- W125792197 abstract "AbstractThe constant strive for improved efficiency and lower-cost industrial processes often results in progressively higher temperatures and more aggressive environments. High- temperature corrosion is a well-known problem in biomass- and waste-fired boilers and is one of the obstacles to overcome in achieving a more sustainable society. Alkali- and chlorine- induced corrosion of chromia-forming alloys has been studied by several researchers. However, the literature is scarce on how alumina forming-alloys, e.g. FeCrAl alloys, perform in such an aggressive environment. In this thesis, the KCl-induced corrosion of FeCrAl alloys is studied through well-planned laboratory exposures, detailed analyses and corrosion tests in a full scale waste-fired power boiler. In the laboratory, the effect of adding small amounts of KCl was investigated on polished FeCrAl samples in O2 or O2 + H2O environments up to 168 hours at 600 °C. Pre-formed alumina scales were prepared on the alloy substrate through pre-oxidation at various conditions. The pre-treated samples were subsequently exposed to O2 + H2O + KCl in order to investigate their corrosion resistance. The samples were analysed using TGA, SEM/EDX, XRD, IC, AES, SIMS, BIB cross sections and STEM/EDX. In order to evaluate the validity of the findings in the laboratory studies, corrosion tests were carried out in a full-scale combined heat and power (CHP) boiler.The study showed that KCl-induced corrosion caused a rapidly growing iron-chromium-rich oxide to form in O2 and O2 + H2O environments at 600 °C. Chromate formation and alloy chlorination were found to initiate the formation of a non-protective oxide scale. Alloy chlorination was greater in O2 than in O2 + H2O resulting in a more porous scale with poor adhesion to the alloy substrate. Pre-treating the alloy prior to exposure to O2 + H2O + KCl mitigated the corrosion, since alumina, itself, is rather inert towards corrosion. However, the corrosion started locally, most likely at flaws/cracks in the alumina scale and then spread laterally until the entire surface suffered from breakaway corrosion. Similar results were obtained in the corrosion tests in the waste-fired boiler. The pre-formed alumina scale failed after only 24 hours in the boiler at both 600 and 700 °C." @default.
- W125792197 created "2016-06-24" @default.
- W125792197 creator A5084723557 @default.
- W125792197 date "2014-01-01" @default.
- W125792197 modified "2023-09-28" @default.
- W125792197 title "High Temperature Oxidation and Chlorination of FeCrAl alloys" @default.
- W125792197 hasPublicationYear "2014" @default.
- W125792197 type Work @default.
- W125792197 sameAs 125792197 @default.
- W125792197 citedByCount "1" @default.
- W125792197 countsByYear W1257921972015 @default.
- W125792197 crossrefType "dissertation" @default.
- W125792197 hasAuthorship W125792197A5084723557 @default.
- W125792197 hasConcept C127413603 @default.
- W125792197 hasConcept C191897082 @default.
- W125792197 hasConcept C192562407 @default.
- W125792197 hasConcept C205688572 @default.
- W125792197 hasConcept C20625102 @default.
- W125792197 hasConcept C2779851234 @default.
- W125792197 hasConcept C2780013297 @default.
- W125792197 hasConcept C2780026712 @default.
- W125792197 hasConcept C2780532540 @default.
- W125792197 hasConcept C2781099003 @default.
- W125792197 hasConcept C505241676 @default.
- W125792197 hasConcept C511782168 @default.
- W125792197 hasConcept C548081761 @default.
- W125792197 hasConceptScore W125792197C127413603 @default.
- W125792197 hasConceptScore W125792197C191897082 @default.
- W125792197 hasConceptScore W125792197C192562407 @default.
- W125792197 hasConceptScore W125792197C205688572 @default.
- W125792197 hasConceptScore W125792197C20625102 @default.
- W125792197 hasConceptScore W125792197C2779851234 @default.
- W125792197 hasConceptScore W125792197C2780013297 @default.
- W125792197 hasConceptScore W125792197C2780026712 @default.
- W125792197 hasConceptScore W125792197C2780532540 @default.
- W125792197 hasConceptScore W125792197C2781099003 @default.
- W125792197 hasConceptScore W125792197C505241676 @default.
- W125792197 hasConceptScore W125792197C511782168 @default.
- W125792197 hasConceptScore W125792197C548081761 @default.
- W125792197 hasLocation W1257921971 @default.
- W125792197 hasOpenAccess W125792197 @default.
- W125792197 hasPrimaryLocation W1257921971 @default.
- W125792197 hasRelatedWork W115726726 @default.
- W125792197 hasRelatedWork W1551597433 @default.
- W125792197 hasRelatedWork W1590551170 @default.
- W125792197 hasRelatedWork W2017744128 @default.
- W125792197 hasRelatedWork W2059031927 @default.
- W125792197 hasRelatedWork W2061197218 @default.
- W125792197 hasRelatedWork W2082440974 @default.
- W125792197 hasRelatedWork W2142374301 @default.
- W125792197 hasRelatedWork W2355719151 @default.
- W125792197 hasRelatedWork W2373046798 @default.
- W125792197 hasRelatedWork W2384508924 @default.
- W125792197 hasRelatedWork W2572576755 @default.
- W125792197 hasRelatedWork W2787211944 @default.
- W125792197 hasRelatedWork W2888864035 @default.
- W125792197 hasRelatedWork W2910671471 @default.
- W125792197 hasRelatedWork W2957897763 @default.
- W125792197 hasRelatedWork W317816044 @default.
- W125792197 hasRelatedWork W3204383685 @default.
- W125792197 hasRelatedWork W96927783 @default.
- W125792197 hasRelatedWork W305966316 @default.
- W125792197 isParatext "false" @default.
- W125792197 isRetracted "false" @default.
- W125792197 magId "125792197" @default.
- W125792197 workType "dissertation" @default.