.
- W102768809 hasConceptScore W102768809C112950240 @default.
- W102768809 hasConceptScore W102768809C147789679 @default.
- W102768809 hasConceptScore W102768809C159096172 @default.
- W102768809 hasConceptScore W102768809C159985019 @default.
- W102768809 hasConceptScore W102768809C17525397 @default.
- W102768809 hasConceptScore W102768809C185592680 @default.
- W102768809 hasConceptScore W102768809C192562407 @default.
- W102768809 hasConceptScore W102768809C199343813 @default.
- W102768809 hasConceptScore W102768809C2779227376 @default.
- W102768809 hasConceptScore W102768809C2781448156 @default.
- W102768809 hasConceptScore W102768809C28667232 @default.
- W102768809 hasConceptScore W102768809C51795115 @default.
- W102768809 hasConceptScore W102768809C68928338 @default.
- W102768809 hasConceptScore W102768809C71924100 @default.
- W102768809 hasIssue "2" @default.
- W102768809 hasLocation W1027688091 @default.
- W102768809 hasOpenAccess W102768809 @default.
- W102768809 hasPrimaryLocation W1027688091 @default.
- W102768809 hasRelatedWork W1978058729 @default.
- W102768809 hasRelatedWork W2128170549 @default.
- W102768809 hasRelatedWork W2382533574 @default.
- W102768809 hasRelatedWork W2412629347 @default.
- W102768809 hasRelatedWork W2461337726 @default.
- W102768809 hasRelatedWork W2729932191 @default.
- W102768809 hasRelatedWork W2795554382 @default.
- W102768809 hasRelatedWork W2916472162 @default.
- W102768809 hasRelatedWork W3122552578 @default.
- W102768809 hasRelatedWork W4220974300 @default.
- W102768809 hasVolume "27" @default.
- W102768809 isParatext "false" @default.
- W102768809 isRetracted "false" @default.
- W102768809 magId "102768809" @default.
- W102768809 workType "article" @default.