- W1544544572 abstract "The spallation of aluminum, chromium, and iron oxide scales is a chronic problem that critically impacts technological applications like aerospace, power plant operation, catalysis, petrochemical industry, and the fabrication of composite materials. The presence of interfacial impurities, mainly sulfur, has been reported to accelerate spallation, thereby promoting the high-temperature corrosion of metals and alloys. The precise mechanism for sulfur-induced destruction of oxides, however, is ambiguous. The objective of the present research is to elucidate the microscopic mechanism for the high-temperature corrosion of aluminum alloys in the presence of sulfur. Auger electron spectroscopy (AES), low energy electron diffraction (LEED), and scanning tunneling microscopy (STM) studies were conducted under ultrahigh vacuum (UHV) conditions on oxidized sulfur-free and sulfur-modified Al/Fe and Ni3Al(111). Evaporative deposition of aluminum onto a sulfur-covered iron surface results in the insertion of aluminum between the sulfur adlayer and the substrate, producing an Fe-Al-S interface. Aluminum oxidation at 300 K is retarded in the presence of sulfur. Oxide destabilization, and the formation of metallic aluminum are observed at temperatures > 600 K when sulfur is located at the Al2O3-Fe interface, while the sulfur-free interface is stable up to 900 K. In contrast, the thermal stability (up to at least 1100 K) of the Al2O3 formed on an Ni3Al(111) surface is unaffected by sulfur. Sulfur remains at the oxide-Ni3Al(111) interface after oxidation at 300 K. During annealing, aluminum segregation to the g ¢ -Al2O3-Ni3Al(111) interface occurs, coincident with the removal of sulfur from the interfacial region. A comparison of the results observed for the Al2O3/Fe and Al2O3/Ni3Al systems indicates that the high-temperature stability of Al2O3 films on aluminum alloys is connected with the concentration of aluminum in the alloy." @default.
- W1544544572 created "2016-06-24" @default.
- W1544544572 creator A5006556751 @default.
- W1544544572 date "2000-12-01" @default.
- W1544544572 modified "2023-09-24" @default.
- W1544544572 title "High-Temperature Corrosion of Aluminum Alloys: Oxide-Alloy Interactions and Sulfur Interface Chemistry" @default.
- W1544544572 cites W1519627314 @default.
- W1544544572 cites W1607286065 @default.
- W1544544572 cites W2000652300 @default.
- W1544544572 cites W2056469506 @default.
- W1544544572 cites W2245263283 @default.
- W1544544572 cites W2320806739 @default.
- W1544544572 cites W264891673 @default.
- W1544544572 cites W656923709 @default.
- W1544544572 hasPublicationYear "2000" @default.
- W1544544572 type Work @default.
- W1544544572 sameAs 1544544572 @default.
- W1544544572 citedByCount "1" @default.
- W1544544572 crossrefType "dissertation" @default.
- W1544544572 hasAuthorship W1544544572A5006556751 @default.
- W1544544572 hasConcept C11608111 @default.
- W1544544572 hasConcept C121332964 @default.
- W1544544572 hasConcept C127413603 @default.
- W1544544572 hasConcept C152568617 @default.
- W1544544572 hasConcept C179104552 @default.
- W1544544572 hasConcept C185544564 @default.
- W1544544572 hasConcept C185592680 @default.
- W1544544572 hasConcept C191897082 @default.
- W1544544572 hasConcept C192562407 @default.
- W1544544572 hasConcept C20625102 @default.
- W1544544572 hasConcept C25442681 @default.
- W1544544572 hasConcept C2779851234 @default.
- W1544544572 hasConcept C2780026712 @default.
- W1544544572 hasConcept C2781099003 @default.
- W1544544572 hasConcept C42360764 @default.
- W1544544572 hasConcept C513153333 @default.
- W1544544572 hasConcept C518881349 @default.
- W1544544572 hasConcept C62520636 @default.
- W1544544572 hasConceptScore W1544544572C11608111 @default.
- W1544544572 hasConceptScore W1544544572C121332964 @default.
- W1544544572 hasConceptScore W1544544572C127413603 @default.
- W1544544572 hasConceptScore W1544544572C152568617 @default.
- W1544544572 hasConceptScore W1544544572C179104552 @default.
- W1544544572 hasConceptScore W1544544572C185544564 @default.
- W1544544572 hasConceptScore W1544544572C185592680 @default.
- W1544544572 hasConceptScore W1544544572C191897082 @default.
- W1544544572 hasConceptScore W1544544572C192562407 @default.
- W1544544572 hasConceptScore W1544544572C20625102 @default.
- W1544544572 hasConceptScore W1544544572C25442681 @default.
- W1544544572 hasConceptScore W1544544572C2779851234 @default.
- W1544544572 hasConceptScore W1544544572C2780026712 @default.
- W1544544572 hasConceptScore W1544544572C2781099003 @default.
- W1544544572 hasConceptScore W1544544572C42360764 @default.
- W1544544572 hasConceptScore W1544544572C513153333 @default.
- W1544544572 hasConceptScore W1544544572C518881349 @default.
- W1544544572 hasConceptScore W1544544572C62520636 @default.
- W1544544572 hasLocation W15445445721 @default.
- W1544544572 hasOpenAccess W1544544572 @default.
- W1544544572 hasPrimaryLocation W15445445721 @default.
- W1544544572 hasRelatedWork W1986213545 @default.
- W1544544572 hasRelatedWork W2011874358 @default.
- W1544544572 hasRelatedWork W2014031115 @default.
- W1544544572 hasRelatedWork W2020216400 @default.
- W1544544572 hasRelatedWork W2024405110 @default.
- W1544544572 hasRelatedWork W2072953078 @default.
- W1544544572 hasRelatedWork W2073468290 @default.
- W1544544572 hasRelatedWork W2074225359 @default.
- W1544544572 hasRelatedWork W2093402795 @default.
- W1544544572 hasRelatedWork W2095376571 @default.
- W1544544572 hasRelatedWork W2156662275 @default.
- W1544544572 hasRelatedWork W2319667757 @default.
- W1544544572 hasRelatedWork W2334988517 @default.
- W1544544572 hasRelatedWork W251678916 @default.
- W1544544572 hasRelatedWork W2884075638 @default.
- W1544544572 hasRelatedWork W2937776197 @default.
- W1544544572 hasRelatedWork W3136490433 @default.
- W1544544572 hasRelatedWork W3184614149 @default.
- W1544544572 hasRelatedWork W321309022 @default.
- W1544544572 hasRelatedWork W608444196 @default.
- W1544544572 isParatext "false" @default.
- W1544544572 isRetracted "false" @default.
- W1544544572 magId "1544544572" @default.
- W1544544572 workType "dissertation" @default.