- W134828166 abstract "A series of ladder polymers have been synthesised from polycondensation reactions between phenazinium based monomers such as safranine O and acridine yellow G and benzoquinone type monomers. The same polymeric products were obtained regardless of whether the polymerisations were carried out in polyphosphoric acid, in organic solvent, or in the absence of solvent in the solid phase. However, the degree of completed ladder structure contained within the polymer was found to vary with different synthesis techniques. In general the ladder polymer prepared in PPA was superior in terms of intrinsic viscosity (molecular weight) and thermal stability in comparison to the same polymer prepared in organic solvent or in the solid phase. The polymer solubilities were poor in organic solvents and attempts to increase their solubilities with the introduction of bulky side-groups into the polymer structure was successful only in producing soluble single-strand polymers. The electrical conductivities (o) of the polymers lay in semi-conducting range with a clear trend showing that: 0PPA > 0DMAc/S.P. > 0single-strand > 0two-stagepolymers. The electrical conductivity was found to be stable for at least 30 days at incubation temperatures as high as 250° C. Temperature dependent conductivity studies show that plots of o versus T1/4 are not perfectly linear, although correlation coefficients for plots against '11/4 and T1[beta] show that the data tends to favour Mott's three-dimensional conduction model. Composite samples of thermoplastic PMMA and thermosetting polyester with ladder polymer showed percolation thresholds at 7.9% v/vand 8.6% viv filler loadings respectively with maximum conductivities close to those of the pristine polymer at filler loadings of 11.2% v/vand 13.0% vl» respectively. The temperature dependence of PMMA/ladder composites showed PTC behaviour between the softening point and melting point of PMMA with NTC behaviour thereafter. Thermosetting polyester composites showed little temperature sensitivity up to the point of thermal degradation at which catastrophic, permanent loss in conductivity occurred. The electrical conductivity of ladder/PMMA samples was found to be stable for at least 30 days at 250°C." @default.
- W134828166 created "2016-06-24" @default.
- W134828166 creator A5090008674 @default.
- W134828166 date "1997-01-01" @default.
- W134828166 modified "2023-09-27" @default.
- W134828166 title "The synthesis and characterisation of novel semiconduction ladder polymers and their use as conductive fillers in composite materials" @default.
- W134828166 hasPublicationYear "1997" @default.
- W134828166 type Work @default.
- W134828166 sameAs 134828166 @default.
- W134828166 citedByCount "0" @default.
- W134828166 crossrefType "dissertation" @default.
- W134828166 hasAuthorship W134828166A5090008674 @default.
- W134828166 hasConcept C104779481 @default.
- W134828166 hasConcept C110884469 @default.
- W134828166 hasConcept C127413603 @default.
- W134828166 hasConcept C159985019 @default.
- W134828166 hasConcept C166940927 @default.
- W134828166 hasConcept C171359207 @default.
- W134828166 hasConcept C178790620 @default.
- W134828166 hasConcept C185592680 @default.
- W134828166 hasConcept C188027245 @default.
- W134828166 hasConcept C192562407 @default.
- W134828166 hasConcept C2780471494 @default.
- W134828166 hasConcept C42360764 @default.
- W134828166 hasConcept C521977710 @default.
- W134828166 hasConcept C59061564 @default.
- W134828166 hasConceptScore W134828166C104779481 @default.
- W134828166 hasConceptScore W134828166C110884469 @default.
- W134828166 hasConceptScore W134828166C127413603 @default.
- W134828166 hasConceptScore W134828166C159985019 @default.
- W134828166 hasConceptScore W134828166C166940927 @default.
- W134828166 hasConceptScore W134828166C171359207 @default.
- W134828166 hasConceptScore W134828166C178790620 @default.
- W134828166 hasConceptScore W134828166C185592680 @default.
- W134828166 hasConceptScore W134828166C188027245 @default.
- W134828166 hasConceptScore W134828166C192562407 @default.
- W134828166 hasConceptScore W134828166C2780471494 @default.
- W134828166 hasConceptScore W134828166C42360764 @default.
- W134828166 hasConceptScore W134828166C521977710 @default.
- W134828166 hasConceptScore W134828166C59061564 @default.
- W134828166 hasLocation W1348281661 @default.
- W134828166 hasOpenAccess W134828166 @default.
- W134828166 hasPrimaryLocation W1348281661 @default.
- W134828166 hasRelatedWork W175718710 @default.
- W134828166 hasRelatedWork W1990433017 @default.
- W134828166 hasRelatedWork W1996197860 @default.
- W134828166 hasRelatedWork W1999891089 @default.
- W134828166 hasRelatedWork W2011045149 @default.
- W134828166 hasRelatedWork W2016271270 @default.
- W134828166 hasRelatedWork W2019802122 @default.
- W134828166 hasRelatedWork W2064717244 @default.
- W134828166 hasRelatedWork W2106965245 @default.
- W134828166 hasRelatedWork W2282921361 @default.
- W134828166 hasRelatedWork W2368709608 @default.
- W134828166 hasRelatedWork W2413019665 @default.
- W134828166 hasRelatedWork W2789503090 @default.
- W134828166 hasRelatedWork W2794043487 @default.
- W134828166 hasRelatedWork W2878459826 @default.
- W134828166 hasRelatedWork W2896023084 @default.
- W134828166 hasRelatedWork W3030484809 @default.
- W134828166 hasRelatedWork W3199759390 @default.
- W134828166 hasRelatedWork W637163510 @default.
- W134828166 hasRelatedWork W1780065340 @default.
- W134828166 isParatext "false" @default.
- W134828166 isRetracted "false" @default.
- W134828166 magId "134828166" @default.
- W134828166 workType "dissertation" @default.