- W146985553 abstract "Polyamide-imide (PAI) and polyurea-amide-imide (PUAI) resins were polymerized from five reactants: 4,4'-oxydianiline, 4-nitrobenzoyl chloride, 4,4'-diphenylmethane diisocyanate, 1,2,4,5-benzenetetracarboxylic dianhydride, and 3,3'-4,4'-benzophenone tetracarboxylic dianhydride. Their chemical structures were characterized using elemental analysis, FTIR and 1 H NMR spectroscopy. Their thermal properties, adhesive properties, electrical properties, heat resistance, and chemical resistance were studied. The experimental results show that the glass transition temperatures of PAI and PUAI films occurred respectively at 360 °C and 229 °C, and the 10% weight loss occurred respectively at approximately 481 °C and 420 °C. The optimal hot-press conditions for PAI/copper foil (CU) composite were 380°C and 4.90 MPa, whereas those for PUAI/copper foil (CU) composites were 250 °C and 4.90 MPa. Values of the peel strength, dielectric constant, and dissipation factor were obtained and the peel strength was re-measured after a thermal stability test. The chemical resistance tests showed that the peel strength retention values of the PAI/CU and PUAI/CU composites were respectively more than 95% and more than 94% after immersing in 10% H 2 SO 4 solution at 70 °C for 1 h." @default.
- W146985553 created "2016-06-24" @default.
- W146985553 creator A5015178100 @default.
- W146985553 creator A5028098036 @default.
- W146985553 creator A5081493541 @default.
- W146985553 date "2005-11-01" @default.
- W146985553 modified "2023-10-12" @default.
- W146985553 title "Preparation and Properties of Thermoplastic Polyamide-imide and Polyurea-amide-imide/Copper Foil Composites" @default.
- W146985553 cites W1983792880 @default.
- W146985553 cites W1999508150 @default.
- W146985553 cites W2016214568 @default.
- W146985553 cites W2018010017 @default.
- W146985553 cites W2063576766 @default.
- W146985553 cites W2067254879 @default.
- W146985553 cites W2070018299 @default.
- W146985553 cites W2077708075 @default.
- W146985553 cites W2078477142 @default.
- W146985553 cites W2087432570 @default.
- W146985553 cites W2089834412 @default.
- W146985553 cites W2106653694 @default.
- W146985553 cites W2115402239 @default.
- W146985553 cites W2137326125 @default.
- W146985553 cites W2155908659 @default.
- W146985553 cites W2164507160 @default.
- W146985553 cites W2483188302 @default.
- W146985553 cites W2530884537 @default.
- W146985553 cites W34133094 @default.
- W146985553 doi "https://doi.org/10.1177/096739110501300804" @default.
- W146985553 hasPublicationYear "2005" @default.
- W146985553 type Work @default.
- W146985553 sameAs 146985553 @default.
- W146985553 citedByCount "2" @default.
- W146985553 countsByYear W1469855532021 @default.
- W146985553 crossrefType "journal-article" @default.
- W146985553 hasAuthorship W146985553A5015178100 @default.
- W146985553 hasAuthorship W146985553A5028098036 @default.
- W146985553 hasAuthorship W146985553A5081493541 @default.
- W146985553 hasConcept C122865956 @default.
- W146985553 hasConcept C159985019 @default.
- W146985553 hasConcept C178790620 @default.
- W146985553 hasConcept C185592680 @default.
- W146985553 hasConcept C188027245 @default.
- W146985553 hasConcept C190399342 @default.
- W146985553 hasConcept C191897082 @default.
- W146985553 hasConcept C192562407 @default.
- W146985553 hasConcept C2777604212 @default.
- W146985553 hasConcept C2779578285 @default.
- W146985553 hasConcept C2780290348 @default.
- W146985553 hasConcept C2780700233 @default.
- W146985553 hasConcept C2781113870 @default.
- W146985553 hasConcept C521977710 @default.
- W146985553 hasConcept C544778455 @default.
- W146985553 hasConcept C59061564 @default.
- W146985553 hasConcept C7363328 @default.
- W146985553 hasConceptScore W146985553C122865956 @default.
- W146985553 hasConceptScore W146985553C159985019 @default.
- W146985553 hasConceptScore W146985553C178790620 @default.
- W146985553 hasConceptScore W146985553C185592680 @default.
- W146985553 hasConceptScore W146985553C188027245 @default.
- W146985553 hasConceptScore W146985553C190399342 @default.
- W146985553 hasConceptScore W146985553C191897082 @default.
- W146985553 hasConceptScore W146985553C192562407 @default.
- W146985553 hasConceptScore W146985553C2777604212 @default.
- W146985553 hasConceptScore W146985553C2779578285 @default.
- W146985553 hasConceptScore W146985553C2780290348 @default.
- W146985553 hasConceptScore W146985553C2780700233 @default.
- W146985553 hasConceptScore W146985553C2781113870 @default.
- W146985553 hasConceptScore W146985553C521977710 @default.
- W146985553 hasConceptScore W146985553C544778455 @default.
- W146985553 hasConceptScore W146985553C59061564 @default.
- W146985553 hasConceptScore W146985553C7363328 @default.
- W146985553 hasIssue "8" @default.
- W146985553 hasLocation W1469855531 @default.
- W146985553 hasOpenAccess W146985553 @default.
- W146985553 hasPrimaryLocation W1469855531 @default.
- W146985553 hasRelatedWork W146985553 @default.
- W146985553 hasRelatedWork W1529865302 @default.
- W146985553 hasRelatedWork W1824029043 @default.
- W146985553 hasRelatedWork W1964086589 @default.
- W146985553 hasRelatedWork W1975608897 @default.
- W146985553 hasRelatedWork W1994103032 @default.
- W146985553 hasRelatedWork W2010350659 @default.
- W146985553 hasRelatedWork W2058635225 @default.
- W146985553 hasRelatedWork W2060797326 @default.
- W146985553 hasRelatedWork W4248419280 @default.
- W146985553 hasVolume "13" @default.
- W146985553 isParatext "false" @default.
- W146985553 isRetracted "false" @default.
- W146985553 magId "146985553" @default.
- W146985553 workType "article" @default.