- W1504381630 abstract "Bulk glass of SrAl2Si2O8 composition crystallized at temperatures below 1000 C into hexacelsian, a hexagonal phase which undergoes a reversible, rapid transformation to an orthorhombic phase at 758 C, and at higher temperatures crystallized as celsian, a monoclinic phase. The glass transition temperature and crystallization onset temperature were determined to be 883 C and 1086 C, respectively, from DSC at a heating rate of 20 C/min. Thermal expansion of the various phases and density and bend strengths of cold isostatically pressed glass powder bars, sintered at various temperatures, were measured. The kinetics of the hexacelsian-to-celsian transformation for SrAl2Si2O8 were studied. Hexacelsian flakes were isothermally heat treated at temperatures from 1025-1200 C for various times. Avrami plots were determined by quantitatively measuring the amount of monoclinic celsian formed at various times using x ray diffraction. The Avrami constant was determined to be 1.1, suggesting a diffusionless, one dimensional transformation mechanism. The activation energy was determined from an Arrhenius plot of 1n k vs. 1/T to be 125 kilocal/mole. This value is consistent with a mechanism which transforms the layered hexacelsian structure to a three dimensional framework celsian structure and involves the breaking of Si-O bonds." @default.
- W1504381630 created "2016-06-24" @default.
- W1504381630 creator A5040232716 @default.
- W1504381630 creator A5054654565 @default.
- W1504381630 date "1992-01-01" @default.
- W1504381630 modified "2023-09-27" @default.
- W1504381630 title "Phase transformations in SrAl2Si2O8 glass" @default.
- W1504381630 cites W2006979836 @default.
- W1504381630 hasPublicationYear "1992" @default.
- W1504381630 type Work @default.
- W1504381630 sameAs 1504381630 @default.
- W1504381630 citedByCount "0" @default.
- W1504381630 crossrefType "journal-article" @default.
- W1504381630 hasAuthorship W1504381630A5040232716 @default.
- W1504381630 hasAuthorship W1504381630A5054654565 @default.
- W1504381630 hasConcept C113196181 @default.
- W1504381630 hasConcept C115624301 @default.
- W1504381630 hasConcept C121332964 @default.
- W1504381630 hasConcept C133347239 @default.
- W1504381630 hasConcept C147789679 @default.
- W1504381630 hasConcept C178790620 @default.
- W1504381630 hasConcept C185592680 @default.
- W1504381630 hasConcept C192562407 @default.
- W1504381630 hasConcept C199289684 @default.
- W1504381630 hasConcept C203036418 @default.
- W1504381630 hasConcept C37243968 @default.
- W1504381630 hasConcept C43617362 @default.
- W1504381630 hasConcept C44280652 @default.
- W1504381630 hasConcept C61276311 @default.
- W1504381630 hasConcept C8010536 @default.
- W1504381630 hasConcept C86183883 @default.
- W1504381630 hasConcept C8739425 @default.
- W1504381630 hasConcept C95121573 @default.
- W1504381630 hasConcept C97355855 @default.
- W1504381630 hasConceptScore W1504381630C113196181 @default.
- W1504381630 hasConceptScore W1504381630C115624301 @default.
- W1504381630 hasConceptScore W1504381630C121332964 @default.
- W1504381630 hasConceptScore W1504381630C133347239 @default.
- W1504381630 hasConceptScore W1504381630C147789679 @default.
- W1504381630 hasConceptScore W1504381630C178790620 @default.
- W1504381630 hasConceptScore W1504381630C185592680 @default.
- W1504381630 hasConceptScore W1504381630C192562407 @default.
- W1504381630 hasConceptScore W1504381630C199289684 @default.
- W1504381630 hasConceptScore W1504381630C203036418 @default.
- W1504381630 hasConceptScore W1504381630C37243968 @default.
- W1504381630 hasConceptScore W1504381630C43617362 @default.
- W1504381630 hasConceptScore W1504381630C44280652 @default.
- W1504381630 hasConceptScore W1504381630C61276311 @default.
- W1504381630 hasConceptScore W1504381630C8010536 @default.
- W1504381630 hasConceptScore W1504381630C86183883 @default.
- W1504381630 hasConceptScore W1504381630C8739425 @default.
- W1504381630 hasConceptScore W1504381630C95121573 @default.
- W1504381630 hasConceptScore W1504381630C97355855 @default.
- W1504381630 hasLocation W15043816301 @default.
- W1504381630 hasOpenAccess W1504381630 @default.
- W1504381630 hasPrimaryLocation W15043816301 @default.
- W1504381630 hasRelatedWork W1566764244 @default.
- W1504381630 hasRelatedWork W1571019569 @default.
- W1504381630 hasRelatedWork W1977519026 @default.
- W1504381630 hasRelatedWork W1981658235 @default.
- W1504381630 hasRelatedWork W1987179532 @default.
- W1504381630 hasRelatedWork W1992760573 @default.
- W1504381630 hasRelatedWork W2050471614 @default.
- W1504381630 hasRelatedWork W2058065076 @default.
- W1504381630 hasRelatedWork W2087669928 @default.
- W1504381630 hasRelatedWork W2318072615 @default.
- W1504381630 hasRelatedWork W2479005495 @default.
- W1504381630 hasRelatedWork W2493663829 @default.
- W1504381630 hasRelatedWork W2584471775 @default.
- W1504381630 hasRelatedWork W2593234073 @default.
- W1504381630 hasRelatedWork W2737958337 @default.
- W1504381630 hasRelatedWork W2914483345 @default.
- W1504381630 hasRelatedWork W2959955104 @default.
- W1504381630 hasRelatedWork W3091368448 @default.
- W1504381630 hasRelatedWork W3134243350 @default.
- W1504381630 hasRelatedWork W789447349 @default.
- W1504381630 isParatext "false" @default.
- W1504381630 isRetracted "false" @default.
- W1504381630 magId "1504381630" @default.
- W1504381630 workType "article" @default.