- W174476677 abstract "The purpose of this study was to evaluate the effect of etching and silane priming on bond strength to a feldspathic porcelain (VMK 68) of a composite resin (Clearfil APX). Two hydrofluoric acid etchants (2.5% and 5%) and seven different etching times (0, 30, 60, 90, 120, 150, and 180 seconds) were used to etch the porcelain specimens respectively. A self-curing bonding agent containing a silane coupler (Clearfil Porcelain Bond) was used on both etched and unetched porcelain surfaces. Etched relief patterns were observed by means of a scanning electron microscope, and the bond strengths between the photocured composite resin and the porcelain were determined. Scanning electron micrographs revealed complicated etching patterns with increased etching time periods. Shear testing results showed that the bond strength to the unetched porcelain of the composite resin was very low, and that etching periods for more than 30 seconds effectively enhanced the bond strength. Of the two etching agents applied to the unsilanated porcelain, the buffered 2.5% etchant produced higher bond strengths than the 5% etchant for all etching time periods except for 180 seconds. Silane priming was effective and critical for improving bond strength to the porcelain. Application of the silane bonding agent to the porcelain after hydrofluoric acid etching appeared to be suitable for achieving consistent bonding between the composite resin and the porcelain." @default.
- W174476677 created "2016-06-24" @default.
- W174476677 creator A5041893900 @default.
- W174476677 creator A5059955076 @default.
- W174476677 creator A5088493760 @default.
- W174476677 date "1998-12-24" @default.
- W174476677 modified "2023-09-23" @default.
- W174476677 title "Effect of etchant, etching period, and silane priming on bond strength to porcelain of composite resin." @default.
- W174476677 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/9863446" @default.
- W174476677 hasPublicationYear "1998" @default.
- W174476677 type Work @default.
- W174476677 sameAs 174476677 @default.
- W174476677 citedByCount "55" @default.
- W174476677 countsByYear W1744766772012 @default.
- W174476677 countsByYear W1744766772013 @default.
- W174476677 countsByYear W1744766772014 @default.
- W174476677 countsByYear W1744766772015 @default.
- W174476677 countsByYear W1744766772016 @default.
- W174476677 countsByYear W1744766772017 @default.
- W174476677 countsByYear W1744766772018 @default.
- W174476677 countsByYear W1744766772019 @default.
- W174476677 countsByYear W1744766772020 @default.
- W174476677 countsByYear W1744766772021 @default.
- W174476677 countsByYear W1744766772022 @default.
- W174476677 crossrefType "journal-article" @default.
- W174476677 hasAuthorship W174476677A5041893900 @default.
- W174476677 hasAuthorship W174476677A5059955076 @default.
- W174476677 hasAuthorship W174476677A5088493760 @default.
- W174476677 hasConcept C100460472 @default.
- W174476677 hasConcept C100701293 @default.
- W174476677 hasConcept C104779481 @default.
- W174476677 hasConcept C159096172 @default.
- W174476677 hasConcept C159985019 @default.
- W174476677 hasConcept C191897082 @default.
- W174476677 hasConcept C192562407 @default.
- W174476677 hasConcept C26771246 @default.
- W174476677 hasConcept C2776967294 @default.
- W174476677 hasConcept C2778024649 @default.
- W174476677 hasConcept C2779227376 @default.
- W174476677 hasConcept C59822182 @default.
- W174476677 hasConcept C68928338 @default.
- W174476677 hasConcept C81444415 @default.
- W174476677 hasConcept C86803240 @default.
- W174476677 hasConceptScore W174476677C100460472 @default.
- W174476677 hasConceptScore W174476677C100701293 @default.
- W174476677 hasConceptScore W174476677C104779481 @default.
- W174476677 hasConceptScore W174476677C159096172 @default.
- W174476677 hasConceptScore W174476677C159985019 @default.
- W174476677 hasConceptScore W174476677C191897082 @default.
- W174476677 hasConceptScore W174476677C192562407 @default.
- W174476677 hasConceptScore W174476677C26771246 @default.
- W174476677 hasConceptScore W174476677C2776967294 @default.
- W174476677 hasConceptScore W174476677C2778024649 @default.
- W174476677 hasConceptScore W174476677C2779227376 @default.
- W174476677 hasConceptScore W174476677C59822182 @default.
- W174476677 hasConceptScore W174476677C68928338 @default.
- W174476677 hasConceptScore W174476677C81444415 @default.
- W174476677 hasConceptScore W174476677C86803240 @default.
- W174476677 hasIssue "5" @default.
- W174476677 hasLocation W1744766771 @default.
- W174476677 hasOpenAccess W174476677 @default.
- W174476677 hasPrimaryLocation W1744766771 @default.
- W174476677 hasRelatedWork W174476677 @default.
- W174476677 hasRelatedWork W1984154518 @default.
- W174476677 hasRelatedWork W1990295344 @default.
- W174476677 hasRelatedWork W1999241991 @default.
- W174476677 hasRelatedWork W2353429225 @default.
- W174476677 hasRelatedWork W2370638742 @default.
- W174476677 hasRelatedWork W2461337726 @default.
- W174476677 hasRelatedWork W3036781689 @default.
- W174476677 hasRelatedWork W3149533641 @default.
- W174476677 hasRelatedWork W852971756 @default.
- W174476677 hasVolume "23" @default.
- W174476677 isParatext "false" @default.
- W174476677 isRetracted "false" @default.
- W174476677 magId "174476677" @default.
- W174476677 workType "article" @default.