- W156192076 abstract "To determine the shear bond strength to dentin of five newer-generation self-etching adhesive systems.Flat bonding sites were prepared on 100 extracted human molar teeth with 600-grit silicon carbide paper, which exposed the dentin. The systems tested were: Clearfil SE Bond; Optibond Solo Plus Self-Etch; Xeno CF III; Tyrian SPE; and Adper Prompt L-Pop. Following application of each adhesive system, bonded assemblies of Z-100 were prepared using a gelatin capsule matrix (n = 20). Ten specimens in each group were debonded after water storage for 24 hours at 37 degrees C, and 10 were stored for at least 30 days, followed by thermocycling for 850 cycles between water baths at 5 degrees C and 55 degrees C, with a dwell time of 1 minute in each bath. Specimens were loaded to failure in an Instron Model 1123 testing machine with a crosshead speed of 5 mm/min. Statistical analysis included a two-way analysis of variance (adhesive and time) and Tukey's post hoc test.Mean shear bond strengths (MPa) at 24 hours were: Clearfil, 26.4+/-4.2; Optibond, 23.5+/-4.4; Xeno, 19.5+/-4.2; Tyrian, 16.5+/-3.7; and Adper, 15.3+/-3.3. Mean shear bond strengths (MPa) after storage and thermocycling were: Optibond, 27.5+/-5.7; Clearfil, 25.5+/-4.9; Adper, 21.5+/-3.3; Xeno, 20.4+/-2.2; and Tyrian, 19.2+/-6.4. Both adhesive system and storage time were significant factors affecting shear bond strength (P < .05).There are significant differences in the in vitro dentin shear bond strength among the self-etching adhesive materials tested. Water storage and thermocycling did not significantly degrade the shear bond strength of the materials in this study." @default.
- W156192076 created "2016-06-24" @default.
- W156192076 creator A5021519496 @default.
- W156192076 creator A5040020493 @default.
- W156192076 date "2005-04-01" @default.
- W156192076 modified "2023-10-18" @default.
- W156192076 title "Bond strength of composite to dentin using self-etching adhesive systems." @default.
- W156192076 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/15835421" @default.
- W156192076 hasPublicationYear "2005" @default.
- W156192076 type Work @default.
- W156192076 sameAs 156192076 @default.
- W156192076 citedByCount "19" @default.
- W156192076 countsByYear W1561920762012 @default.
- W156192076 countsByYear W1561920762013 @default.
- W156192076 countsByYear W1561920762014 @default.
- W156192076 countsByYear W1561920762015 @default.
- W156192076 countsByYear W1561920762021 @default.
- W156192076 countsByYear W1561920762023 @default.
- W156192076 crossrefType "journal-article" @default.
- W156192076 hasAuthorship W156192076A5021519496 @default.
- W156192076 hasAuthorship W156192076A5040020493 @default.
- W156192076 hasConcept C104779481 @default.
- W156192076 hasConcept C108797602 @default.
- W156192076 hasConcept C112950240 @default.
- W156192076 hasConcept C159096172 @default.
- W156192076 hasConcept C159985019 @default.
- W156192076 hasConcept C178405089 @default.
- W156192076 hasConcept C178790620 @default.
- W156192076 hasConcept C180478085 @default.
- W156192076 hasConcept C183300977 @default.
- W156192076 hasConcept C185592680 @default.
- W156192076 hasConcept C192562407 @default.
- W156192076 hasConcept C199343813 @default.
- W156192076 hasConcept C202271784 @default.
- W156192076 hasConcept C2779227376 @default.
- W156192076 hasConcept C2779263046 @default.
- W156192076 hasConcept C2781311116 @default.
- W156192076 hasConcept C68928338 @default.
- W156192076 hasConcept C71924100 @default.
- W156192076 hasConceptScore W156192076C104779481 @default.
- W156192076 hasConceptScore W156192076C108797602 @default.
- W156192076 hasConceptScore W156192076C112950240 @default.
- W156192076 hasConceptScore W156192076C159096172 @default.
- W156192076 hasConceptScore W156192076C159985019 @default.
- W156192076 hasConceptScore W156192076C178405089 @default.
- W156192076 hasConceptScore W156192076C178790620 @default.
- W156192076 hasConceptScore W156192076C180478085 @default.
- W156192076 hasConceptScore W156192076C183300977 @default.
- W156192076 hasConceptScore W156192076C185592680 @default.
- W156192076 hasConceptScore W156192076C192562407 @default.
- W156192076 hasConceptScore W156192076C199343813 @default.
- W156192076 hasConceptScore W156192076C202271784 @default.
- W156192076 hasConceptScore W156192076C2779227376 @default.
- W156192076 hasConceptScore W156192076C2779263046 @default.
- W156192076 hasConceptScore W156192076C2781311116 @default.
- W156192076 hasConceptScore W156192076C68928338 @default.
- W156192076 hasConceptScore W156192076C71924100 @default.
- W156192076 hasIssue "4" @default.
- W156192076 hasLocation W1561920761 @default.
- W156192076 hasOpenAccess W156192076 @default.
- W156192076 hasPrimaryLocation W1561920761 @default.
- W156192076 hasRelatedWork W2091680033 @default.
- W156192076 hasRelatedWork W2127583519 @default.
- W156192076 hasRelatedWork W2170927686 @default.
- W156192076 hasRelatedWork W2413394781 @default.
- W156192076 hasRelatedWork W2418195631 @default.
- W156192076 hasRelatedWork W2520041327 @default.
- W156192076 hasRelatedWork W2917739437 @default.
- W156192076 hasRelatedWork W2997383902 @default.
- W156192076 hasRelatedWork W4231735235 @default.
- W156192076 hasRelatedWork W1278977765 @default.
- W156192076 hasVolume "36" @default.
- W156192076 isParatext "false" @default.
- W156192076 isRetracted "false" @default.
- W156192076 magId "156192076" @default.
- W156192076 workType "article" @default.