- W103804826 abstract "Tests were carried out with titarium IMP-1A (technically pure Ti prepared by calcium hydride method) and IMP-7 (Ti alloy with 3% Al and 2% U) subjected to plastic deformation. The specimens were annealed at300, 350, and 400 deg C in order to determine the time and temperature effects. The strength limit with slightly lowered plasticity was reached at 20% deformation at which point the mechanical strength of IMP-1A increased from 67.8 to 90.8 kg/mm/sup 2/ and that of IMP-7 from 88 to 100.5 kg/mm/sup 2/. The sharpest drop in plasticity was observed at 10% deformation. The improved strength of the metal is retained at 300 deg C and it slowly weakens and acquires greater plasticity at 350 and 400 deg C. (R.V.J.)" @default.
- W103804826 created "2016-06-24" @default.
- W103804826 creator A5027625508 @default.
- W103804826 creator A5031902247 @default.
- W103804826 date "1959-10-01" @default.
- W103804826 modified "2023-09-27" @default.
- W103804826 title "INCREASE OF THE STRENGTH OF TITANIUM BASE ALLOYS DURING COLD PLASTIC DEFORMATION" @default.
- W103804826 hasPublicationYear "1959" @default.
- W103804826 type Work @default.
- W103804826 sameAs 103804826 @default.
- W103804826 citedByCount "0" @default.
- W103804826 crossrefType "journal-article" @default.
- W103804826 hasAuthorship W103804826A5027625508 @default.
- W103804826 hasAuthorship W103804826A5031902247 @default.
- W103804826 hasConcept C159985019 @default.
- W103804826 hasConcept C191897082 @default.
- W103804826 hasConcept C192562407 @default.
- W103804826 hasConcept C19474535 @default.
- W103804826 hasConcept C204366326 @default.
- W103804826 hasConcept C2780026712 @default.
- W103804826 hasConcept C40241539 @default.
- W103804826 hasConcept C506065880 @default.
- W103804826 hasConcept C79186407 @default.
- W103804826 hasConcept C8953137 @default.
- W103804826 hasConceptScore W103804826C159985019 @default.
- W103804826 hasConceptScore W103804826C191897082 @default.
- W103804826 hasConceptScore W103804826C192562407 @default.
- W103804826 hasConceptScore W103804826C19474535 @default.
- W103804826 hasConceptScore W103804826C204366326 @default.
- W103804826 hasConceptScore W103804826C2780026712 @default.
- W103804826 hasConceptScore W103804826C40241539 @default.
- W103804826 hasConceptScore W103804826C506065880 @default.
- W103804826 hasConceptScore W103804826C79186407 @default.
- W103804826 hasConceptScore W103804826C8953137 @default.
- W103804826 hasLocation W1038048261 @default.
- W103804826 hasOpenAccess W103804826 @default.
- W103804826 hasPrimaryLocation W1038048261 @default.
- W103804826 hasRelatedWork W1978137558 @default.
- W103804826 hasRelatedWork W2015994835 @default.
- W103804826 hasRelatedWork W2018077044 @default.
- W103804826 hasRelatedWork W2026564040 @default.
- W103804826 hasRelatedWork W2032963083 @default.
- W103804826 hasRelatedWork W2160274212 @default.
- W103804826 hasRelatedWork W2210660418 @default.
- W103804826 hasRelatedWork W2559820755 @default.
- W103804826 hasRelatedWork W2794355740 @default.
- W103804826 hasRelatedWork W2900157187 @default.
- W103804826 hasRelatedWork W2951668274 @default.
- W103804826 hasRelatedWork W3047726638 @default.
- W103804826 hasRelatedWork W3139612109 @default.
- W103804826 hasRelatedWork W1526234485 @default.
- W103804826 hasRelatedWork W2529616030 @default.
- W103804826 hasRelatedWork W2828927315 @default.
- W103804826 hasRelatedWork W2854811939 @default.
- W103804826 hasRelatedWork W2878049338 @default.
- W103804826 hasRelatedWork W2882610219 @default.
- W103804826 hasRelatedWork W978561729 @default.
- W103804826 isParatext "false" @default.
- W103804826 isRetracted "false" @default.
- W103804826 magId "103804826" @default.
- W103804826 workType "article" @default.