- W1585877443 abstract "Abstract : The principal fracture controlling parameters and the effects of welding thereon are discussed. From the results of tests on notched and welded specimens it was apparent that the effect on fracture behavior of the thermal and strain cycling that occurs during welding is not fully understood. Notched bend specimens subjected to a cycle of axial prestraining at temperatures usually in the range of 300 to 800F were tested to evaluate the fracture behavior of three structural steels, ABS-C, A212-B, and A441 steels. It was found that cracking occurred in some of the hotstrained specimens of ABS-C and A212-B steels at loads as low as 87 percent of the 'yield load' when they were tested at temperatures of -80 of +80F. One specimen of A441 steel also exhibited cracking at 88 percent of the 'yield load' at a temperature of -40F, but in most cases the hot-strained A441 steel specimens showed greater resistance to fracturing than those of the other two steels. Some of the notched bend specimens of the ABS-C steel exhibited cracking during the axial prestraining at a temperature in the range of 300 to 600F. Similarly, cracking occurred during welding at the root of notches in some of the notched and welded specimens of ABS-C steel. Specimens which cracked during hot-straining are apparently less susceptible to fracturing at low applied loads." @default.
- W1585877443 created "2016-06-24" @default.
- W1585877443 creator A5001312686 @default.
- W1585877443 creator A5004156807 @default.
- W1585877443 date "1967-02-01" @default.
- W1585877443 modified "2023-09-23" @default.
- W1585877443 title "Influence of Thermal and Strain Cycling on Fracture Susceptibility of Mild Steel" @default.
- W1585877443 hasPublicationYear "1967" @default.
- W1585877443 type Work @default.
- W1585877443 sameAs 1585877443 @default.
- W1585877443 citedByCount "0" @default.
- W1585877443 crossrefType "journal-article" @default.
- W1585877443 hasAuthorship W1585877443A5001312686 @default.
- W1585877443 hasAuthorship W1585877443A5004156807 @default.
- W1585877443 hasConcept C121332964 @default.
- W1585877443 hasConcept C153294291 @default.
- W1585877443 hasConcept C159985019 @default.
- W1585877443 hasConcept C177564732 @default.
- W1585877443 hasConcept C191897082 @default.
- W1585877443 hasConcept C192562407 @default.
- W1585877443 hasConcept C19474535 @default.
- W1585877443 hasConcept C204530211 @default.
- W1585877443 hasConcept C43369102 @default.
- W1585877443 hasConcept C58396970 @default.
- W1585877443 hasConceptScore W1585877443C121332964 @default.
- W1585877443 hasConceptScore W1585877443C153294291 @default.
- W1585877443 hasConceptScore W1585877443C159985019 @default.
- W1585877443 hasConceptScore W1585877443C177564732 @default.
- W1585877443 hasConceptScore W1585877443C191897082 @default.
- W1585877443 hasConceptScore W1585877443C192562407 @default.
- W1585877443 hasConceptScore W1585877443C19474535 @default.
- W1585877443 hasConceptScore W1585877443C204530211 @default.
- W1585877443 hasConceptScore W1585877443C43369102 @default.
- W1585877443 hasConceptScore W1585877443C58396970 @default.
- W1585877443 hasLocation W15858774431 @default.
- W1585877443 hasOpenAccess W1585877443 @default.
- W1585877443 hasPrimaryLocation W15858774431 @default.
- W1585877443 hasRelatedWork W1964811186 @default.
- W1585877443 hasRelatedWork W1988840612 @default.
- W1585877443 hasRelatedWork W1995904593 @default.
- W1585877443 hasRelatedWork W2017988497 @default.
- W1585877443 hasRelatedWork W2086258650 @default.
- W1585877443 hasRelatedWork W2176459813 @default.
- W1585877443 hasRelatedWork W2254158088 @default.
- W1585877443 hasRelatedWork W2315456970 @default.
- W1585877443 hasRelatedWork W2321645272 @default.
- W1585877443 hasRelatedWork W2327744411 @default.
- W1585877443 hasRelatedWork W2331620584 @default.
- W1585877443 hasRelatedWork W2378509564 @default.
- W1585877443 hasRelatedWork W2390703578 @default.
- W1585877443 hasRelatedWork W2484862095 @default.
- W1585877443 hasRelatedWork W2556010937 @default.
- W1585877443 hasRelatedWork W286240940 @default.
- W1585877443 hasRelatedWork W2948437343 @default.
- W1585877443 hasRelatedWork W3006615672 @default.
- W1585877443 hasRelatedWork W3173547473 @default.
- W1585877443 hasRelatedWork W1524488554 @default.
- W1585877443 isParatext "false" @default.
- W1585877443 isRetracted "false" @default.
- W1585877443 magId "1585877443" @default.
- W1585877443 workType "article" @default.