• W1556804143 abstract "Dielectric thin films of either TiO2 or BaTiO3 were sputtered in O2/Ar plasmas on Si wafers to thicknesses ranging from approximately 25 to 200 nm with patterned Ni or Pt electrodes sputtered in Ar plasmas at thicknesses from about 20 to 250 nm to form nano-capacitors. Statistical design of experiments (DOE) was used to determine the effects of the deposition power, plasma composition, and deposition temperature on the measured electrical properties of the nano-capacitors. Additional tests to determine the effects of the dielectric and electrode thickness on the measured dielectric responses of the devices were also undertaken. Characterization was performed with a combination of direct current (DC) and alternating current (AC) testing methods including AC impedance, coercive field and leakage current versus voltage, scanning electron microscopy, transmission electron microscopy (TEM), x-ray diffraction (XRD), x-ray photoelectron spectroscopy, focused ion beam microscopy, and atomic force microscopy. The dielectric properties were found to depend on complex interactions of the process variables that could be modeled using statistical software. The permittivity was found to range from 100 to 10,000 with losses between 0.013 and 0.570. The resistance at 1 V DC varied from approximately 1.5 to 360 GΩ, and either a ferroelectric or paraelectric hysteretic response was observed for all specimens tested. Chemical analyses showed the films to be oxygen rich, while XRD and TEM data indicated the BaTiO3 was amorphous. The electrical, chemical, and microstructural properties were found to depend on the sputtering conditions of the BaTiO3, dielectric thickness, electrode material choice, and the electrode thickness. Collectively, the results indicated that the properties of nanometer thick dielectric and electrode materials have a significant impact on the measured electrical properties." @default.
• W1556804143 created "2016-06-24" @default.
• W1556804143 creator A5056188023 @default.
• W1556804143 date "2008-01-01" @default.
• W1556804143 modified "2023-09-27" @default.
• W1556804143 title "Thin film techniques for the fabrication of nano-scale high energy density capacitors" @default.
• W1556804143 cites W1491964788 @default.
• W1556804143 cites W183576081 @default.
• W1556804143 cites W1964192055 @default.
• W1556804143 cites W1993317588 @default.
• W1556804143 cites W1993640316 @default.
• W1556804143 cites W2002480225 @default.
• W1556804143 cites W2006242157 @default.
• W1556804143 cites W2013508057 @default.
• W1556804143 cites W2040550991 @default.
• W1556804143 cites W2051920709 @default.
• W1556804143 cites W2073890388 @default.
• W1556804143 cites W2078000481 @default.
• W1556804143 cites W2085524287 @default.
• W1556804143 cites W2088488745 @default.
• W1556804143 cites W2088525793 @default.
• W1556804143 cites W2092036944 @default.
• W1556804143 cites W2092415735 @default.
• W1556804143 cites W2102149624 @default.
• W1556804143 cites W2110644670 @default.
• W1556804143 cites W2136175522 @default.
• W1556804143 cites W2143666585 @default.
• W1556804143 cites W2159192171 @default.
• W1556804143 cites W32545580 @default.
• W1556804143 cites W621379396 @default.
• W1556804143 cites W3134994101 @default.
• W1556804143 hasPublicationYear "2008" @default.
• W1556804143 type Work @default.
• W1556804143 sameAs 1556804143 @default.
• W1556804143 citedByCount "0" @default.
• W1556804143 crossrefType "journal-article" @default.
• W1556804143 hasAuthorship W1556804143A5056188023 @default.
• W1556804143 hasConcept C113196181 @default.
• W1556804143 hasConcept C119599485 @default.
• W1556804143 hasConcept C121332964 @default.
• W1556804143 hasConcept C127413603 @default.
• W1556804143 hasConcept C133386390 @default.
• W1556804143 hasConcept C146088050 @default.
• W1556804143 hasConcept C159985019 @default.
• W1556804143 hasConcept C165801399 @default.
• W1556804143 hasConcept C171250308 @default.
• W1556804143 hasConcept C175708663 @default.
• W1556804143 hasConcept C185592680 @default.
• W1556804143 hasConcept C19067145 @default.
• W1556804143 hasConcept C192562407 @default.
• W1556804143 hasConcept C22423302 @default.
• W1556804143 hasConcept C26771246 @default.
• W1556804143 hasConcept C43617362 @default.
• W1556804143 hasConcept C46141821 @default.
• W1556804143 hasConcept C49040817 @default.
• W1556804143 hasConcept C52192207 @default.
• W1556804143 hasConcept C56052488 @default.
• W1556804143 hasConcept C8010536 @default.
• W1556804143 hasConceptScore W1556804143C113196181 @default.
• W1556804143 hasConceptScore W1556804143C119599485 @default.
• W1556804143 hasConceptScore W1556804143C121332964 @default.
• W1556804143 hasConceptScore W1556804143C127413603 @default.
• W1556804143 hasConceptScore W1556804143C133386390 @default.
• W1556804143 hasConceptScore W1556804143C146088050 @default.
• W1556804143 hasConceptScore W1556804143C159985019 @default.
• W1556804143 hasConceptScore W1556804143C165801399 @default.
• W1556804143 hasConceptScore W1556804143C171250308 @default.
• W1556804143 hasConceptScore W1556804143C175708663 @default.
• W1556804143 hasConceptScore W1556804143C185592680 @default.
• W1556804143 hasConceptScore W1556804143C19067145 @default.
• W1556804143 hasConceptScore W1556804143C192562407 @default.
• W1556804143 hasConceptScore W1556804143C22423302 @default.
• W1556804143 hasConceptScore W1556804143C26771246 @default.
• W1556804143 hasConceptScore W1556804143C43617362 @default.
• W1556804143 hasConceptScore W1556804143C46141821 @default.
• W1556804143 hasConceptScore W1556804143C49040817 @default.
• W1556804143 hasConceptScore W1556804143C52192207 @default.
• W1556804143 hasConceptScore W1556804143C56052488 @default.
• W1556804143 hasConceptScore W1556804143C8010536 @default.
• W1556804143 hasLocation W15568041431 @default.
• W1556804143 hasOpenAccess W1556804143 @default.
• W1556804143 hasPrimaryLocation W15568041431 @default.
• W1556804143 hasRelatedWork W1510486425 @default.
• W1556804143 hasRelatedWork W1539289392 @default.
• W1556804143 hasRelatedWork W155349164 @default.
• W1556804143 hasRelatedWork W1607663753 @default.
• W1556804143 hasRelatedWork W1857690592 @default.
• W1556804143 hasRelatedWork W1970311002 @default.
• W1556804143 hasRelatedWork W1970619648 @default.
• W1556804143 hasRelatedWork W1975659754 @default.
• W1556804143 hasRelatedWork W2023285895 @default.
• W1556804143 hasRelatedWork W2027905844 @default.
• W1556804143 hasRelatedWork W2098744833 @default.
• W1556804143 hasRelatedWork W2112858299 @default.
• W1556804143 hasRelatedWork W2126272298 @default.
• W1556804143 hasRelatedWork W2126309615 @default.
• W1556804143 hasRelatedWork W2135962824 @default.
• W1556804143 hasRelatedWork W2341572539 @default.
• W1556804143 hasRelatedWork W2414976369 @default.
• W1556804143 hasRelatedWork W2153583220 @default.

• next