• W1514489247 endingPage "189" @default.
• W1514489247 startingPage "173" @default.
• W1514489247 abstract "Two naphthalene-aromatic polyamides were prepared from 2,6-naphthalenedicarboxylic acid and various aromatic diamines by a modified Higashi phosphorylation reaction. The first polymer, poly(4,4′-diaminobenzanilide-2,6-naphthalamide)** (DBNA), was synthesized by the reaction of 2,6-naphthalenedicarboxylic acid with 4,4′-diaminobenzanilide. The second polymer, 50/50 copoly(1,4-phenylene/1,4-bis(4′-phenoxy)benzene-2,6-naphthalamide)*** (PBNA), is a copolymer synthesized using an equimolar ratio of 1,4-phenylene diamine and 1,4-bis(4′-aminophenoxy)benzene. These two polymers have inherent viscosities of 4.17 and 2.32 dL g-1, respectively, and dissolve in N-methyl-2-pyrrolidone (NMP)containing LiCl. Highstrength films were obtained by casting from these polymer solutions. Blends of DBNA/amorphous nylon and of PBNA/amorphous nylon were prepared by rapidly precipitating the ternary NMP solution into deionized water, and hot-pressing to films at 185°C. The compatibility, morphology, and mechanical properties were investigated by dynamic mechanical analysis (DMA), scanning electron microscopy (SEM), and tensile tests. The results revealed that both DBNA and PBNA were partially compatible with amorphous nylon. DBNA formed microfibrils in the amorphous nylon matrix, and its mechanical properties, tensile strength and modulus, improved with increasing DBNA content. PBNA had no reinforcing effect, perhaps because it did not form microfibrils in the amorphous nylon matrix. Zwei aromatische Polyamide auf Naphthalin-Basis wurden durch modifizierte Higashi-Phosphorylierung aus Naphthalin-2,6-dicarbonsäure und aromatischen Diaminen hergestellt. Das erste Polymere, Poly(4,4′-diaminobenzanilid-2,6-naphthyl-amid)* (DBNA), wurde aus Naphthalin-2,6-dicarbonsaure und 4,4'-Diaminobenzanilid erhalten. Zur Synthese des zweiten Polymeren, 50/50-Copoly(1,4-phenylen/1,4-bis(4'-phenoxy) phenylen-2,6-naphthylamid)** (PBNA), wurden aquimolare Mengen 4-Phenylendiamin und 1,4-Bis(4'-aminophenoxy)benzol rnit Naphthalin 2,6-dicarbonsaure umgesetzt. Die Polymeren mit inhajenten Viskositaten von 4,17 bzw. 2,32 dL g-' sind in LiC1-haltigem N-Methylpyrrolidon (NMP) loslich. Durch FilmgieBen wurden hochfeste Filme erhalten. Blends aus DBNA bzw. PBNA mit amorphem Nylon wurden durch rasches Fallen der temaren NMP-Losungen in deionisiertem Wasser hergestellt und bei 185 C zu Filmen geprel3t. Die Vertraglichkeiten, Morphologien und mechanischen Eigenschaften der Polyamide wurden durch dynamisch-mechanische Analyse, Rasterelektronenmikroskopie und Zugversuche charakterisiert. Die Ergebnisse zeigten, dalj beide Polyamide rnit Nylon teilweise kompatibel sind. DBNA bildet Mikrofibrillen in der Nylonmatrix, und Zugfestigkeit sowie Zugmodul des Blends nehmen rnit steigendem DBNA-Gehalt zu. PBNA bildet keine Mikrofibrillen in der Nylonmatrix und zeigte, moglicherweise aus diesem Grund, keinen die Matrix verstarkenden Effekt." @default.
• W1514489247 created "2016-06-24" @default.
• W1514489247 creator A5025212854 @default.
• W1514489247 creator A5058193480 @default.
• W1514489247 date "1996-04-01" @default.
• W1514489247 modified "2023-10-16" @default.
• W1514489247 doi "https://doi.org/10.1002/apmc.1996.052370110" @default.
• W1514489247 hasPublicationYear "1996" @default.
• W1514489247 type Work @default.
• W1514489247 sameAs 1514489247 @default.
• W1514489247 citedByCount "5" @default.
• W1514489247 countsByYear W15144892472019 @default.
• W1514489247 crossrefType "journal-article" @default.
• W1514489247 hasAuthorship W1514489247A5025212854 @default.
• W1514489247 hasAuthorship W1514489247A5058193480 @default.
• W1514489247 hasConcept C127413603 @default.
• W1514489247 hasConcept C13965031 @default.
• W1514489247 hasConcept C178790620 @default.
• W1514489247 hasConcept C185592680 @default.
• W1514489247 hasConcept C188027245 @default.
• W1514489247 hasConcept C190399342 @default.
• W1514489247 hasConcept C192562407 @default.
• W1514489247 hasConcept C2776026683 @default.
• W1514489247 hasConcept C2780871995 @default.
• W1514489247 hasConcept C42360764 @default.
• W1514489247 hasConcept C521977710 @default.
• W1514489247 hasConcept C56052488 @default.
• W1514489247 hasConceptScore W1514489247C127413603 @default.
• W1514489247 hasConceptScore W1514489247C13965031 @default.
• W1514489247 hasConceptScore W1514489247C178790620 @default.
• W1514489247 hasConceptScore W1514489247C185592680 @default.
• W1514489247 hasConceptScore W1514489247C188027245 @default.
• W1514489247 hasConceptScore W1514489247C190399342 @default.
• W1514489247 hasConceptScore W1514489247C192562407 @default.
• W1514489247 hasConceptScore W1514489247C2776026683 @default.
• W1514489247 hasConceptScore W1514489247C2780871995 @default.
• W1514489247 hasConceptScore W1514489247C42360764 @default.
• W1514489247 hasConceptScore W1514489247C521977710 @default.
• W1514489247 hasConceptScore W1514489247C56052488 @default.
• W1514489247 hasIssue "1" @default.
• W1514489247 hasLocation W15144892471 @default.
• W1514489247 hasOpenAccess W1514489247 @default.
• W1514489247 hasPrimaryLocation W15144892471 @default.
• W1514489247 hasRelatedWork W1925698511 @default.
• W1514489247 hasRelatedWork W1997817349 @default.
• W1514489247 hasRelatedWork W2002555758 @default.
• W1514489247 hasRelatedWork W2010655344 @default.
• W1514489247 hasRelatedWork W2016258168 @default.
• W1514489247 hasRelatedWork W2045816332 @default.
• W1514489247 hasRelatedWork W2078794024 @default.
• W1514489247 hasRelatedWork W2101922907 @default.
• W1514489247 hasRelatedWork W2292225664 @default.
• W1514489247 hasRelatedWork W3192727899 @default.
• W1514489247 hasVolume "237" @default.
• W1514489247 isParatext "false" @default.
• W1514489247 isRetracted "false" @default.
• W1514489247 magId "1514489247" @default.
• W1514489247 workType "article" @default.