- W1185484015 abstract "Low-carbon (0.08 wt% C) steel has been subjected to three different heat treatments to obtain dual-phase steels with different microstructures. An understanding of structure–property was established through tensile tests, in conjunction with scanning electron microscope and transmission electron microscope. The results show that the steel after intermediate quenching (IQ) consisting of fine and fibrous martensite exhibited the intermediate strength, highest elongation and the best comprehensive performance of mechanical properties, whereas the steel subjected to intercritical annealing (IA) produced a network martensite along ferrite grain boundaries, having the lowest strength and intermediate elongation. Besides, step quenching (SQ) resulted in a coarse and blocky ferrite–martensite microstructure showing the worst mechanical properties of the three different heat-treatment conditions. The strain-hardening behavior was studied through the modified Crussard–Jaoul model, indicating two stages of strain-hardening behavior for all three samples. The highest magnitude of strain-hardening ability was obtained by IQ annealing routes. The analysis of the fractured surface revealed that ferrite/martensite interfaces are the most susceptible for microvoid nucleation. However, martensite microcracks were also observed in SQ sample, and the microvoids are nucleated within the ferrite grain in IA sample as well. The variations in strength, elongation, strain-hardening behavior and fracture mechanism of the steel with different heat-treatment schedules were further discussed in relation to the microstructural features." @default.
- W1185484015 created "2016-06-24" @default.
- W1185484015 creator A5083642249 @default.
- W1185484015 creator A5084723540 @default.
- W1185484015 creator A5086568371 @default.
- W1185484015 date "2015-08-15" @default.
- W1185484015 modified "2023-10-06" @default.
- W1185484015 title "Effect of Heat-Treatment Schedule on the Microstructure and Mechanical Properties of Cold-Rolled Dual-Phase Steels" @default.
- W1185484015 cites W1827105872 @default.
- W1185484015 cites W1963561744 @default.
- W1185484015 cites W1964213665 @default.
- W1185484015 cites W1967969063 @default.
- W1185484015 cites W1968176185 @default.
- W1185484015 cites W1968928483 @default.
- W1185484015 cites W1971476145 @default.
- W1185484015 cites W1974501822 @default.
- W1185484015 cites W1975390225 @default.
- W1185484015 cites W1986696576 @default.
- W1185484015 cites W1990481039 @default.
- W1185484015 cites W1996355194 @default.
- W1185484015 cites W2001988687 @default.
- W1185484015 cites W2007912308 @default.
- W1185484015 cites W2008685514 @default.
- W1185484015 cites W2015833966 @default.
- W1185484015 cites W2021157314 @default.
- W1185484015 cites W2021907105 @default.
- W1185484015 cites W2022130505 @default.
- W1185484015 cites W2022481231 @default.
- W1185484015 cites W2035119515 @default.
- W1185484015 cites W2036893375 @default.
- W1185484015 cites W2039934129 @default.
- W1185484015 cites W2040756888 @default.
- W1185484015 cites W2048757205 @default.
- W1185484015 cites W2051938100 @default.
- W1185484015 cites W2057960590 @default.
- W1185484015 cites W2060844227 @default.
- W1185484015 cites W2061026000 @default.
- W1185484015 cites W2074953829 @default.
- W1185484015 cites W2079967968 @default.
- W1185484015 cites W2080246395 @default.
- W1185484015 cites W2085034486 @default.
- W1185484015 cites W2092388064 @default.
- W1185484015 cites W2093036852 @default.
- W1185484015 cites W2093898775 @default.
- W1185484015 cites W2098373853 @default.
- W1185484015 cites W2123280956 @default.
- W1185484015 cites W2129860841 @default.
- W1185484015 cites W2154208079 @default.
- W1185484015 cites W2163669714 @default.
- W1185484015 doi "https://doi.org/10.1007/s40195-015-0305-x" @default.
- W1185484015 hasPublicationYear "2015" @default.
- W1185484015 type Work @default.
- W1185484015 sameAs 1185484015 @default.
- W1185484015 citedByCount "28" @default.
- W1185484015 countsByYear W11854840152016 @default.
- W1185484015 countsByYear W11854840152017 @default.
- W1185484015 countsByYear W11854840152018 @default.
- W1185484015 countsByYear W11854840152019 @default.
- W1185484015 countsByYear W11854840152020 @default.
- W1185484015 countsByYear W11854840152021 @default.
- W1185484015 countsByYear W11854840152022 @default.
- W1185484015 countsByYear W11854840152023 @default.
- W1185484015 crossrefType "journal-article" @default.
- W1185484015 hasAuthorship W1185484015A5083642249 @default.
- W1185484015 hasAuthorship W1185484015A5084723540 @default.
- W1185484015 hasAuthorship W1185484015A5086568371 @default.
- W1185484015 hasBestOaLocation W11854840152 @default.
- W1185484015 hasConcept C112950240 @default.
- W1185484015 hasConcept C156413551 @default.
- W1185484015 hasConcept C159551322 @default.
- W1185484015 hasConcept C159985019 @default.
- W1185484015 hasConcept C18747287 @default.
- W1185484015 hasConcept C191897082 @default.
- W1185484015 hasConcept C192562407 @default.
- W1185484015 hasConcept C26771246 @default.
- W1185484015 hasConcept C2777855556 @default.
- W1185484015 hasConcept C2779227376 @default.
- W1185484015 hasConcept C2779344738 @default.
- W1185484015 hasConcept C33947775 @default.
- W1185484015 hasConcept C37210646 @default.
- W1185484015 hasConcept C44255700 @default.
- W1185484015 hasConcept C87976508 @default.
- W1185484015 hasConceptScore W1185484015C112950240 @default.
- W1185484015 hasConceptScore W1185484015C156413551 @default.
- W1185484015 hasConceptScore W1185484015C159551322 @default.
- W1185484015 hasConceptScore W1185484015C159985019 @default.
- W1185484015 hasConceptScore W1185484015C18747287 @default.
- W1185484015 hasConceptScore W1185484015C191897082 @default.
- W1185484015 hasConceptScore W1185484015C192562407 @default.
- W1185484015 hasConceptScore W1185484015C26771246 @default.
- W1185484015 hasConceptScore W1185484015C2777855556 @default.
- W1185484015 hasConceptScore W1185484015C2779227376 @default.
- W1185484015 hasConceptScore W1185484015C2779344738 @default.
- W1185484015 hasConceptScore W1185484015C33947775 @default.
- W1185484015 hasConceptScore W1185484015C37210646 @default.
- W1185484015 hasConceptScore W1185484015C44255700 @default.
- W1185484015 hasConceptScore W1185484015C87976508 @default.
- W1185484015 hasIssue "9" @default.