- W1196306216 abstract "Hot corrosion tests of alumina (Al2O3) and carbon silicate (SiC) ceramics exposed to KCl–NaCl molten salt were performed at high temperatures (700 and 800°C) and for long times (100–400 h) in order to improve the reliability of tanks and heat exchangers for molten salts. The samples were tested by being immersed in molten salt and under salt vapor. Basic corrosion data, such as the corrosion product, surface conditions, and 4-point bending strength were acquired. In the case of the Al2O3 ceramics, neither corrosion products nor a significant roughness of the Al2O3 particles was observed. In the case of the SiC ceramics, the observed corrosion product was SiO2, and considerable roughness was found at the surface of the immersed sample. The surface roughness became more pronounced as the corrosion temperature and time increased. On the other hand, a SiO2 thin film was observed on the surface of the sample that was exposed to salt vapor. A significant strength decrease was not observed for the two types of Al2O3 and SiC ceramics. Therefore, Al2O3 ceramics are expected to represent a suitable container material for molten salts. On the other hand, predicting the lifetime of the material is necessary if SiC ceramics are intended to be used." @default.
- W1196306216 created "2016-06-24" @default.
- W1196306216 creator A5027839715 @default.
- W1196306216 creator A5041820338 @default.
- W1196306216 creator A5055874360 @default.
- W1196306216 date "2015-01-01" @default.
- W1196306216 modified "2023-09-26" @default.
- W1196306216 title "Hot corrosion of Al<sub>2</sub>O<sub>3</sub> and SiC ceramics by KCl–NaCl molten salt" @default.
- W1196306216 cites W1978421279 @default.
- W1196306216 cites W1990424379 @default.
- W1196306216 cites W1992079615 @default.
- W1196306216 cites W2012966657 @default.
- W1196306216 cites W2054521880 @default.
- W1196306216 cites W2055214541 @default.
- W1196306216 cites W2082801457 @default.
- W1196306216 cites W2097894952 @default.
- W1196306216 cites W2114198429 @default.
- W1196306216 cites W2118180970 @default.
- W1196306216 cites W2316930862 @default.
- W1196306216 cites W2512689607 @default.
- W1196306216 cites W2606211977 @default.
- W1196306216 doi "https://doi.org/10.2109/jcersj2.123.685" @default.
- W1196306216 hasPublicationYear "2015" @default.
- W1196306216 type Work @default.
- W1196306216 sameAs 1196306216 @default.
- W1196306216 citedByCount "13" @default.
- W1196306216 countsByYear W11963062162017 @default.
- W1196306216 countsByYear W11963062162018 @default.
- W1196306216 countsByYear W11963062162020 @default.
- W1196306216 countsByYear W11963062162021 @default.
- W1196306216 countsByYear W11963062162022 @default.
- W1196306216 countsByYear W11963062162023 @default.
- W1196306216 crossrefType "journal-article" @default.
- W1196306216 hasAuthorship W1196306216A5027839715 @default.
- W1196306216 hasAuthorship W1196306216A5041820338 @default.
- W1196306216 hasAuthorship W1196306216A5055874360 @default.
- W1196306216 hasBestOaLocation W11963062161 @default.
- W1196306216 hasConcept C107365816 @default.
- W1196306216 hasConcept C134132462 @default.
- W1196306216 hasConcept C147789679 @default.
- W1196306216 hasConcept C159985019 @default.
- W1196306216 hasConcept C178405089 @default.
- W1196306216 hasConcept C185592680 @default.
- W1196306216 hasConcept C191897082 @default.
- W1196306216 hasConcept C192562407 @default.
- W1196306216 hasConcept C20625102 @default.
- W1196306216 hasConcept C2776371256 @default.
- W1196306216 hasConcept C2778353533 @default.
- W1196306216 hasConcept C71039073 @default.
- W1196306216 hasConceptScore W1196306216C107365816 @default.
- W1196306216 hasConceptScore W1196306216C134132462 @default.
- W1196306216 hasConceptScore W1196306216C147789679 @default.
- W1196306216 hasConceptScore W1196306216C159985019 @default.
- W1196306216 hasConceptScore W1196306216C178405089 @default.
- W1196306216 hasConceptScore W1196306216C185592680 @default.
- W1196306216 hasConceptScore W1196306216C191897082 @default.
- W1196306216 hasConceptScore W1196306216C192562407 @default.
- W1196306216 hasConceptScore W1196306216C20625102 @default.
- W1196306216 hasConceptScore W1196306216C2776371256 @default.
- W1196306216 hasConceptScore W1196306216C2778353533 @default.
- W1196306216 hasConceptScore W1196306216C71039073 @default.
- W1196306216 hasIssue "1440" @default.
- W1196306216 hasLocation W11963062161 @default.
- W1196306216 hasOpenAccess W1196306216 @default.
- W1196306216 hasPrimaryLocation W11963062161 @default.
- W1196306216 hasRelatedWork W2025687592 @default.
- W1196306216 hasRelatedWork W2281145519 @default.
- W1196306216 hasRelatedWork W2394131053 @default.
- W1196306216 hasRelatedWork W2789571739 @default.
- W1196306216 hasRelatedWork W2944045227 @default.
- W1196306216 hasRelatedWork W2947582800 @default.
- W1196306216 hasRelatedWork W2971956475 @default.
- W1196306216 hasRelatedWork W3096164317 @default.
- W1196306216 hasRelatedWork W3097783663 @default.
- W1196306216 hasRelatedWork W887366579 @default.
- W1196306216 hasVolume "123" @default.
- W1196306216 isParatext "false" @default.
- W1196306216 isRetracted "false" @default.
- W1196306216 magId "1196306216" @default.
- W1196306216 workType "article" @default.