- W1963969083 abstract "summary The aim of this study was to determine how curing γ-methacryloxypropyltrimethoxysilane (γ-MPS) to the surface of E-glass fibre affects the transverse strength of autopolymerizing polymethylmethacrylate–glass fibre composite (PMMA-GF). For this purpose, unidirectional glass fibres treated with γ-MPS solution and cured for various lengths of time at different temperatures (+50°C, +1OO°C and +150°C) were used as a strengthener of PMMA test specimens (n = 10 per group). The mean concentration of glass fibres in the test specimens was 17 wt%. The unreinforced test specimens and the test specimens reinforced with unsilanized fibres were compared, but no statistical difference in their transverse strengths was found (p = 0.568). The results also revealed that when the curing temperatures of the γ-MPS were compared, the highest transverse strength (152 MPa) for the PMMA-GF composite was obtained by curing the MPS for 120 min at +100°C; the lowest strength (91 MPa) was obtained by polymerizing the MPS at +150°C (P<0.001). However, SEM photomicrographs taken from the interface of the glass fibre and PMMA showed that the fibre adhered equally well to the PMMA treated at +100°C or at +150°C. This suggests that reduction in transverse strength of composite test specimens is caused by other factors, for example, by improper impregnation of PMMA into the fibre bundle, rather than by inadequate adhesion." @default.
- W1963969083 created "2016-06-24" @default.
- W1963969083 creator A5011215915 @default.
- W1963969083 date "2008-06-28" @default.
- W1963969083 modified "2023-10-18" @default.
- W1963969083 title "Curing of a silane coupling agent and its effect on the transverse strength of autopolymerizing polymethylmethacrylate-glass fibre composite" @default.
- W1963969083 cites W1976259219 @default.
- W1963969083 cites W1978349112 @default.
- W1963969083 cites W1992312824 @default.
- W1963969083 cites W2007954457 @default.
- W1963969083 cites W2018474716 @default.
- W1963969083 cites W2048505774 @default.
- W1963969083 cites W2051140911 @default.
- W1963969083 cites W2060890486 @default.
- W1963969083 cites W2079716673 @default.
- W1963969083 cites W2082334524 @default.
- W1963969083 cites W2090856537 @default.
- W1963969083 cites W2119496006 @default.
- W1963969083 cites W2135596676 @default.
- W1963969083 cites W2143107112 @default.
- W1963969083 doi "https://doi.org/10.1111/j.1365-2842.1997.tb00304.x" @default.
- W1963969083 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/9061621" @default.
- W1963969083 hasPublicationYear "2008" @default.
- W1963969083 type Work @default.
- W1963969083 sameAs 1963969083 @default.
- W1963969083 citedByCount "29" @default.
- W1963969083 countsByYear W19639690832012 @default.
- W1963969083 countsByYear W19639690832013 @default.
- W1963969083 countsByYear W19639690832014 @default.
- W1963969083 countsByYear W19639690832015 @default.
- W1963969083 countsByYear W19639690832016 @default.
- W1963969083 countsByYear W19639690832017 @default.
- W1963969083 countsByYear W19639690832018 @default.
- W1963969083 countsByYear W19639690832019 @default.
- W1963969083 countsByYear W19639690832021 @default.
- W1963969083 countsByYear W19639690832022 @default.
- W1963969083 countsByYear W19639690832023 @default.
- W1963969083 crossrefType "journal-article" @default.
- W1963969083 hasAuthorship W1963969083A5011215915 @default.
- W1963969083 hasConcept C104779481 @default.
- W1963969083 hasConcept C127413603 @default.
- W1963969083 hasConcept C132976073 @default.
- W1963969083 hasConcept C154954056 @default.
- W1963969083 hasConcept C159985019 @default.
- W1963969083 hasConcept C177229083 @default.
- W1963969083 hasConcept C192562407 @default.
- W1963969083 hasConcept C2778024649 @default.
- W1963969083 hasConcept C66938386 @default.
- W1963969083 hasConceptScore W1963969083C104779481 @default.
- W1963969083 hasConceptScore W1963969083C127413603 @default.
- W1963969083 hasConceptScore W1963969083C132976073 @default.
- W1963969083 hasConceptScore W1963969083C154954056 @default.
- W1963969083 hasConceptScore W1963969083C159985019 @default.
- W1963969083 hasConceptScore W1963969083C177229083 @default.
- W1963969083 hasConceptScore W1963969083C192562407 @default.
- W1963969083 hasConceptScore W1963969083C2778024649 @default.
- W1963969083 hasConceptScore W1963969083C66938386 @default.
- W1963969083 hasIssue "2" @default.
- W1963969083 hasLocation W19639690831 @default.
- W1963969083 hasLocation W19639690832 @default.
- W1963969083 hasOpenAccess W1963969083 @default.
- W1963969083 hasPrimaryLocation W19639690831 @default.
- W1963969083 hasRelatedWork W1975608897 @default.
- W1963969083 hasRelatedWork W1988779382 @default.
- W1963969083 hasRelatedWork W2005496670 @default.
- W1963969083 hasRelatedWork W2054113325 @default.
- W1963969083 hasRelatedWork W2082293200 @default.
- W1963969083 hasRelatedWork W2492611110 @default.
- W1963969083 hasRelatedWork W3045627597 @default.
- W1963969083 hasRelatedWork W3048672776 @default.
- W1963969083 hasRelatedWork W4367059546 @default.
- W1963969083 hasRelatedWork W52641919 @default.
- W1963969083 hasVolume "24" @default.
- W1963969083 isParatext "false" @default.
- W1963969083 isRetracted "false" @default.
- W1963969083 magId "1963969083" @default.
- W1963969083 workType "article" @default.