- W1755141937 abstract "In the present study, mechanical alloying (MA) was used to deposit well-bonded TiC coatings on D2 steel substrates from titanium and carbon powders. The effect of milling duration and ball-to-powder mass ratio (BPMR), as well as the effect of substrate hardening has been investigated. Microstructure of the coated samples was studied by scanning electron microscopy (SEM). Chemical composition was analyzed by energy dispersive X-ray spectroscopy (EDS). Transmission electron microscopy (TEM) provided evidence for the existence of nanocrystalline coating. Microhardness test was carried out to examine the mechanical properties of the coatings. The coating adhesion strength was evaluated by scratch test. It was shown that a dense and uniform TiC coating with strong bonding to substrate could be formed at the optimal condition (35 h of milling duration, BPMR of 50:1 and hardened substrate). In addition, a possible mechanism was proposed for the formation of TiC coatings during mechanical alloying." @default.
- W1755141937 created "2016-06-24" @default.
- W1755141937 creator A5020672954 @default.
- W1755141937 creator A5021535377 @default.
- W1755141937 creator A5063594668 @default.
- W1755141937 creator A5064254009 @default.
- W1755141937 date "2016-01-01" @default.
- W1755141937 modified "2023-09-23" @default.
- W1755141937 title "Fabrication of nanocrystalline TiC coating on AISI D2 steel substrate via high-energy mechanical alloying of Ti and C" @default.
- W1755141937 cites W1973562432 @default.
- W1755141937 cites W1977126477 @default.
- W1755141937 cites W1981584388 @default.
- W1755141937 cites W1985434835 @default.
- W1755141937 cites W1991452376 @default.
- W1755141937 cites W1992810092 @default.
- W1755141937 cites W1992831378 @default.
- W1755141937 cites W1994222613 @default.
- W1755141937 cites W1997277140 @default.
- W1755141937 cites W1998666452 @default.
- W1755141937 cites W2002229368 @default.
- W1755141937 cites W2002321999 @default.
- W1755141937 cites W2008291737 @default.
- W1755141937 cites W2015239066 @default.
- W1755141937 cites W2029511169 @default.
- W1755141937 cites W2032914674 @default.
- W1755141937 cites W2035747012 @default.
- W1755141937 cites W2039479316 @default.
- W1755141937 cites W2040432202 @default.
- W1755141937 cites W2042533370 @default.
- W1755141937 cites W2042708429 @default.
- W1755141937 cites W2043225755 @default.
- W1755141937 cites W2058846690 @default.
- W1755141937 cites W2059224315 @default.
- W1755141937 cites W2065369898 @default.
- W1755141937 cites W2069215742 @default.
- W1755141937 cites W2069472074 @default.
- W1755141937 cites W2069824336 @default.
- W1755141937 cites W2073204882 @default.
- W1755141937 cites W2074945675 @default.
- W1755141937 cites W2084258325 @default.
- W1755141937 cites W2087535204 @default.
- W1755141937 cites W2087785015 @default.
- W1755141937 cites W2093128331 @default.
- W1755141937 cites W2095130512 @default.
- W1755141937 cites W2098728048 @default.
- W1755141937 cites W2104060495 @default.
- W1755141937 cites W2106115556 @default.
- W1755141937 cites W2139623996 @default.
- W1755141937 cites W2152386587 @default.
- W1755141937 cites W2316833311 @default.
- W1755141937 cites W4210978293 @default.
- W1755141937 doi "https://doi.org/10.1016/j.powtec.2015.10.030" @default.
- W1755141937 hasPublicationYear "2016" @default.
- W1755141937 type Work @default.
- W1755141937 sameAs 1755141937 @default.
- W1755141937 citedByCount "42" @default.
- W1755141937 countsByYear W17551419372016 @default.
- W1755141937 countsByYear W17551419372017 @default.
- W1755141937 countsByYear W17551419372018 @default.
- W1755141937 countsByYear W17551419372019 @default.
- W1755141937 countsByYear W17551419372020 @default.
- W1755141937 countsByYear W17551419372021 @default.
- W1755141937 countsByYear W17551419372022 @default.
- W1755141937 countsByYear W17551419372023 @default.
- W1755141937 crossrefType "journal-article" @default.
- W1755141937 hasAuthorship W1755141937A5020672954 @default.
- W1755141937 hasAuthorship W1755141937A5021535377 @default.
- W1755141937 hasAuthorship W1755141937A5063594668 @default.
- W1755141937 hasAuthorship W1755141937A5064254009 @default.
- W1755141937 hasConcept C111368507 @default.
- W1755141937 hasConcept C127313418 @default.
- W1755141937 hasConcept C140676511 @default.
- W1755141937 hasConcept C146088050 @default.
- W1755141937 hasConcept C147438087 @default.
- W1755141937 hasConcept C159985019 @default.
- W1755141937 hasConcept C165720898 @default.
- W1755141937 hasConcept C171250308 @default.
- W1755141937 hasConcept C191897082 @default.
- W1755141937 hasConcept C192562407 @default.
- W1755141937 hasConcept C26771246 @default.
- W1755141937 hasConcept C2777289219 @default.
- W1755141937 hasConcept C2781448156 @default.
- W1755141937 hasConcept C87976508 @default.
- W1755141937 hasConceptScore W1755141937C111368507 @default.
- W1755141937 hasConceptScore W1755141937C127313418 @default.
- W1755141937 hasConceptScore W1755141937C140676511 @default.
- W1755141937 hasConceptScore W1755141937C146088050 @default.
- W1755141937 hasConceptScore W1755141937C147438087 @default.
- W1755141937 hasConceptScore W1755141937C159985019 @default.
- W1755141937 hasConceptScore W1755141937C165720898 @default.
- W1755141937 hasConceptScore W1755141937C171250308 @default.
- W1755141937 hasConceptScore W1755141937C191897082 @default.
- W1755141937 hasConceptScore W1755141937C192562407 @default.
- W1755141937 hasConceptScore W1755141937C26771246 @default.
- W1755141937 hasConceptScore W1755141937C2777289219 @default.
- W1755141937 hasConceptScore W1755141937C2781448156 @default.
- W1755141937 hasConceptScore W1755141937C87976508 @default.
- W1755141937 hasLocation W17551419371 @default.