- W1963497352 abstract "To evaluate the masking ability of IPS e.max all-ceramics system of HO series. IPS e.max Press HO ingots were fabricated into twenty cylindrical specimens (n=5) with the diameter of 13mm and four different thinknesses (0.4mm, 0.6mm, 0.8mm, 1.0mm). All specimens after veneered, gazed and cemented to metal substrate disks (thickness 3mm, diameter 13mm) were measured on both the white background and metal substrate disks background using a spectrophotometer and values of L, a and b were calculated to compare color differences among four groups. Meanwhile ΔE with the preselected required color (A2 color) were calculated. ΔE<1.5 was considered a clinically acceptable color match. In the 0.4mm thickness specimens group, the values of L, a and b significantly increased (-1.36±0.05, -0.15±0.06, -1.46±0.02, respectively) between the white background and abutment background. But there were no significant color differences in the other three groups (P<0.05). In the 0.6mm and 0.8mm thicknesses specimens groups, the color difference values (0.71±0.04, 1.14±0.06, respectively) with A2 color were less than the defined value. Thus the cylindrical specimens with the thickness of 0.6mm, 0.8mm and 1.0mm could mask the metal substrate disks background sufficiently and the thickness of 0.6mm and 0.8mm had an acceptable color match compared with the target color. IPS e.max all-ceramics system of HO series can produce clinically acceptable color match and have the capacity to mask a dark background such as a dark tooth or core buildup material." @default.
- W1963497352 created "2016-06-24" @default.
- W1963497352 creator A5018318591 @default.
- W1963497352 creator A5033110724 @default.
- W1963497352 creator A5075158030 @default.
- W1963497352 creator A5077057546 @default.
- W1963497352 creator A5084617243 @default.
- W1963497352 creator A5087784341 @default.
- W1963497352 date "2012-06-01" @default.
- W1963497352 modified "2023-10-16" @default.
- W1963497352 title "Masking Ability of IPS e.max ALL-Ceramics System of HO Series" @default.
- W1963497352 cites W1490434452 @default.
- W1963497352 cites W1975142139 @default.
- W1963497352 cites W2046895221 @default.
- W1963497352 cites W2061191445 @default.
- W1963497352 cites W2121758634 @default.
- W1963497352 doi "https://doi.org/10.4028/www.scientific.net/kem.512-515.1784" @default.
- W1963497352 hasPublicationYear "2012" @default.
- W1963497352 type Work @default.
- W1963497352 sameAs 1963497352 @default.
- W1963497352 citedByCount "1" @default.
- W1963497352 countsByYear W19634973522021 @default.
- W1963497352 crossrefType "journal-article" @default.
- W1963497352 hasAuthorship W1963497352A5018318591 @default.
- W1963497352 hasAuthorship W1963497352A5033110724 @default.
- W1963497352 hasAuthorship W1963497352A5075158030 @default.
- W1963497352 hasAuthorship W1963497352A5077057546 @default.
- W1963497352 hasAuthorship W1963497352A5084617243 @default.
- W1963497352 hasAuthorship W1963497352A5087784341 @default.
- W1963497352 hasConcept C105795698 @default.
- W1963497352 hasConcept C111368507 @default.
- W1963497352 hasConcept C120665830 @default.
- W1963497352 hasConcept C121332964 @default.
- W1963497352 hasConcept C127313418 @default.
- W1963497352 hasConcept C134132462 @default.
- W1963497352 hasConcept C142362112 @default.
- W1963497352 hasConcept C153349607 @default.
- W1963497352 hasConcept C159985019 @default.
- W1963497352 hasConcept C162307627 @default.
- W1963497352 hasConcept C186991048 @default.
- W1963497352 hasConcept C192562407 @default.
- W1963497352 hasConcept C193601281 @default.
- W1963497352 hasConcept C2777289219 @default.
- W1963497352 hasConcept C2777402240 @default.
- W1963497352 hasConcept C3018023364 @default.
- W1963497352 hasConcept C33923547 @default.
- W1963497352 hasConcept C41008148 @default.
- W1963497352 hasConcept C76155785 @default.
- W1963497352 hasConceptScore W1963497352C105795698 @default.
- W1963497352 hasConceptScore W1963497352C111368507 @default.
- W1963497352 hasConceptScore W1963497352C120665830 @default.
- W1963497352 hasConceptScore W1963497352C121332964 @default.
- W1963497352 hasConceptScore W1963497352C127313418 @default.
- W1963497352 hasConceptScore W1963497352C134132462 @default.
- W1963497352 hasConceptScore W1963497352C142362112 @default.
- W1963497352 hasConceptScore W1963497352C153349607 @default.
- W1963497352 hasConceptScore W1963497352C159985019 @default.
- W1963497352 hasConceptScore W1963497352C162307627 @default.
- W1963497352 hasConceptScore W1963497352C186991048 @default.
- W1963497352 hasConceptScore W1963497352C192562407 @default.
- W1963497352 hasConceptScore W1963497352C193601281 @default.
- W1963497352 hasConceptScore W1963497352C2777289219 @default.
- W1963497352 hasConceptScore W1963497352C2777402240 @default.
- W1963497352 hasConceptScore W1963497352C3018023364 @default.
- W1963497352 hasConceptScore W1963497352C33923547 @default.
- W1963497352 hasConceptScore W1963497352C41008148 @default.
- W1963497352 hasConceptScore W1963497352C76155785 @default.
- W1963497352 hasLocation W19634973521 @default.
- W1963497352 hasOpenAccess W1963497352 @default.
- W1963497352 hasPrimaryLocation W19634973521 @default.
- W1963497352 hasRelatedWork W1967533247 @default.
- W1963497352 hasRelatedWork W2023929301 @default.
- W1963497352 hasRelatedWork W2069022996 @default.
- W1963497352 hasRelatedWork W2281145519 @default.
- W1963497352 hasRelatedWork W2349154417 @default.
- W1963497352 hasRelatedWork W2391782042 @default.
- W1963497352 hasRelatedWork W2511081116 @default.
- W1963497352 hasRelatedWork W2939243712 @default.
- W1963497352 hasRelatedWork W3137397578 @default.
- W1963497352 hasRelatedWork W4205295844 @default.
- W1963497352 hasVolume "512-515" @default.
- W1963497352 isParatext "false" @default.
- W1963497352 isRetracted "false" @default.
- W1963497352 magId "1963497352" @default.
- W1963497352 workType "article" @default.