• W1620027451 abstract "The 5 wt.% Al2O3-coated Li1.20Mn0.55Ni0.16Co0.09O2 was prepared by the mechanochemical reaction. The optimal condition for sample preparation was determined to be the rotation speed of 2000 rpm and the reaction time of 5 min by SEM, XRD, and XANES measurements. Surface analysis using XANES data demonstrated that all the samples were rather uniformly covered with nano-Al2O3 particles. The pristine and 5 wt.% Al2O3-coated samples after the stepwise pre-cycling treatment showed the discharge capacity of 243 and 216 mAh/g at 323 K, respectively. Although the Al2O3-coated sample showed less discharge capacity compared with the pristine sample, the Al2O3-coated sample showed better discharge capacity retention compared with the pristine sample after 35 cycles at 323 K. These results demonstrate that the mechanochemical Al2O3-coating process is an effective way of improving the cycle performance at high temperature." @default.
• W1620027451 created "2016-06-24" @default.
• W1620027451 creator A5001864383 @default.
• W1620027451 creator A5022926836 @default.
• W1620027451 creator A5023000287 @default.
• W1620027451 creator A5023087031 @default.
• W1620027451 creator A5024318252 @default.
• W1620027451 creator A5048602027 @default.
• W1620027451 date "2014-09-01" @default.
• W1620027451 modified "2023-10-14" @default.
• W1620027451 title "The effects of Al2O3 coating on the performance of layered Li1.20Mn0.55Ni0.16Co0.09O2 materials for lithium-ion rechargeable battery" @default.
• W1620027451 cites W1550595230 @default.
• W1620027451 cites W1968075514 @default.
• W1620027451 cites W1972295088 @default.
• W1620027451 cites W1982926166 @default.
• W1620027451 cites W1990261680 @default.
• W1620027451 cites W1994508715 @default.
• W1620027451 cites W2012573811 @default.
• W1620027451 cites W2017699547 @default.
• W1620027451 cites W2031725186 @default.
• W1620027451 cites W2044077630 @default.
• W1620027451 cites W2055130990 @default.
• W1620027451 cites W2056244208 @default.
• W1620027451 cites W2067277817 @default.
• W1620027451 cites W2069419870 @default.
• W1620027451 cites W2075087780 @default.
• W1620027451 cites W2079607738 @default.
• W1620027451 cites W2084351950 @default.
• W1620027451 cites W2164438036 @default.
• W1620027451 cites W2205329437 @default.
• W1620027451 cites W2398620784 @default.
• W1620027451 doi "https://doi.org/10.1016/j.ssi.2013.09.045" @default.
• W1620027451 hasPublicationYear "2014" @default.
• W1620027451 type Work @default.
• W1620027451 sameAs 1620027451 @default.
• W1620027451 citedByCount "19" @default.
• W1620027451 countsByYear W16200274512014 @default.
• W1620027451 countsByYear W16200274512015 @default.
• W1620027451 countsByYear W16200274512016 @default.
• W1620027451 countsByYear W16200274512017 @default.
• W1620027451 countsByYear W16200274512018 @default.
• W1620027451 countsByYear W16200274512019 @default.
• W1620027451 countsByYear W16200274512020 @default.
• W1620027451 countsByYear W16200274512022 @default.
• W1620027451 crossrefType "journal-article" @default.
• W1620027451 hasAuthorship W1620027451A5001864383 @default.
• W1620027451 hasAuthorship W1620027451A5022926836 @default.
• W1620027451 hasAuthorship W1620027451A5023000287 @default.
• W1620027451 hasAuthorship W1620027451A5023087031 @default.
• W1620027451 hasAuthorship W1620027451A5024318252 @default.
• W1620027451 hasAuthorship W1620027451A5048602027 @default.
• W1620027451 hasConcept C110715899 @default.
• W1620027451 hasConcept C113196181 @default.
• W1620027451 hasConcept C121332964 @default.
• W1620027451 hasConcept C127413603 @default.
• W1620027451 hasConcept C134018914 @default.
• W1620027451 hasConcept C145148216 @default.
• W1620027451 hasConcept C159985019 @default.
• W1620027451 hasConcept C163258240 @default.
• W1620027451 hasConcept C178790620 @default.
• W1620027451 hasConcept C185592680 @default.
• W1620027451 hasConcept C192562407 @default.
• W1620027451 hasConcept C2778541603 @default.
• W1620027451 hasConcept C2779197387 @default.
• W1620027451 hasConcept C2781448156 @default.
• W1620027451 hasConcept C32891209 @default.
• W1620027451 hasConcept C42360764 @default.
• W1620027451 hasConcept C43617362 @default.
• W1620027451 hasConcept C555008776 @default.
• W1620027451 hasConcept C62520636 @default.
• W1620027451 hasConcept C71924100 @default.
• W1620027451 hasConceptScore W1620027451C110715899 @default.
• W1620027451 hasConceptScore W1620027451C113196181 @default.
• W1620027451 hasConceptScore W1620027451C121332964 @default.
• W1620027451 hasConceptScore W1620027451C127413603 @default.
• W1620027451 hasConceptScore W1620027451C134018914 @default.
• W1620027451 hasConceptScore W1620027451C145148216 @default.
• W1620027451 hasConceptScore W1620027451C159985019 @default.
• W1620027451 hasConceptScore W1620027451C163258240 @default.
• W1620027451 hasConceptScore W1620027451C178790620 @default.
• W1620027451 hasConceptScore W1620027451C185592680 @default.
• W1620027451 hasConceptScore W1620027451C192562407 @default.
• W1620027451 hasConceptScore W1620027451C2778541603 @default.
• W1620027451 hasConceptScore W1620027451C2779197387 @default.
• W1620027451 hasConceptScore W1620027451C2781448156 @default.
• W1620027451 hasConceptScore W1620027451C32891209 @default.
• W1620027451 hasConceptScore W1620027451C42360764 @default.
• W1620027451 hasConceptScore W1620027451C43617362 @default.
• W1620027451 hasConceptScore W1620027451C555008776 @default.
• W1620027451 hasConceptScore W1620027451C62520636 @default.
• W1620027451 hasConceptScore W1620027451C71924100 @default.
• W1620027451 hasLocation W16200274511 @default.
• W1620027451 hasOpenAccess W1620027451 @default.
• W1620027451 hasPrimaryLocation W16200274511 @default.
• W1620027451 hasRelatedWork W1959830367 @default.
• W1620027451 hasRelatedWork W2007739424 @default.
• W1620027451 hasRelatedWork W2335674404 @default.
• W1620027451 hasRelatedWork W2527667974 @default.

• next