- W19238471 abstract "The in-sodium biaxial creep deformation of internally pressurized tube specimens of alloys M-813 and Nimonic PE16 was measured at 650/sup 0/C under constant stress conditions after 4000 hours of sodium exposure. Each alloy had specimens at two different stress levels, viz., 0 and 165 MPa (24,000 psi). The data showed negative diameter changes at zero stress, which were attributed to material densification associated with precipitation. Although material densification was also seen in comparable in-argon experiments, the in-sodium creep strains at 165 MPa and 650/sup 0/C were much lower than the corresponding in-argon values. The higher creep strains in argon are explained on the basis of two parallel mechanisms involving oxygen, which is present at a low level in sodium (1 ppM) as compared with approximately 1000 ppM in the argon environment. The trends in the current data are consistent with observations by earlier authors. Sodium exposure of Nimonic PE16 also resulted in 4 ..mu..m deep intergranular penetration, which did not have any apparent effect on its biaxial creep behavior." @default.
- W19238471 created "2016-06-24" @default.
- W19238471 creator A5041547684 @default.
- W19238471 creator A5075351869 @default.
- W19238471 date "1980-04-01" @default.
- W19238471 modified "2023-09-24" @default.
- W19238471 title "In-sodium creep behavior of alloys M-813 and Nimonic PE16" @default.
- W19238471 hasPublicationYear "1980" @default.
- W19238471 type Work @default.
- W19238471 sameAs 19238471 @default.
- W19238471 citedByCount "0" @default.
- W19238471 crossrefType "journal-article" @default.
- W19238471 hasAuthorship W19238471A5041547684 @default.
- W19238471 hasAuthorship W19238471A5075351869 @default.
- W19238471 hasConcept C145514866 @default.
- W19238471 hasConcept C149912024 @default.
- W19238471 hasConcept C178790620 @default.
- W19238471 hasConcept C184102282 @default.
- W19238471 hasConcept C185592680 @default.
- W19238471 hasConcept C191897082 @default.
- W19238471 hasConcept C192562407 @default.
- W19238471 hasConcept C207055975 @default.
- W19238471 hasConcept C2780026712 @default.
- W19238471 hasConcept C537181965 @default.
- W19238471 hasConcept C540031477 @default.
- W19238471 hasConcept C547737533 @default.
- W19238471 hasConceptScore W19238471C145514866 @default.
- W19238471 hasConceptScore W19238471C149912024 @default.
- W19238471 hasConceptScore W19238471C178790620 @default.
- W19238471 hasConceptScore W19238471C184102282 @default.
- W19238471 hasConceptScore W19238471C185592680 @default.
- W19238471 hasConceptScore W19238471C191897082 @default.
- W19238471 hasConceptScore W19238471C192562407 @default.
- W19238471 hasConceptScore W19238471C207055975 @default.
- W19238471 hasConceptScore W19238471C2780026712 @default.
- W19238471 hasConceptScore W19238471C537181965 @default.
- W19238471 hasConceptScore W19238471C540031477 @default.
- W19238471 hasConceptScore W19238471C547737533 @default.
- W19238471 hasLocation W192384711 @default.
- W19238471 hasOpenAccess W19238471 @default.
- W19238471 hasPrimaryLocation W192384711 @default.
- W19238471 hasRelatedWork W1987336723 @default.
- W19238471 hasRelatedWork W2026564040 @default.
- W19238471 hasRelatedWork W2031375440 @default.
- W19238471 hasRelatedWork W2033291934 @default.
- W19238471 hasRelatedWork W2065651279 @default.
- W19238471 hasRelatedWork W2066727083 @default.
- W19238471 hasRelatedWork W2106694808 @default.
- W19238471 hasRelatedWork W2317235953 @default.
- W19238471 hasRelatedWork W2322167902 @default.
- W19238471 hasRelatedWork W2325779075 @default.
- W19238471 hasRelatedWork W2559820755 @default.
- W19238471 hasRelatedWork W2794355740 @default.
- W19238471 hasRelatedWork W2945518542 @default.
- W19238471 hasRelatedWork W3047726638 @default.
- W19238471 hasRelatedWork W3126672394 @default.
- W19238471 hasRelatedWork W3139612109 @default.
- W19238471 hasRelatedWork W3164829130 @default.
- W19238471 hasRelatedWork W3196541499 @default.
- W19238471 hasRelatedWork W1526234485 @default.
- W19238471 hasRelatedWork W2820509188 @default.
- W19238471 isParatext "false" @default.
- W19238471 isRetracted "false" @default.
- W19238471 magId "19238471" @default.
- W19238471 workType "article" @default.