- W1556687018 abstract "Ferroelectric and insulating properties of sol-gel-derived and face-to-face annealed strontium bismuth tantalate (SBT) thin films were investigated, in which the precursor solutions in the form of Sr/sub 0.8/Bi/sub x/Ta/sub 2/O/sub 9/ were used and the x-value was changed from 2.0 to 2.4. The remanent polarization (2Pr) showed the maximum value at the Bi composition of 2.3. At this Bi composition, the 2Pr value of a face-to-face annealed SBT film crystallized at 750/spl deg/C was as large as 19.8 /spl mu/C/cm/sup 2/, while it was 16.7 /spl mu/C/cm/sup 2/ in a film without face-to-face annealing. It was also found from the time dependence of leakage current density that the minimum leakage current density of the face-to-face annealed SBT films at the Bi composition of 2.3 was lower than 1 nA/cm/sup 2/ at the electric field of 130 kV/cm." @default.
- W1556687018 created "2016-06-24" @default.
- W1556687018 creator A5062623956 @default.
- W1556687018 creator A5070010707 @default.
- W1556687018 creator A5070935901 @default.
- W1556687018 creator A5075968757 @default.
- W1556687018 date "2002-11-11" @default.
- W1556687018 modified "2023-09-23" @default.
- W1556687018 title "Ferroelectric properties of face-to-face annealed Sr/sub 0.8/Bi/sub x/Ta/sub 2/O/sub 9/ thin films" @default.
- W1556687018 cites W1637195705 @default.
- W1556687018 cites W1988928734 @default.
- W1556687018 cites W1989225731 @default.
- W1556687018 cites W1989410815 @default.
- W1556687018 cites W2036802251 @default.
- W1556687018 cites W2050060802 @default.
- W1556687018 cites W2082443998 @default.
- W1556687018 cites W2483605251 @default.
- W1556687018 doi "https://doi.org/10.1109/isaf.2000.942463" @default.
- W1556687018 hasPublicationYear "2002" @default.
- W1556687018 type Work @default.
- W1556687018 sameAs 1556687018 @default.
- W1556687018 citedByCount "0" @default.
- W1556687018 crossrefType "proceedings-article" @default.
- W1556687018 hasAuthorship W1556687018A5062623956 @default.
- W1556687018 hasAuthorship W1556687018A5070010707 @default.
- W1556687018 hasAuthorship W1556687018A5070935901 @default.
- W1556687018 hasAuthorship W1556687018A5075968757 @default.
- W1556687018 hasConcept C113196181 @default.
- W1556687018 hasConcept C133386390 @default.
- W1556687018 hasConcept C171250308 @default.
- W1556687018 hasConcept C185592680 @default.
- W1556687018 hasConcept C19067145 @default.
- W1556687018 hasConcept C191897082 @default.
- W1556687018 hasConcept C192562407 @default.
- W1556687018 hasConcept C2777303380 @default.
- W1556687018 hasConcept C2777855556 @default.
- W1556687018 hasConcept C43617362 @default.
- W1556687018 hasConcept C49040817 @default.
- W1556687018 hasConcept C533668322 @default.
- W1556687018 hasConcept C79090758 @default.
- W1556687018 hasConceptScore W1556687018C113196181 @default.
- W1556687018 hasConceptScore W1556687018C133386390 @default.
- W1556687018 hasConceptScore W1556687018C171250308 @default.
- W1556687018 hasConceptScore W1556687018C185592680 @default.
- W1556687018 hasConceptScore W1556687018C19067145 @default.
- W1556687018 hasConceptScore W1556687018C191897082 @default.
- W1556687018 hasConceptScore W1556687018C192562407 @default.
- W1556687018 hasConceptScore W1556687018C2777303380 @default.
- W1556687018 hasConceptScore W1556687018C2777855556 @default.
- W1556687018 hasConceptScore W1556687018C43617362 @default.
- W1556687018 hasConceptScore W1556687018C49040817 @default.
- W1556687018 hasConceptScore W1556687018C533668322 @default.
- W1556687018 hasConceptScore W1556687018C79090758 @default.
- W1556687018 hasLocation W15566870181 @default.
- W1556687018 hasOpenAccess W1556687018 @default.
- W1556687018 hasPrimaryLocation W15566870181 @default.
- W1556687018 hasRelatedWork W1662132949 @default.
- W1556687018 hasRelatedWork W1977345039 @default.
- W1556687018 hasRelatedWork W1999461156 @default.
- W1556687018 hasRelatedWork W2020561925 @default.
- W1556687018 hasRelatedWork W2039703849 @default.
- W1556687018 hasRelatedWork W2048843040 @default.
- W1556687018 hasRelatedWork W2054964629 @default.
- W1556687018 hasRelatedWork W2317988969 @default.
- W1556687018 hasRelatedWork W3151949860 @default.
- W1556687018 hasRelatedWork W4200206782 @default.
- W1556687018 isParatext "false" @default.
- W1556687018 isRetracted "false" @default.
- W1556687018 magId "1556687018" @default.
- W1556687018 workType "article" @default.