- W1965034056 abstract "Rapidly solidified ribbons of 50 μm and 100 μm in thickness were prepared by a single roll method. Al6Fe, Al12Mo and Al3Fe precipitates are observed in quenched specimens of 100 μm thick ribbons but hardly observed in those of 50 μm thick ribbons. Using the 50 μm and 100 μm thick ribbons, two kinds of alloy bar were produced by hot extrusion at 723 K. The alloy bar made from 100 μm ribbons shows a higher 1000 h creep rupture strength at 573 K∼673 K than the bar made from 50 μm ribbons. The “n” value calculated from the equation ε=k·σn is 7 and 9 for the bars made from 50 μm and 100 μm ribbons, respectively." @default.
- W1965034056 created "2016-06-24" @default.
- W1965034056 creator A5014891307 @default.
- W1965034056 creator A5043725497 @default.
- W1965034056 date "1996-01-01" @default.
- W1965034056 modified "2023-09-24" @default.
- W1965034056 title "Effect of cooling rate of rapid solidification on softening behavior of Al-8%Fe-2%Mo alloy." @default.
- W1965034056 cites W2003321157 @default.
- W1965034056 cites W2030616753 @default.
- W1965034056 cites W2317704576 @default.
- W1965034056 cites W2508185237 @default.
- W1965034056 cites W4249894551 @default.
- W1965034056 doi "https://doi.org/10.2464/jilm.46.21" @default.
- W1965034056 hasPublicationYear "1996" @default.
- W1965034056 type Work @default.
- W1965034056 sameAs 1965034056 @default.
- W1965034056 citedByCount "3" @default.
- W1965034056 countsByYear W19650340562022 @default.
- W1965034056 crossrefType "journal-article" @default.
- W1965034056 hasAuthorship W1965034056A5014891307 @default.
- W1965034056 hasAuthorship W1965034056A5043725497 @default.
- W1965034056 hasBestOaLocation W19650340561 @default.
- W1965034056 hasConcept C121332964 @default.
- W1965034056 hasConcept C149912024 @default.
- W1965034056 hasConcept C153294291 @default.
- W1965034056 hasConcept C159985019 @default.
- W1965034056 hasConcept C188721877 @default.
- W1965034056 hasConcept C191897082 @default.
- W1965034056 hasConcept C192562407 @default.
- W1965034056 hasConcept C2778958987 @default.
- W1965034056 hasConcept C2780026712 @default.
- W1965034056 hasConcept C2781098093 @default.
- W1965034056 hasConceptScore W1965034056C121332964 @default.
- W1965034056 hasConceptScore W1965034056C149912024 @default.
- W1965034056 hasConceptScore W1965034056C153294291 @default.
- W1965034056 hasConceptScore W1965034056C159985019 @default.
- W1965034056 hasConceptScore W1965034056C188721877 @default.
- W1965034056 hasConceptScore W1965034056C191897082 @default.
- W1965034056 hasConceptScore W1965034056C192562407 @default.
- W1965034056 hasConceptScore W1965034056C2778958987 @default.
- W1965034056 hasConceptScore W1965034056C2780026712 @default.
- W1965034056 hasConceptScore W1965034056C2781098093 @default.
- W1965034056 hasIssue "1" @default.
- W1965034056 hasLocation W19650340561 @default.
- W1965034056 hasOpenAccess W1965034056 @default.
- W1965034056 hasPrimaryLocation W19650340561 @default.
- W1965034056 hasRelatedWork W1974778737 @default.
- W1965034056 hasRelatedWork W1979080992 @default.
- W1965034056 hasRelatedWork W2023925844 @default.
- W1965034056 hasRelatedWork W2048829577 @default.
- W1965034056 hasRelatedWork W2055156998 @default.
- W1965034056 hasRelatedWork W2357966028 @default.
- W1965034056 hasRelatedWork W2394175211 @default.
- W1965034056 hasRelatedWork W4324144252 @default.
- W1965034056 hasRelatedWork W4324318643 @default.
- W1965034056 hasRelatedWork W4379207670 @default.
- W1965034056 hasVolume "46" @default.
- W1965034056 isParatext "false" @default.
- W1965034056 isRetracted "false" @default.
- W1965034056 magId "1965034056" @default.
- W1965034056 workType "article" @default.