- W1640940015 abstract "A study of the response of several nickel aluminide alloys to SigmaJig testing was done to examine their weld solidification cracking behavior and the effect of Zr concentration. The alloys were based on the Ni-8Al-7.7Cr-1.5Mo-0.003B wt% composition and contained Zr concentrations of 3, 4.5, and 6 wt%. Vacuum induction melted ingots with a diameter of 2.7 in and weight about 18 lb were made of each alloy, and were used to make 2 x 2 x 0.030 in specimens for the Sigmajig test. The gas tungsten arc welds were made at travel speeds of 10, 20, and 30 ipm with heat inputs of 2--2.5 kJ/in. When an arc was established before traveling onto the test specimen centerline cracking was always observed. This problem was overcome by initiating the arc directly on the specimens. Using this approach, the 3 wt% Zr alloy withstood an applied stress of 24 ksi without cracking at a welding speed of 10 ipm. This alloy cracked at 4 ksi applied at 20 ipm, and with no applied load at 30 ipm. Only limited testing was done on the remaining alloys, but the results indicate that resistance to solidification cracking increases with Zr concentration. Zirconium has limited solid solubility and segregates strongly to interdendritic regions during solidification where it forms a Ni solid solution-Ni{sub 5}Zr eutectic. The volume fraction of the eutectic increases with Zr concentration. The solidification cracking behavior of these alloys is consistent with phenomenological theory, and is discussed in this context. The results from SigmaJig testing are analyzed using finite element modeling of the development of mechanical strains during solidification of welds. Experimental data from the test substantially agree with recent analysis results." @default.
- W1640940015 created "2016-06-24" @default.
- W1640940015 creator A5055364655 @default.
- W1640940015 creator A5056189990 @default.
- W1640940015 date "1995-09-01" @default.
- W1640940015 modified "2023-09-25" @default.
- W1640940015 title "Analysis of weld solidification cracking in cast nickel aluminide alloys" @default.
- W1640940015 cites W239624880 @default.
- W1640940015 doi "https://doi.org/10.2172/102247" @default.
- W1640940015 hasPublicationYear "1995" @default.
- W1640940015 type Work @default.
- W1640940015 sameAs 1640940015 @default.
- W1640940015 citedByCount "0" @default.
- W1640940015 crossrefType "report" @default.
- W1640940015 hasAuthorship W1640940015A5055364655 @default.
- W1640940015 hasAuthorship W1640940015A5056189990 @default.
- W1640940015 hasConcept C159985019 @default.
- W1640940015 hasConcept C18168003 @default.
- W1640940015 hasConcept C191897082 @default.
- W1640940015 hasConcept C192562407 @default.
- W1640940015 hasConcept C19474535 @default.
- W1640940015 hasConcept C27501479 @default.
- W1640940015 hasConcept C2777240487 @default.
- W1640940015 hasConcept C2778537444 @default.
- W1640940015 hasConcept C2780026712 @default.
- W1640940015 hasConcept C2780289051 @default.
- W1640940015 hasConcept C2781372787 @default.
- W1640940015 hasConcept C534791751 @default.
- W1640940015 hasConcept C58396970 @default.
- W1640940015 hasConcept C65590680 @default.
- W1640940015 hasConceptScore W1640940015C159985019 @default.
- W1640940015 hasConceptScore W1640940015C18168003 @default.
- W1640940015 hasConceptScore W1640940015C191897082 @default.
- W1640940015 hasConceptScore W1640940015C192562407 @default.
- W1640940015 hasConceptScore W1640940015C19474535 @default.
- W1640940015 hasConceptScore W1640940015C27501479 @default.
- W1640940015 hasConceptScore W1640940015C2777240487 @default.
- W1640940015 hasConceptScore W1640940015C2778537444 @default.
- W1640940015 hasConceptScore W1640940015C2780026712 @default.
- W1640940015 hasConceptScore W1640940015C2780289051 @default.
- W1640940015 hasConceptScore W1640940015C2781372787 @default.
- W1640940015 hasConceptScore W1640940015C534791751 @default.
- W1640940015 hasConceptScore W1640940015C58396970 @default.
- W1640940015 hasConceptScore W1640940015C65590680 @default.
- W1640940015 hasLocation W16409400151 @default.
- W1640940015 hasLocation W16409400152 @default.
- W1640940015 hasOpenAccess W1640940015 @default.
- W1640940015 hasPrimaryLocation W16409400151 @default.
- W1640940015 hasRelatedWork W2068805119 @default.
- W1640940015 hasRelatedWork W2084225513 @default.
- W1640940015 hasRelatedWork W2092397426 @default.
- W1640940015 hasRelatedWork W2116848758 @default.
- W1640940015 hasRelatedWork W2352982341 @default.
- W1640940015 hasRelatedWork W2789316799 @default.
- W1640940015 hasRelatedWork W3092071701 @default.
- W1640940015 hasRelatedWork W4238199672 @default.
- W1640940015 hasRelatedWork W4250486179 @default.
- W1640940015 hasRelatedWork W4362455380 @default.
- W1640940015 isParatext "false" @default.
- W1640940015 isRetracted "false" @default.
- W1640940015 magId "1640940015" @default.
- W1640940015 workType "report" @default.