- W165199781 abstract "Contents of calcium fluoride in steel making slags and fluorspars were analyzed by determining fluorine using non-destructive 14 MeV neutron activation analysis.A dual sample irradiation assembly was used to irradiate an analytical sample and an external reference sample of a definite amount of calcium fluoride at the same time. Amounts of fluorine were determined from the ratio of counts of photo peak areas of 0.197 MeV energy of 19O calculated by the TPA method in each spectrum of the analytical and the external reference sample.Decay curves of gross counts, bakground counts and photo peak area counts were analyzed by the least square method using 19O, 16N, 18F and 28Al as the factors. The results confirmed that 19O was interfered by only 16N when the counts of photo peak were used for calculation.Experimental conditions obtained from the investigation of the optimum conditions of activation analysis and those obtained from the experimental results of the ratio of photo peak/background were in good agreement.For the actual analytical conditions, however, the sample decay duration longer than the calculated optimum was chosen to decay 16N. Analytical conditions of 30 s for the sample irradiation, 60 s for decay, and 15 s for the measurement were used. Even if the weight of oxygen present in steel making slags is 30 times as much as fluorine, the contribution of 16N on counts of 19O photo peak area was suppressed down to about 4% of the counts using this analytical condition.There was a significant difference between the gradients of the calibration curves made by synthetic steel making slags containing various materials and by calcium fluoride standards which did not contain any other material. Therefore, it is necessary to use the calibration curves for both the group of steel making slags and the group of calucium fluoride and fluorspars.The results obtained by this method were compared with those by the pyro-hydrolytic method showing good agreement in the entire range of fluorine concentrations." @default.
- W165199781 created "2016-06-24" @default.
- W165199781 creator A5029247381 @default.
- W165199781 date "1978-01-01" @default.
- W165199781 modified "2023-10-16" @default.
- W165199781 title "Determination of Fluorine in Steel Making Slags by 14 MeV Neutron Activation Analysis" @default.
- W165199781 doi "https://doi.org/10.2320/jinstmet1952.42.12_1161" @default.
- W165199781 hasPublicationYear "1978" @default.
- W165199781 type Work @default.
- W165199781 sameAs 165199781 @default.
- W165199781 citedByCount "0" @default.
- W165199781 crossrefType "journal-article" @default.
- W165199781 hasAuthorship W165199781A5029247381 @default.
- W165199781 hasBestOaLocation W1651997811 @default.
- W165199781 hasConcept C111337013 @default.
- W165199781 hasConcept C113196181 @default.
- W165199781 hasConcept C121332964 @default.
- W165199781 hasConcept C177322064 @default.
- W165199781 hasConcept C179104552 @default.
- W165199781 hasConcept C185544564 @default.
- W165199781 hasConcept C185592680 @default.
- W165199781 hasConcept C191897082 @default.
- W165199781 hasConcept C192562407 @default.
- W165199781 hasConcept C2780828025 @default.
- W165199781 hasConcept C43617362 @default.
- W165199781 hasConcept C4666530 @default.
- W165199781 hasConcept C506198293 @default.
- W165199781 hasConceptScore W165199781C111337013 @default.
- W165199781 hasConceptScore W165199781C113196181 @default.
- W165199781 hasConceptScore W165199781C121332964 @default.
- W165199781 hasConceptScore W165199781C177322064 @default.
- W165199781 hasConceptScore W165199781C179104552 @default.
- W165199781 hasConceptScore W165199781C185544564 @default.
- W165199781 hasConceptScore W165199781C185592680 @default.
- W165199781 hasConceptScore W165199781C191897082 @default.
- W165199781 hasConceptScore W165199781C192562407 @default.
- W165199781 hasConceptScore W165199781C2780828025 @default.
- W165199781 hasConceptScore W165199781C43617362 @default.
- W165199781 hasConceptScore W165199781C4666530 @default.
- W165199781 hasConceptScore W165199781C506198293 @default.
- W165199781 hasIssue "12" @default.
- W165199781 hasLocation W1651997811 @default.
- W165199781 hasOpenAccess W165199781 @default.
- W165199781 hasPrimaryLocation W1651997811 @default.
- W165199781 hasRelatedWork W1982039542 @default.
- W165199781 hasRelatedWork W1985458910 @default.
- W165199781 hasRelatedWork W2015533237 @default.
- W165199781 hasRelatedWork W2025556684 @default.
- W165199781 hasRelatedWork W2025922906 @default.
- W165199781 hasRelatedWork W202785632 @default.
- W165199781 hasRelatedWork W2033039978 @default.
- W165199781 hasRelatedWork W2066764218 @default.
- W165199781 hasRelatedWork W2072784152 @default.
- W165199781 hasRelatedWork W2613251200 @default.
- W165199781 hasVolume "42" @default.
- W165199781 isParatext "false" @default.
- W165199781 isRetracted "false" @default.
- W165199781 magId "165199781" @default.
- W165199781 workType "article" @default.