- W1834067032 abstract "In this thesis the influence of spinning speed and drawing ratio is investigated by means of solid state NMR spectroscopy. It is shown that increasing spinning speeds result in a preferred formation of the gamma crystalline phase, while increasing drawing ratios result in a preferred formation of the alpha crystalline phase. The crystallinity of the fibers increases with increasing drawing ratio and increasing spinning speed. The orientation of the polymer chains increases in both cases. A conversion of the gamma phase into the alpha crystalline phase by drawing can be observed. A distinction between four different phases (alpha and gamma crystalline, mobile and rigid amorphous) is possible and for each its fraction and orientation could be measured. Furthermore the dependence of the carbonyl tensor values on the fractions of the two different crystalline phases was shown. In der vorliegenden Arbeit wurde der Einfluss der Herstellungsbedingungen auf Struktur und Orientierung von Nylon-6 Fasern mittels Festkorper NMR Spektroskopie untersucht. Die untersuchten Herstellungsbedingungen waren Spinngeschwindigkeit und Streckgrad. Es konnte gezeigt werden, dass eine Erhohung der Spinngeschwindigkeit zu einer bevorzugten Bildung der gamma kristallinen Phase fuhrt, wahrend eine Erhohung des Streckgrades zu einer bevorzugten Bildung der alpha kristallinen Phase fuhrt. Die Kristallinitat steigt sowohl mit Erhohung des Streckgrades als auch der Spinngeschwindigkeit. Ebenso nimmt die Orientierung der Polymerketten in beiden Fallen zu. Eine Umwandlung der gamma kristallinen Phase in die alpha kristalline Phase ist bei Streckung zu beobachten. Fur die vier unterscheidbaren Phasen (alpha und gamma kristallin, sowie mobil und rigid amorph) konnten jeweils die Anteile und Orientierungen separat bestimmt werden. Des weiteren konnte eine Anderung der Carbonyltenorwerte in Abhangigkeit der Anteile eider Kristallstrukturen nachgewiesen werden." @default.
- W1834067032 created "2016-06-24" @default.
- W1834067032 creator A5037554008 @default.
- W1834067032 date "2000-07-05" @default.
- W1834067032 modified "2023-09-24" @default.
- W1834067032 title "Untersuchung der Einflüsse von Spinngeschwindigkeit und Streckgrad auf die Struktur und Orientierung von Nylon-6 Fasern mit Hilfe der Festkörper-Spektroskopie" @default.
- W1834067032 hasPublicationYear "2000" @default.
- W1834067032 type Work @default.
- W1834067032 sameAs 1834067032 @default.
- W1834067032 citedByCount "0" @default.
- W1834067032 crossrefType "dissertation" @default.
- W1834067032 hasAuthorship W1834067032A5037554008 @default.
- W1834067032 hasConcept C121332964 @default.
- W1834067032 hasConcept C154815118 @default.
- W1834067032 hasConcept C178790620 @default.
- W1834067032 hasConcept C185592680 @default.
- W1834067032 hasConcept C188027245 @default.
- W1834067032 hasConcept C192562407 @default.
- W1834067032 hasConcept C44280652 @default.
- W1834067032 hasConcept C46275449 @default.
- W1834067032 hasConcept C8010536 @default.
- W1834067032 hasConceptScore W1834067032C121332964 @default.
- W1834067032 hasConceptScore W1834067032C154815118 @default.
- W1834067032 hasConceptScore W1834067032C178790620 @default.
- W1834067032 hasConceptScore W1834067032C185592680 @default.
- W1834067032 hasConceptScore W1834067032C188027245 @default.
- W1834067032 hasConceptScore W1834067032C192562407 @default.
- W1834067032 hasConceptScore W1834067032C44280652 @default.
- W1834067032 hasConceptScore W1834067032C46275449 @default.
- W1834067032 hasConceptScore W1834067032C8010536 @default.
- W1834067032 hasLocation W18340670321 @default.
- W1834067032 hasOpenAccess W1834067032 @default.
- W1834067032 hasPrimaryLocation W18340670321 @default.
- W1834067032 isParatext "false" @default.
- W1834067032 isRetracted "false" @default.
- W1834067032 magId "1834067032" @default.
- W1834067032 workType "dissertation" @default.