• W1963567247 abstract "In this study, various weight percentages (0, 0.05 and 0.1 wt.%) of graphene nanosheet doped lead-free Sn–8Zn–3Bi solder alloys were investigated in order to analyze the electromigration induced microstructural development and mechanical properties, such as the shear strength and microhardness, as well as the melting characteristics of the novel composite solders. The effect of electromigration on the solder joint was systematically studied by using a newly developed wire-type testing configuration. The samples were stressed under a current density of 5 × 103 A/cm2 at 100 °C for different aging periods in order to study the electromigration induced reliability issues. For solders with and without the graphene, γ-Cu5Zn8 intermetallic compounds (IMCs) were found at the solder and Cu pad interface. The majority of the added graphene nanosheets were proved to be uniformly distributed in the β-Sn matrix. After the graphene addition, needle-like Zn-rich phases with a finer microstructure were discovered in the solder matrix. The growth rate of the IMC layers of the graphene doped solder was slower in comparison to IMC layers in plain solder at the interfaces. With 0.1 wt.% graphene addition, the measured IMC growth rate was decreased from 30.9 × 10−14 to 24.9 × 10−14 cm2/s. The melting temperature of the doped solder measured by differential scanning calorimeter (DSC) showed little difference from that of the plain solder. The Vickers hardness, up to 29.9 Hv with 0.1 wt.% graphene addition, is 9.1% higher than that of plain solder. The graphene doped solder consistently demonstrated higher ball shear strength as a function of aging time. The ball shear strength value was increased by 10.2 ± 0.8% than that of plain solders during the whole aging period. The improvement was due to the dispersion-strengthening mechanism, refined microstructure and excellent intrinsic mechanical properties of graphene. Moreover, fracture occurred at the IMC interface of the doped samples showed a ductile fracture pattern with a large distribution of dimples on the rough surface." @default.
• W1963567247 created "2016-06-24" @default.
• W1963567247 creator A5020146275 @default.
• W1963567247 creator A5039204587 @default.
• W1963567247 creator A5048157050 @default.
• W1963567247 creator A5087072231 @default.
• W1963567247 date "2013-12-01" @default.
• W1963567247 modified "2023-10-16" @default.
• W1963567247 title "Effect of graphene doping on microstructural and mechanical properties of Sn–8Zn–3Bi solder joints together with electromigration analysis" @default.
• W1963567247 cites W1967587828 @default.
• W1963567247 cites W1970656917 @default.
• W1963567247 cites W1972038331 @default.
• W1963567247 cites W1973178977 @default.
• W1963567247 cites W1976745495 @default.
• W1963567247 cites W1981292483 @default.
• W1963567247 cites W1988795747 @default.
• W1963567247 cites W1995128912 @default.
• W1963567247 cites W1997727285 @default.
• W1963567247 cites W2001235230 @default.
• W1963567247 cites W2001439586 @default.
• W1963567247 cites W2002151973 @default.
• W1963567247 cites W2006999073 @default.
• W1963567247 cites W2010971702 @default.
• W1963567247 cites W2013247754 @default.
• W1963567247 cites W2019420858 @default.
• W1963567247 cites W2021945273 @default.
• W1963567247 cites W2021969851 @default.
• W1963567247 cites W2026519647 @default.
• W1963567247 cites W2027521533 @default.
• W1963567247 cites W2035724607 @default.
• W1963567247 cites W2037171084 @default.
• W1963567247 cites W2044015015 @default.
• W1963567247 cites W2044103838 @default.
• W1963567247 cites W2056488548 @default.
• W1963567247 cites W2056801163 @default.
• W1963567247 cites W2061141647 @default.
• W1963567247 cites W2069554460 @default.
• W1963567247 cites W2074143039 @default.
• W1963567247 cites W2075936644 @default.
• W1963567247 cites W2080388957 @default.
• W1963567247 cites W2080445773 @default.
• W1963567247 cites W2083768946 @default.
• W1963567247 cites W2084525959 @default.
• W1963567247 cites W2089936014 @default.
• W1963567247 cites W2090442472 @default.
• W1963567247 cites W2091611125 @default.
• W1963567247 cites W2092025627 @default.
• W1963567247 cites W2152700488 @default.
• W1963567247 cites W3102525999 @default.
• W1963567247 cites W647798093 @default.
• W1963567247 cites W2058480212 @default.
• W1963567247 doi "https://doi.org/10.1016/j.jallcom.2013.05.124" @default.
• W1963567247 hasPublicationYear "2013" @default.
• W1963567247 type Work @default.
• W1963567247 sameAs 1963567247 @default.
• W1963567247 citedByCount "69" @default.
• W1963567247 countsByYear W19635672472014 @default.
• W1963567247 countsByYear W19635672472015 @default.
• W1963567247 countsByYear W19635672472016 @default.
• W1963567247 countsByYear W19635672472017 @default.
• W1963567247 countsByYear W19635672472018 @default.
• W1963567247 countsByYear W19635672472019 @default.
• W1963567247 countsByYear W19635672472020 @default.
• W1963567247 countsByYear W19635672472021 @default.
• W1963567247 countsByYear W19635672472022 @default.
• W1963567247 countsByYear W19635672472023 @default.
• W1963567247 crossrefType "journal-article" @default.
• W1963567247 hasAuthorship W1963567247A5020146275 @default.
• W1963567247 hasAuthorship W1963567247A5039204587 @default.
• W1963567247 hasAuthorship W1963567247A5048157050 @default.
• W1963567247 hasAuthorship W1963567247A5087072231 @default.
• W1963567247 hasConcept C133392424 @default.
• W1963567247 hasConcept C138055206 @default.
• W1963567247 hasConcept C159985019 @default.
• W1963567247 hasConcept C171250308 @default.
• W1963567247 hasConcept C191897082 @default.
• W1963567247 hasConcept C192562407 @default.
• W1963567247 hasConcept C27501479 @default.
• W1963567247 hasConcept C2780026712 @default.
• W1963567247 hasConcept C30080830 @default.
• W1963567247 hasConcept C49040817 @default.
• W1963567247 hasConcept C50296614 @default.
• W1963567247 hasConcept C57863236 @default.
• W1963567247 hasConcept C87976508 @default.
• W1963567247 hasConceptScore W1963567247C133392424 @default.
• W1963567247 hasConceptScore W1963567247C138055206 @default.
• W1963567247 hasConceptScore W1963567247C159985019 @default.
• W1963567247 hasConceptScore W1963567247C171250308 @default.
• W1963567247 hasConceptScore W1963567247C191897082 @default.
• W1963567247 hasConceptScore W1963567247C192562407 @default.
• W1963567247 hasConceptScore W1963567247C27501479 @default.
• W1963567247 hasConceptScore W1963567247C2780026712 @default.
• W1963567247 hasConceptScore W1963567247C30080830 @default.
• W1963567247 hasConceptScore W1963567247C49040817 @default.
• W1963567247 hasConceptScore W1963567247C50296614 @default.
• W1963567247 hasConceptScore W1963567247C57863236 @default.
• W1963567247 hasConceptScore W1963567247C87976508 @default.
• W1963567247 hasLocation W19635672471 @default.

• next