- W1488961242 abstract "This paper studies the vibration fatigue failure of /spl mu/BGA solder-joints reflowed with different temperature profiles, and ageing at 120/spl deg/C for 1, 4, 9, 16, 25, 36 days. The effect of the thickness of the Ni/sub 3/Sn/sub 4/ and Cu-Sn intermetallic compound (IMC) on the fatigue lifetime is also reported. During the vibration fatigue test, in order to identify the failure of /spl mu/BGA solder joint, electrical interruption was monitored continuously through the daisy-chain network. Our results show that the fatigue lifetime of the solder joint firstly increases and then decreases with increasing heating factor (Q/sub n/), which is defined as the integral of the measured temperature over the dwell time above liquidus (183/spl deg/C) in the reflow profile. The greatest lifetime occurs when Q/sub n/ is near 500 s/spl deg/C. Moreover, the lifetime of the solder joint decreases linearly with the increasing fourth root of the ageing time. The SEM/EDX inspection shows that only Ni/sub 3/Sn/sub 4/ IMC and Cu/sub 6/Sn/sub 5//Cu/sub 3/Sn IMCs are formed between the solder and the nickel-plated PCB pad, and the solder/component-metallization interface respectively. For non-aged samples reflowed with different profiles, the fatigue crack generally initiates at valleys in the rough surface of the interface of the Ni/sub 3/Sn/sub 4/ IMC with the bulk solder. Then it propagates mostly near the Ni/solder, and occasionally in the IMC layer or along the Ni/solder interface. For aged samples, the fatigue crack mostly initiates and propagates in the Cu/sub 6/Sn/sub 5/-phase/bulksolder interface or the Cu/sub 3/Sn/Cu/sub 6/Sn/sub 5/ interface on component-metallization. Evidently, the intermetallic compounds contribute mainly to the fatigue failure of /spl mu/BGA solder joints. The thicker the IMC layer, the shorter the fatigue lifetime of solder joint. The initial formation of the IMCs at the interface during soldering ensures a good metallurgical bond between the solder and the substrate. However, a thick IMC layer influences the solder joint strength, which results in mechanical failure due to volume shrinkage during the transformation from solid phase to the intermetallic compound." @default.
- W1488961242 created "2016-06-24" @default.
- W1488961242 creator A5003413816 @default.
- W1488961242 creator A5009075675 @default.
- W1488961242 creator A5024126823 @default.
- W1488961242 creator A5062242819 @default.
- W1488961242 date "2002-11-07" @default.
- W1488961242 modified "2023-09-24" @default.
- W1488961242 title "Vibration fatigue of μBGA solder joint" @default.
- W1488961242 cites W1039712956 @default.
- W1488961242 cites W1975127620 @default.
- W1488961242 cites W2024311851 @default.
- W1488961242 cites W2071206766 @default.
- W1488961242 cites W2075302063 @default.
- W1488961242 cites W2088929950 @default.
- W1488961242 cites W2107938193 @default.
- W1488961242 cites W2120060789 @default.
- W1488961242 cites W2126200438 @default.
- W1488961242 cites W2135162454 @default.
- W1488961242 cites W2147615371 @default.
- W1488961242 cites W2149237593 @default.
- W1488961242 cites W2166014898 @default.
- W1488961242 doi "https://doi.org/10.1109/ectc.2000.853388" @default.
- W1488961242 hasPublicationYear "2002" @default.
- W1488961242 type Work @default.
- W1488961242 sameAs 1488961242 @default.
- W1488961242 citedByCount "8" @default.
- W1488961242 crossrefType "proceedings-article" @default.
- W1488961242 hasAuthorship W1488961242A5003413816 @default.
- W1488961242 hasAuthorship W1488961242A5009075675 @default.
- W1488961242 hasAuthorship W1488961242A5024126823 @default.
- W1488961242 hasAuthorship W1488961242A5062242819 @default.
- W1488961242 hasConcept C119599485 @default.
- W1488961242 hasConcept C127413603 @default.
- W1488961242 hasConcept C145653223 @default.
- W1488961242 hasConcept C159985019 @default.
- W1488961242 hasConcept C18555067 @default.
- W1488961242 hasConcept C191281628 @default.
- W1488961242 hasConcept C191897082 @default.
- W1488961242 hasConcept C192562407 @default.
- W1488961242 hasConcept C27501479 @default.
- W1488961242 hasConcept C2780026712 @default.
- W1488961242 hasConcept C50296614 @default.
- W1488961242 hasConcept C525849907 @default.
- W1488961242 hasConcept C59014099 @default.
- W1488961242 hasConcept C66938386 @default.
- W1488961242 hasConcept C94709252 @default.
- W1488961242 hasConceptScore W1488961242C119599485 @default.
- W1488961242 hasConceptScore W1488961242C127413603 @default.
- W1488961242 hasConceptScore W1488961242C145653223 @default.
- W1488961242 hasConceptScore W1488961242C159985019 @default.
- W1488961242 hasConceptScore W1488961242C18555067 @default.
- W1488961242 hasConceptScore W1488961242C191281628 @default.
- W1488961242 hasConceptScore W1488961242C191897082 @default.
- W1488961242 hasConceptScore W1488961242C192562407 @default.
- W1488961242 hasConceptScore W1488961242C27501479 @default.
- W1488961242 hasConceptScore W1488961242C2780026712 @default.
- W1488961242 hasConceptScore W1488961242C50296614 @default.
- W1488961242 hasConceptScore W1488961242C525849907 @default.
- W1488961242 hasConceptScore W1488961242C59014099 @default.
- W1488961242 hasConceptScore W1488961242C66938386 @default.
- W1488961242 hasConceptScore W1488961242C94709252 @default.
- W1488961242 hasLocation W14889612421 @default.
- W1488961242 hasOpenAccess W1488961242 @default.
- W1488961242 hasPrimaryLocation W14889612421 @default.
- W1488961242 hasRelatedWork W1544945603 @default.
- W1488961242 hasRelatedWork W1908614489 @default.
- W1488961242 hasRelatedWork W1912115001 @default.
- W1488961242 hasRelatedWork W1986402821 @default.
- W1488961242 hasRelatedWork W2026937842 @default.
- W1488961242 hasRelatedWork W2037947369 @default.
- W1488961242 hasRelatedWork W2097892440 @default.
- W1488961242 hasRelatedWork W2098143596 @default.
- W1488961242 hasRelatedWork W2101644748 @default.
- W1488961242 hasRelatedWork W2114781719 @default.
- W1488961242 hasRelatedWork W2129692550 @default.
- W1488961242 hasRelatedWork W2134816927 @default.
- W1488961242 hasRelatedWork W2135162454 @default.
- W1488961242 hasRelatedWork W2160556881 @default.
- W1488961242 hasRelatedWork W2166014898 @default.
- W1488961242 hasRelatedWork W2171925162 @default.
- W1488961242 hasRelatedWork W2789334033 @default.
- W1488961242 hasRelatedWork W2799157498 @default.
- W1488961242 hasRelatedWork W2897951050 @default.
- W1488961242 hasRelatedWork W2993427929 @default.
- W1488961242 isParatext "false" @default.
- W1488961242 isRetracted "false" @default.
- W1488961242 magId "1488961242" @default.
- W1488961242 workType "article" @default.