• W1604497103 abstract "A study of the resistance of polyurethane films to various swelling and degrading environments was carried out. Physical properties of the resulting polymers were correlated with chemical variations in the polyether and isocyanate structures. Thermal resistance was determined by various techniques, including differential thermal analysis, thermogravimetric analysis, and heat aging. High crosslink density and the use of polyisocyanates of high aromatic content resulted in increased thermal stability. Resistance to moisture at high temperatures was also found to increase with crosslink density; it was influenced by the type of polyol and isocyanate used in the urethane reaction. Solvent resistance of polyurethane structures increased at higher crosslink densities, appeared to be unaffected by the type of aromatic diisocyanate, and was reduced with the use of a large excess of isocyanate. The ultraviolet resistance of films prepared from various isocyanates decreased in the order: tolylene diisocyanate (TDI) > polyphenyl polymethylene polyisocyanate (PAPI) > xylylene diisocyanate (XDI).Une etude de la resistance des films de polyurethane a differents agents de gonflement et de degradation a ete effectuee. Les proprietes physiques des polymeres resultants ont ete reliees aux variations chimiques des structures polyether et isocyanates. La resistance thermique a ete determinee par differentes techniques, y compris l'analyse thermique differentielle, l'analyse thermogravimetrique et les vieillissements a la chaleur. Une haute densite de pontage et l'utilisation de polyisocyanates a composants aromatiques ont comme effets une stabilite thermique accrue. La resistance a l'humidite a temperature elevee a egalement ete trouvee croitre avec la densite de pontage; elle est influencee par le type de polyol et d'isocyanate utilise dans la reaction urethane. La resistance aux solvants des structures polyurethaniques croit aved la densite de pontage plus elevee; elle semble etre non-affectee par le type de diisocyanate aromatique et decroit avec l'utilisation d'un grand exces d'isocyanate. La resistance a l'ultraviolet de films prepares au depart de differents diisocyanates decroit dans l'ordre: toluene diisocyanate (TDI > polyphenyl, polymethylene, polyisocyanate (PAPI) > xylylene diisocyanate (XDI).Eine Untersuchung der Bestandigkeit von Polyurethanfilmen gegen verschiedene Quellungs- und Abbaubedingungen wurde ausgefuhrt. Die physikalischen Eigenschaften der entstehenden Polymeren wurden zu chemischen Veranderungen der Polyather- und Isocyanatstrukturen in Beziehung gestellt. Die Warmebestandigkeit wurde nach verschiedenen Methoden, namlich Differentialthermoanalyse, thermogravimetrische Analyse und Hitzealterung, bestimmt. Hohe Vernetzungsdichte und die Verwendung von Polyisocyanaten mit hohem Aromatengehalt fuhrten zu erhohter Warmebestandigkeit. Auch die Feuchtigkeitsbestandigkeit bei hoher Temperatur nahm mit der Vernetzungsdichte zu; sie wurde vom Typ des bei der Urethanreaktion verwendeten Polyols und Isocyanates beeinflusst. Die Losungsmittelbestandigkeit von Polyurethanstrukturen nahm bei hoherer Vernetzungsdichte zu, schien vom Typ des aromatischen Diisocyanates unbeeinflusst zu sein und wurde durch Verwendung eines grossen Isocyanatuberschusses herabgesetzt. Die Ultraviolettbestandigkeit der aus verschiedenen Isocyanaten dargestellten Filme nahm in der Reihenfolge: Toluylendiisocyanat (TDI) > Polyphenylpolymethylen-polyisocyanat (PAPI) > Xylylendiisocyanat (XDI) ab." @default.
• W1604497103 created "2016-06-24" @default.
• W1604497103 creator A5038008376 @default.
• W1604497103 creator A5063140920 @default.
• W1604497103 date "1967-01-01" @default.
• W1604497103 modified "2023-09-25" @default.
• W1604497103 title "The effect of chemical structure on thermal, hydrolytic, and solvent resistance of polyurethane films" @default.
• W1604497103 cites W1969571315 @default.
• W1604497103 cites W1990699044 @default.
• W1604497103 cites W2034389664 @default.
• W1604497103 cites W2034832040 @default.
• W1604497103 cites W2036807223 @default.
• W1604497103 cites W2038628055 @default.
• W1604497103 cites W2081584494 @default.
• W1604497103 cites W2086369649 @default.
• W1604497103 cites W2095503438 @default.
• W1604497103 cites W2099235107 @default.
• W1604497103 cites W2125249495 @default.
• W1604497103 cites W2148688626 @default.
• W1604497103 cites W2151148535 @default.
• W1604497103 cites W2165260755 @default.
• W1604497103 cites W2178415171 @default.
• W1604497103 cites W2219729996 @default.
• W1604497103 cites W2316028853 @default.
• W1604497103 cites W2319342026 @default.
• W1604497103 cites W385197745 @default.
• W1604497103 doi "https://doi.org/10.1002/polc.5070160527" @default.
• W1604497103 hasPublicationYear "1967" @default.
• W1604497103 type Work @default.
• W1604497103 sameAs 1604497103 @default.
• W1604497103 citedByCount "6" @default.
• W1604497103 crossrefType "journal-article" @default.
• W1604497103 hasAuthorship W1604497103A5038008376 @default.
• W1604497103 hasAuthorship W1604497103A5063140920 @default.
• W1604497103 hasConcept C15920480 @default.
• W1604497103 hasConcept C159985019 @default.
• W1604497103 hasConcept C178790620 @default.
• W1604497103 hasConcept C185592680 @default.
• W1604497103 hasConcept C188027245 @default.
• W1604497103 hasConcept C192562407 @default.
• W1604497103 hasConcept C2779578285 @default.
• W1604497103 hasConcept C2779887276 @default.
• W1604497103 hasConcept C2780290348 @default.
• W1604497103 hasConcept C2780471494 @default.
• W1604497103 hasConcept C2780534471 @default.
• W1604497103 hasConcept C521977710 @default.
• W1604497103 hasConcept C59061564 @default.
• W1604497103 hasConcept C60100273 @default.
• W1604497103 hasConceptScore W1604497103C15920480 @default.
• W1604497103 hasConceptScore W1604497103C159985019 @default.
• W1604497103 hasConceptScore W1604497103C178790620 @default.
• W1604497103 hasConceptScore W1604497103C185592680 @default.
• W1604497103 hasConceptScore W1604497103C188027245 @default.
• W1604497103 hasConceptScore W1604497103C192562407 @default.
• W1604497103 hasConceptScore W1604497103C2779578285 @default.
• W1604497103 hasConceptScore W1604497103C2779887276 @default.
• W1604497103 hasConceptScore W1604497103C2780290348 @default.
• W1604497103 hasConceptScore W1604497103C2780471494 @default.
• W1604497103 hasConceptScore W1604497103C2780534471 @default.
• W1604497103 hasConceptScore W1604497103C521977710 @default.
• W1604497103 hasConceptScore W1604497103C59061564 @default.
• W1604497103 hasConceptScore W1604497103C60100273 @default.
• W1604497103 hasIssue "5" @default.
• W1604497103 hasLocation W16044971031 @default.
• W1604497103 hasOpenAccess W1604497103 @default.
• W1604497103 hasPrimaryLocation W16044971031 @default.
• W1604497103 hasVolume "16" @default.
• W1604497103 isParatext "false" @default.
• W1604497103 isRetracted "false" @default.
• W1604497103 magId "1604497103" @default.
• W1604497103 workType "article" @default.