- W1583667519 abstract "For the alloy AZ91 (Mg-9.OAl-0.7Zn-0.13Mn) die cast specimens were subjected to torsion testing at 150, 180, 240, 300, 420 and 450C at 0.05 0.5 and 5.0 s -1 The as-cast specimens exhibited hot shortness at 360C and above; however in that domain, after prior thermomechanical processing (TMP) at 300C, they showed much improved properties (which were reported along with as-cast properties at 300C and below). For AZ31-Mn (Mg-3.2Al-1-1Zn-0.34Mn), AZ31 (Mg-2-8Al-0-88Zn-0.01Mn), AZ63 (Mg-5-5Al-2.7Zn-0.34Mn) and ZK60 (Mg-5.7Zn-0.65Zr-O-O1A]), the specimens were subjected to hot torsion testing in the range 180 to 450C and 0.01, 0.1, and 1.0 s -1 . In the temperature range below 300C flow curves rise to a peak with failure occurring immediately thereafter. Above 300C the flow curves exhibited a peak and a gradual decline towards steady state. The temperature and strain rate dependence of the strength is described by a sinh-Arrhenius equation with Q HW between 125 and 144 kJ/mol; this indicates control by climb in comparison with creep in the range 200-400C. The alloy strength and activation energy declined in the order AZ63, AZ31-Mn AZ91, AZ31 and ZK60, while ductility increased with decreasing strength. In working of Mg alloys from 150 to 450C, the flow curves harden to a peak and work soften to a steady state regime above 300C. At temperatures below 300C, twinning is observed initially to bring grains into more suitable slip orientations. At high T a substructure develops due to basal and prismatic slip, Forming cells of augmented misorientation first near the grain boundaries and later towards the grain cores. Near the peak, new grains appear along the old boundaries (mantle) as a result of dynamic recrystallization DRX but not in the core of the initial grains. As T rises, the new grains are larger and the mantle broader, enhanced DRX results in higher ductility. At intermediate T, shear bands form through alignment of mantle zones resulting in reduced grain sizes and higher misorientation. Dynamic recrystallization does not become general as in Cu or Ni, thus it does not markedly raise the ductility. Retention of the hot worked substructure, or the refined grains, improves the strength and ductility of the product." @default.
- W1583667519 created "2016-06-24" @default.
- W1583667519 creator A5082922233 @default.
- W1583667519 date "1997-01-01" @default.
- W1583667519 modified "2023-09-27" @default.
- W1583667519 title "Hot workability of magnesium alloys" @default.
- W1583667519 hasPublicationYear "1997" @default.
- W1583667519 type Work @default.
- W1583667519 sameAs 1583667519 @default.
- W1583667519 citedByCount "0" @default.
- W1583667519 crossrefType "dissertation" @default.
- W1583667519 hasAuthorship W1583667519A5082922233 @default.
- W1583667519 hasConcept C121332964 @default.
- W1583667519 hasConcept C141071460 @default.
- W1583667519 hasConcept C149912024 @default.
- W1583667519 hasConcept C159985019 @default.
- W1583667519 hasConcept C178790620 @default.
- W1583667519 hasConcept C185592680 @default.
- W1583667519 hasConcept C191897082 @default.
- W1583667519 hasConcept C192562407 @default.
- W1583667519 hasConcept C2780026712 @default.
- W1583667519 hasConcept C39353612 @default.
- W1583667519 hasConcept C543218039 @default.
- W1583667519 hasConcept C71924100 @default.
- W1583667519 hasConcept C77461463 @default.
- W1583667519 hasConcept C86183883 @default.
- W1583667519 hasConcept C95121573 @default.
- W1583667519 hasConcept C97355855 @default.
- W1583667519 hasConceptScore W1583667519C121332964 @default.
- W1583667519 hasConceptScore W1583667519C141071460 @default.
- W1583667519 hasConceptScore W1583667519C149912024 @default.
- W1583667519 hasConceptScore W1583667519C159985019 @default.
- W1583667519 hasConceptScore W1583667519C178790620 @default.
- W1583667519 hasConceptScore W1583667519C185592680 @default.
- W1583667519 hasConceptScore W1583667519C191897082 @default.
- W1583667519 hasConceptScore W1583667519C192562407 @default.
- W1583667519 hasConceptScore W1583667519C2780026712 @default.
- W1583667519 hasConceptScore W1583667519C39353612 @default.
- W1583667519 hasConceptScore W1583667519C543218039 @default.
- W1583667519 hasConceptScore W1583667519C71924100 @default.
- W1583667519 hasConceptScore W1583667519C77461463 @default.
- W1583667519 hasConceptScore W1583667519C86183883 @default.
- W1583667519 hasConceptScore W1583667519C95121573 @default.
- W1583667519 hasConceptScore W1583667519C97355855 @default.
- W1583667519 hasLocation W15836675191 @default.
- W1583667519 hasOpenAccess W1583667519 @default.
- W1583667519 hasPrimaryLocation W15836675191 @default.
- W1583667519 hasRelatedWork W1966355199 @default.
- W1583667519 hasRelatedWork W1968900969 @default.
- W1583667519 hasRelatedWork W1973960352 @default.
- W1583667519 hasRelatedWork W1980467093 @default.
- W1583667519 hasRelatedWork W1993508682 @default.
- W1583667519 hasRelatedWork W2000598280 @default.
- W1583667519 hasRelatedWork W2021286334 @default.
- W1583667519 hasRelatedWork W2038531611 @default.
- W1583667519 hasRelatedWork W2071255722 @default.
- W1583667519 hasRelatedWork W2076203727 @default.
- W1583667519 hasRelatedWork W2076462714 @default.
- W1583667519 hasRelatedWork W2286763846 @default.
- W1583667519 hasRelatedWork W2372278064 @default.
- W1583667519 hasRelatedWork W2387091584 @default.
- W1583667519 hasRelatedWork W2883341365 @default.
- W1583667519 hasRelatedWork W2886758168 @default.
- W1583667519 hasRelatedWork W3047961670 @default.
- W1583667519 hasRelatedWork W3081066206 @default.
- W1583667519 hasRelatedWork W3094296409 @default.
- W1583667519 hasRelatedWork W3135406617 @default.
- W1583667519 isParatext "false" @default.
- W1583667519 isRetracted "false" @default.
- W1583667519 magId "1583667519" @default.
- W1583667519 workType "dissertation" @default.