- W1804804592 abstract "The density of crystals of poly(ethylene terephthalate), (PETP), Qc is checked by X-ray diffraction assuming a triclinic unit cell and the indices of reflections as found by Bunn. The following unit cell dimensions are found: a = 4,48Å, b = 5,85Å, c = 10,75 Å, α = 99,5°, β = 118,4°, and γ = 111,2°. This gives the density Qc as 1,515g/cm3 which is about 4% higher than that reported by Bunn. Negligible differences in spacings for samples annealed at different temperatures (120°C–260°C) have been found. Only for an annealing temperature of 100°C the higher d-values lead to Qc = 1,484g/cm3. For undrawn PETP films annealed at 250°C the same value of Qc as for drawn PETP was obtained on the basis of Guinier X-ray patterns. No systematic variation of crystal plane spacings was found for drawn PETP fibers annealed at 220°C and containing mole fractions of 1,7 to 4,2% diethylene glycol, (2,2′-oxydiethanol), as comonomer. Die Dichte von kristallinem Poly(äthylenterephthalat), (PETP), Qc wurde röntgenographisch überprüft. Der Berechnung wurden die von Bunn angegebene trikline Symmetrie und Indizierung der Reflexe zugrunde gelegt. Es wurden die folgenden Elementarzellenparameter gefunden: a = 4,48 Å, b = 5,85 Å, c = 10,75 Å, α = 99,5°, β = 118,4° und γ = 111,2°. Damit ergibt sich eine Dichte Qc = 1,515g/cm3, welche etwa 4% höher als die von Bunn angegeben ist. Proben, die bei verschiedenen Temperaturen zwischen 120 und 260°C getempert waren, zeigten nur vernachlässigbare Unterschiede in den Netzebenenabständen. Bei der bei 100°C getemperten Probe wurde eine Dichte Qc = 1,484g/cm3 beobachtet. An unverstreckten, bei 250°C getemperten PETP-Filmen, wurde mit Hilfe von Guinier Aufnahmen der gleiche Dichtewert Qc wie der von verstrecktem PETP ermittelt. Beiverstreckten PETP-Borsten, die bei 220°C getempert waren und Molenbrüche zwischen 1.7 und 4,2% Diäthylenglykol, (2,2′-Oxydiathanol) enthielten, wurden keine systematischen Anderungen der Netzebenenabstande gefunden." @default.
- W1804804592 created "2016-06-24" @default.
- W1804804592 creator A5005908395 @default.
- W1804804592 creator A5010294630 @default.
- W1804804592 creator A5069353852 @default.
- W1804804592 date "1975-08-01" @default.
- W1804804592 modified "2023-10-12" @default.
- W1804804592 doi "https://doi.org/10.1002/macp.1975.021760821" @default.
- W1804804592 hasPublicationYear "1975" @default.
- W1804804592 type Work @default.
- W1804804592 sameAs 1804804592 @default.
- W1804804592 citedByCount "101" @default.
- W1804804592 countsByYear W18048045922013 @default.
- W1804804592 countsByYear W18048045922014 @default.
- W1804804592 countsByYear W18048045922017 @default.
- W1804804592 countsByYear W18048045922018 @default.
- W1804804592 countsByYear W18048045922020 @default.
- W1804804592 countsByYear W18048045922021 @default.
- W1804804592 countsByYear W18048045922022 @default.
- W1804804592 countsByYear W18048045922023 @default.
- W1804804592 crossrefType "journal-article" @default.
- W1804804592 hasAuthorship W1804804592A5005908395 @default.
- W1804804592 hasAuthorship W1804804592A5010294630 @default.
- W1804804592 hasAuthorship W1804804592A5069353852 @default.
- W1804804592 hasConcept C115624301 @default.
- W1804804592 hasConcept C159985019 @default.
- W1804804592 hasConcept C178790620 @default.
- W1804804592 hasConcept C185592680 @default.
- W1804804592 hasConcept C188027245 @default.
- W1804804592 hasConcept C192562407 @default.
- W1804804592 hasConcept C2777516009 @default.
- W1804804592 hasConcept C2777855556 @default.
- W1804804592 hasConcept C2779136216 @default.
- W1804804592 hasConcept C2780267503 @default.
- W1804804592 hasConcept C42228675 @default.
- W1804804592 hasConcept C55493867 @default.
- W1804804592 hasConcept C8010536 @default.
- W1804804592 hasConceptScore W1804804592C115624301 @default.
- W1804804592 hasConceptScore W1804804592C159985019 @default.
- W1804804592 hasConceptScore W1804804592C178790620 @default.
- W1804804592 hasConceptScore W1804804592C185592680 @default.
- W1804804592 hasConceptScore W1804804592C188027245 @default.
- W1804804592 hasConceptScore W1804804592C192562407 @default.
- W1804804592 hasConceptScore W1804804592C2777516009 @default.
- W1804804592 hasConceptScore W1804804592C2777855556 @default.
- W1804804592 hasConceptScore W1804804592C2779136216 @default.
- W1804804592 hasConceptScore W1804804592C2780267503 @default.
- W1804804592 hasConceptScore W1804804592C42228675 @default.
- W1804804592 hasConceptScore W1804804592C55493867 @default.
- W1804804592 hasConceptScore W1804804592C8010536 @default.
- W1804804592 hasIssue "8" @default.
- W1804804592 hasLocation W18048045921 @default.
- W1804804592 hasOpenAccess W1804804592 @default.
- W1804804592 hasPrimaryLocation W18048045921 @default.
- W1804804592 hasRelatedWork W193200281 @default.
- W1804804592 hasRelatedWork W2037702960 @default.
- W1804804592 hasRelatedWork W2093137218 @default.
- W1804804592 hasRelatedWork W2093647807 @default.
- W1804804592 hasRelatedWork W2348927050 @default.
- W1804804592 hasRelatedWork W2349059201 @default.
- W1804804592 hasRelatedWork W2465028945 @default.
- W1804804592 hasRelatedWork W2488192702 @default.
- W1804804592 hasRelatedWork W4301782598 @default.
- W1804804592 hasRelatedWork W4302411994 @default.
- W1804804592 hasVolume "176" @default.
- W1804804592 isParatext "false" @default.
- W1804804592 isRetracted "false" @default.
- W1804804592 magId "1804804592" @default.
- W1804804592 workType "article" @default.