- W1573438428 abstract "The weakness of nickel-based solid oxide fuel cell anodes is their low ability to withstand re-oxidation at working temperature, especially for the anode-supported cell design. The volume expansion coming along with nickel (Ni) oxidation induces stresses in the layers and cracks especially for the thin supported electrolyte. Standard Ni-yttria stabilized zirconia (YSZ) anode-supports and half-cells (anode + electrolyte) were studied during repeated reduction and oxidation cycles (RedOx cycles) at different scales and different temperatures. The nanometer scale observations point out that the internal porosity built up during nickel oxidation is the main reason for RedOx instability. This porosity arises from the Kirkendall effect during nickel oxidation. High temperature re-oxidation increases the internal porosity and thus the volume expansion of the anode. At the micrometer scale, the variation of electrolyte cracks and anode porosity could be related to linear expansion of the support. Linear expansion reaches a plateau after more than 10 RedOx cycles and a RedOx-safe temperature of 550 °C could be defined for this microstructure. At the macroscopic scale, the curvature towards the anode half-cell increases during a high temperature RedOx cycle. This increases RedOx instability and is related to the inhomogeneous re-oxidation of the anode across its thickness. The curvature change arises from non-elastic and non-homogeneous deformation of the support during re-oxidation. A Design of Experiment with Surface Response Methodology approach was used to optimize new microstructures for RedOx stability, electrical conductivity and sinterability of anode-supported SOFCs. The major anode internal parameter enhancing RedOx stability is the porosity. Some microstructures show RedOx stable anodes with a rather low 35 % as-sintered porosity, but with 50 % as-sintered porosity, any microstructure is believed to be RedOx stable. Three new different anode compositions, containing from 40 to 60 wt% NiO were produced by tape-casting and tested over more than 10 full RedOx cycles at 800 °C. The electrochemical tests show a constant open circuit voltage (OCV) and about 1 %/cycle of performance degradation between 0.4 and 0.5 Wcm-2 at 0.6 V and 800 °C. The electrical conductivity and electrochemical performance degradations versus time are important during the first reduction but are stabilized after multiple RedOx cycles. The nickel coarsening is limited after multiple RedOx cycles due to the pinning by small zirconia particle inclusions. An anode supported cell 55 cm2 in size with optimized microstructure was implemented in SOFC stack configuration and tested over 50 RedOx cycles. While the performance was nearly constant, the OCV decreased by only 0.1 %/cycle. The performance was three times lower compared to small cells, but shown to be due to poor electrical contact and limiting fuel flow and composition in the employed stack assembly." @default.
- W1573438428 created "2016-06-24" @default.
- W1573438428 creator A5071354042 @default.
- W1573438428 date "2011-01-01" @default.
- W1573438428 modified "2023-09-23" @default.
- W1573438428 title "RedOx Stability of Anode Supported Solid Oxide Fuel Cells" @default.
- W1573438428 doi "https://doi.org/10.5075/epfl-thesis-4893" @default.
- W1573438428 hasPublicationYear "2011" @default.
- W1573438428 type Work @default.
- W1573438428 sameAs 1573438428 @default.
- W1573438428 citedByCount "0" @default.
- W1573438428 crossrefType "journal-article" @default.
- W1573438428 hasAuthorship W1573438428A5071354042 @default.
- W1573438428 hasConcept C127413603 @default.
- W1573438428 hasConcept C147789679 @default.
- W1573438428 hasConcept C159985019 @default.
- W1573438428 hasConcept C17525397 @default.
- W1573438428 hasConcept C185592680 @default.
- W1573438428 hasConcept C191897082 @default.
- W1573438428 hasConcept C192562407 @default.
- W1573438428 hasConcept C2778456004 @default.
- W1573438428 hasConcept C2779851234 @default.
- W1573438428 hasConcept C42360764 @default.
- W1573438428 hasConcept C55904794 @default.
- W1573438428 hasConcept C6648577 @default.
- W1573438428 hasConcept C68801617 @default.
- W1573438428 hasConcept C87976508 @default.
- W1573438428 hasConcept C89395315 @default.
- W1573438428 hasConceptScore W1573438428C127413603 @default.
- W1573438428 hasConceptScore W1573438428C147789679 @default.
- W1573438428 hasConceptScore W1573438428C159985019 @default.
- W1573438428 hasConceptScore W1573438428C17525397 @default.
- W1573438428 hasConceptScore W1573438428C185592680 @default.
- W1573438428 hasConceptScore W1573438428C191897082 @default.
- W1573438428 hasConceptScore W1573438428C192562407 @default.
- W1573438428 hasConceptScore W1573438428C2778456004 @default.
- W1573438428 hasConceptScore W1573438428C2779851234 @default.
- W1573438428 hasConceptScore W1573438428C42360764 @default.
- W1573438428 hasConceptScore W1573438428C55904794 @default.
- W1573438428 hasConceptScore W1573438428C6648577 @default.
- W1573438428 hasConceptScore W1573438428C68801617 @default.
- W1573438428 hasConceptScore W1573438428C87976508 @default.
- W1573438428 hasConceptScore W1573438428C89395315 @default.
- W1573438428 hasLocation W15734384281 @default.
- W1573438428 hasOpenAccess W1573438428 @default.
- W1573438428 hasPrimaryLocation W15734384281 @default.
- W1573438428 hasRelatedWork W1968683794 @default.
- W1573438428 hasRelatedWork W1969798286 @default.
- W1573438428 hasRelatedWork W1980663031 @default.
- W1573438428 hasRelatedWork W1984014577 @default.
- W1573438428 hasRelatedWork W1989408771 @default.
- W1573438428 hasRelatedWork W2034262698 @default.
- W1573438428 hasRelatedWork W2043571108 @default.
- W1573438428 hasRelatedWork W2047209705 @default.
- W1573438428 hasRelatedWork W2058562068 @default.
- W1573438428 hasRelatedWork W2059289914 @default.
- W1573438428 hasRelatedWork W2061633194 @default.
- W1573438428 hasRelatedWork W2081003842 @default.
- W1573438428 hasRelatedWork W2086804145 @default.
- W1573438428 hasRelatedWork W2168256602 @default.
- W1573438428 hasRelatedWork W2310737822 @default.
- W1573438428 hasRelatedWork W2315186868 @default.
- W1573438428 hasRelatedWork W2482909823 @default.
- W1573438428 hasRelatedWork W261609648 @default.
- W1573438428 hasRelatedWork W3194670219 @default.
- W1573438428 hasRelatedWork W413619483 @default.
- W1573438428 isParatext "false" @default.
- W1573438428 isRetracted "false" @default.
- W1573438428 magId "1573438428" @default.
- W1573438428 workType "article" @default.