- W1515085937 abstract "To check technical improvement in the soundness and strength of 12% Cr steel rotor, a 25 tons of rotor with 65 tons of ingot was made in real size and was cut to pieces to take test samples, and the various mechanical tests such as impact, tensile, creep, and fatigue were carried out. The strengths are compared with those of 1% Cr-Mo-V rotor of same size. Microstructures of the samples are examined and reviewed. The results can be summarized as follows. 1) Fracture appearance transition temperatures are 80.deg. C at the center part and 60.deg. C near surface of 12% Cr rotor, and 8.deg. C near surface of 1% Cr-Mo-V rotor. 2) Comparative rapid softening occurs at higher temperatures above 600.deg. C for 12% Cr steel and 550.deg. C for 1% Cr-Mo-V steel in tension tests. 3) Fatigue crack propagation rate of 12% Cr steel is almost same as that of 1% Cr-Mo-V steel at the same corresponding surface part of the rotors. The crack growth rate of center part of 12% Cr rotor is faster than near surface part of the rotor, and the crack growth rate at the load condition of R=0.04 is slower than that of the load condition of R=0.5 for both 12% Cr steel and 1% Cr-Mo-V steel. 4) Crack growth rate of radial direction near surface of 12% Cr rotor is faster than that of transverse direction at the same part because of the difference in residual stresses. 5) Both creep and fatigue strengths of 12% Cr steel are superior to those of 1% Cr-Mo-V steel and the difference is thought the effect of climb and glide controlled creep by solid solution of alloying elements and dispersion of carbides." @default.
- W1515085937 created "2016-06-24" @default.
- W1515085937 creator A5021734443 @default.
- W1515085937 creator A5040370185 @default.
- W1515085937 date "1989-01-01" @default.
- W1515085937 modified "2023-09-24" @default.
- W1515085937 title "Study on the Improvement of Strength for 12% Chromium Steel Rotor" @default.
- W1515085937 hasPublicationYear "1989" @default.
- W1515085937 type Work @default.
- W1515085937 sameAs 1515085937 @default.
- W1515085937 citedByCount "0" @default.
- W1515085937 crossrefType "journal-article" @default.
- W1515085937 hasAuthorship W1515085937A5021734443 @default.
- W1515085937 hasAuthorship W1515085937A5040370185 @default.
- W1515085937 hasConcept C112950240 @default.
- W1515085937 hasConcept C119599485 @default.
- W1515085937 hasConcept C127413603 @default.
- W1515085937 hasConcept C159985019 @default.
- W1515085937 hasConcept C17281054 @default.
- W1515085937 hasConcept C191897082 @default.
- W1515085937 hasConcept C192562407 @default.
- W1515085937 hasConcept C2778547858 @default.
- W1515085937 hasConcept C2780026712 @default.
- W1515085937 hasConcept C511782168 @default.
- W1515085937 hasConceptScore W1515085937C112950240 @default.
- W1515085937 hasConceptScore W1515085937C119599485 @default.
- W1515085937 hasConceptScore W1515085937C127413603 @default.
- W1515085937 hasConceptScore W1515085937C159985019 @default.
- W1515085937 hasConceptScore W1515085937C17281054 @default.
- W1515085937 hasConceptScore W1515085937C191897082 @default.
- W1515085937 hasConceptScore W1515085937C192562407 @default.
- W1515085937 hasConceptScore W1515085937C2778547858 @default.
- W1515085937 hasConceptScore W1515085937C2780026712 @default.
- W1515085937 hasConceptScore W1515085937C511782168 @default.
- W1515085937 hasIssue "2" @default.
- W1515085937 hasLocation W15150859371 @default.
- W1515085937 hasOpenAccess W1515085937 @default.
- W1515085937 hasPrimaryLocation W15150859371 @default.
- W1515085937 hasRelatedWork W1971681391 @default.
- W1515085937 hasRelatedWork W1988295655 @default.
- W1515085937 hasRelatedWork W1989302723 @default.
- W1515085937 hasRelatedWork W2004644219 @default.
- W1515085937 hasRelatedWork W2028686304 @default.
- W1515085937 hasRelatedWork W2031445278 @default.
- W1515085937 hasRelatedWork W2048437061 @default.
- W1515085937 hasRelatedWork W2054113744 @default.
- W1515085937 hasRelatedWork W2069347147 @default.
- W1515085937 hasRelatedWork W2077990590 @default.
- W1515085937 hasRelatedWork W2291776039 @default.
- W1515085937 hasRelatedWork W2326629224 @default.
- W1515085937 hasRelatedWork W2329676994 @default.
- W1515085937 hasRelatedWork W2330005402 @default.
- W1515085937 hasRelatedWork W2335677141 @default.
- W1515085937 hasRelatedWork W2364764439 @default.
- W1515085937 hasRelatedWork W2533894055 @default.
- W1515085937 hasRelatedWork W2892637362 @default.
- W1515085937 hasRelatedWork W3046880250 @default.
- W1515085937 hasRelatedWork W419914410 @default.
- W1515085937 hasVolume "3" @default.
- W1515085937 isParatext "false" @default.
- W1515085937 isRetracted "false" @default.
- W1515085937 magId "1515085937" @default.
- W1515085937 workType "article" @default.