- W148933122 abstract "Methods have been developed for the fabrication of fuel elements consisting of U0/sub 2/ pellets sheathed in aluminum -nickel alloy tubing. Corrosion resistant endclosures were made by hot pressure welding. The corrosion behavior of these elements has been determined in an exposure for two reactor cycles in the X-2 loop in NRX Reactor. Loop conditioner were: deionized water at 280 C flowing at 18 ft/sec over the fuel sheaths. Heat fluxes through the sheaths varied from 11.4 to 68.5 was severe. A penetration of roughly 7 x 10/sup -3/ inches was measured after the first reactor cycle (21 days). The penetration was much less during the second cycle for moderately rated elements (11 -12 watts/ cm/sup 2/) but again about 7 x 10/sup -3/ inches for a highly rated element (68.4 watts/cm/sup 2/). It could be concluded that an increased heat flux resulted in an increased rate of sheath penetration, the increase from ~ 12 watts/cm/sup 2/ to ~70 watts/ cm/sup 2/ approximately doubling the penetration. It is now known that the corrosion observed in this experiment was more severe than would have been found in a system containing a much larger area or corroding aluminum. The severe pitting andmore » erosion of the X-2(h) samples are known to be characteristic of corrosion in a system containing a small area of aluminum in a large volume of purified water. The X-2(h) test was therefore not typical of conditions in a reactor with aluminum-nickel sheathed fuel. (auth)« less" @default.
- W148933122 created "2016-06-24" @default.
- W148933122 creator A5047351971 @default.
- W148933122 creator A5091163666 @default.
- W148933122 date "1958-11-01" @default.
- W148933122 modified "2023-09-26" @default.
- W148933122 title "BEHAVIOUR OF Al-Ni SHEATHING ON UO$sub 2$ FUEL ELEMENTS IRRADIATED IN HIGH TEMPERATURE WATER (X-2h TEST)" @default.
- W148933122 hasPublicationYear "1958" @default.
- W148933122 type Work @default.
- W148933122 sameAs 148933122 @default.
- W148933122 citedByCount "0" @default.
- W148933122 crossrefType "journal-article" @default.
- W148933122 hasAuthorship W148933122A5047351971 @default.
- W148933122 hasAuthorship W148933122A5091163666 @default.
- W148933122 hasConcept C111337013 @default.
- W148933122 hasConcept C113196181 @default.
- W148933122 hasConcept C121332964 @default.
- W148933122 hasConcept C127413603 @default.
- W148933122 hasConcept C159985019 @default.
- W148933122 hasConcept C185544564 @default.
- W148933122 hasConcept C185592680 @default.
- W148933122 hasConcept C191897082 @default.
- W148933122 hasConcept C192562407 @default.
- W148933122 hasConcept C19474535 @default.
- W148933122 hasConcept C20625102 @default.
- W148933122 hasConcept C2780026712 @default.
- W148933122 hasConcept C2780584874 @default.
- W148933122 hasConcept C42475967 @default.
- W148933122 hasConcept C43617362 @default.
- W148933122 hasConcept C504270822 @default.
- W148933122 hasConcept C513153333 @default.
- W148933122 hasConcept C80107235 @default.
- W148933122 hasConceptScore W148933122C111337013 @default.
- W148933122 hasConceptScore W148933122C113196181 @default.
- W148933122 hasConceptScore W148933122C121332964 @default.
- W148933122 hasConceptScore W148933122C127413603 @default.
- W148933122 hasConceptScore W148933122C159985019 @default.
- W148933122 hasConceptScore W148933122C185544564 @default.
- W148933122 hasConceptScore W148933122C185592680 @default.
- W148933122 hasConceptScore W148933122C191897082 @default.
- W148933122 hasConceptScore W148933122C192562407 @default.
- W148933122 hasConceptScore W148933122C19474535 @default.
- W148933122 hasConceptScore W148933122C20625102 @default.
- W148933122 hasConceptScore W148933122C2780026712 @default.
- W148933122 hasConceptScore W148933122C2780584874 @default.
- W148933122 hasConceptScore W148933122C42475967 @default.
- W148933122 hasConceptScore W148933122C43617362 @default.
- W148933122 hasConceptScore W148933122C504270822 @default.
- W148933122 hasConceptScore W148933122C513153333 @default.
- W148933122 hasConceptScore W148933122C80107235 @default.
- W148933122 hasLocation W1489331221 @default.
- W148933122 hasOpenAccess W148933122 @default.
- W148933122 hasPrimaryLocation W1489331221 @default.
- W148933122 hasRelatedWork W1988121822 @default.
- W148933122 hasRelatedWork W2078750342 @default.
- W148933122 hasRelatedWork W2079007322 @default.
- W148933122 hasRelatedWork W3202133464 @default.
- W148933122 hasRelatedWork W2065561286 @default.
- W148933122 hasRelatedWork W2152779480 @default.
- W148933122 hasRelatedWork W2247348167 @default.
- W148933122 hasRelatedWork W2405791446 @default.
- W148933122 hasRelatedWork W2493015987 @default.
- W148933122 hasRelatedWork W2839007729 @default.
- W148933122 hasRelatedWork W2840499648 @default.
- W148933122 hasRelatedWork W2852029140 @default.
- W148933122 hasRelatedWork W2857976854 @default.
- W148933122 hasRelatedWork W2862743829 @default.
- W148933122 hasRelatedWork W2875331191 @default.
- W148933122 hasRelatedWork W2879237872 @default.
- W148933122 hasRelatedWork W2927407456 @default.
- W148933122 hasRelatedWork W2928941418 @default.
- W148933122 hasRelatedWork W2931321580 @default.
- W148933122 hasRelatedWork W2957702213 @default.
- W148933122 isParatext "false" @default.
- W148933122 isRetracted "false" @default.
- W148933122 magId "148933122" @default.
- W148933122 workType "article" @default.