- W1967339556 abstract "Abstract The as-cast Ti 1.02 Cr 1.1 Mn 0.3 Fe 0.6 alloy for hybrid hydrogen storage vessel application was annealed at different temperatures (873 K, 973 K, 1123 K, 1173 K) for 2 h, and annealed at 1123 K for different time (2, 5, 8 h) respectively, and their microstructure and hydrogen storage properties were investigated systematically. The results show that the as-cast alloy has a single C14 Laves phase, and all annealed alloys consist of a C14 Laves main phase and a secondary phase. After annealing at different temperatures for 2 h, the hydrogen absorption pressure at 298 K decreases, however, the maximum hydrogen storage capacity and desorption pressures at 318 K decrease slightly too. As the annealing time extends, the hydrogen absorption plateau pressure at 298 K and hydrogen desorption plateau pressure at 318 K increase, and the hydrogen desorption capacity increases first and then decreases, which reaches the highest desorption capacity of 1.721 wt.% at the annealing time of 5 h. Among the studied alloys, the alloy annealed at 1123 K for 5 h has the best overall properties for hybrid hydrogen storage application, its hydrogen absorption plateau at 298 K is 29.09 MPa, its hydrogen desorption plateau pressure at 318 K is 45.12 MPa, its hydrogen storage capacity is 1.721 wt.% and its dissociation enthalpy (Δ H d ) is 17.78 kJ/mol H 2 ." @default.
- W1967339556 created "2016-06-24" @default.
- W1967339556 creator A5006847732 @default.
- W1967339556 creator A5010466371 @default.
- W1967339556 creator A5049438734 @default.
- W1967339556 creator A5054399541 @default.
- W1967339556 creator A5054659867 @default.
- W1967339556 creator A5055526924 @default.
- W1967339556 creator A5075423250 @default.
- W1967339556 creator A5077357755 @default.
- W1967339556 date "2015-07-01" @default.
- W1967339556 modified "2023-10-17" @default.
- W1967339556 title "Influence of annealing treatment on the microstructure and hydrogen storage performance of Ti1.02Cr1.1Mn0.3Fe0.6 alloy for hybrid hydrogen storage application" @default.
- W1967339556 cites W1516422092 @default.
- W1967339556 cites W1986742455 @default.
- W1967339556 cites W1989079514 @default.
- W1967339556 cites W1989303127 @default.
- W1967339556 cites W1993088302 @default.
- W1967339556 cites W1994114047 @default.
- W1967339556 cites W2018035009 @default.
- W1967339556 cites W2028510618 @default.
- W1967339556 cites W2030599984 @default.
- W1967339556 cites W2035551428 @default.
- W1967339556 cites W2038722085 @default.
- W1967339556 cites W2049439248 @default.
- W1967339556 cites W2066649464 @default.
- W1967339556 cites W2070107637 @default.
- W1967339556 cites W2076743486 @default.
- W1967339556 cites W2090199248 @default.
- W1967339556 cites W2090773418 @default.
- W1967339556 cites W2167383445 @default.
- W1967339556 doi "https://doi.org/10.1016/j.jallcom.2015.02.138" @default.
- W1967339556 hasPublicationYear "2015" @default.
- W1967339556 type Work @default.
- W1967339556 sameAs 1967339556 @default.
- W1967339556 citedByCount "18" @default.
- W1967339556 countsByYear W19673395562018 @default.
- W1967339556 countsByYear W19673395562019 @default.
- W1967339556 countsByYear W19673395562020 @default.
- W1967339556 countsByYear W19673395562021 @default.
- W1967339556 countsByYear W19673395562022 @default.
- W1967339556 crossrefType "journal-article" @default.
- W1967339556 hasAuthorship W1967339556A5006847732 @default.
- W1967339556 hasAuthorship W1967339556A5010466371 @default.
- W1967339556 hasAuthorship W1967339556A5049438734 @default.
- W1967339556 hasAuthorship W1967339556A5054399541 @default.
- W1967339556 hasAuthorship W1967339556A5054659867 @default.
- W1967339556 hasAuthorship W1967339556A5055526924 @default.
- W1967339556 hasAuthorship W1967339556A5075423250 @default.
- W1967339556 hasAuthorship W1967339556A5077357755 @default.
- W1967339556 hasConcept C178790620 @default.
- W1967339556 hasConcept C185592680 @default.
- W1967339556 hasConcept C191897082 @default.
- W1967339556 hasConcept C192562407 @default.
- W1967339556 hasConcept C2777855556 @default.
- W1967339556 hasConcept C2778329844 @default.
- W1967339556 hasConcept C2780026712 @default.
- W1967339556 hasConcept C512968161 @default.
- W1967339556 hasConcept C68044625 @default.
- W1967339556 hasConcept C87976508 @default.
- W1967339556 hasConceptScore W1967339556C178790620 @default.
- W1967339556 hasConceptScore W1967339556C185592680 @default.
- W1967339556 hasConceptScore W1967339556C191897082 @default.
- W1967339556 hasConceptScore W1967339556C192562407 @default.
- W1967339556 hasConceptScore W1967339556C2777855556 @default.
- W1967339556 hasConceptScore W1967339556C2778329844 @default.
- W1967339556 hasConceptScore W1967339556C2780026712 @default.
- W1967339556 hasConceptScore W1967339556C512968161 @default.
- W1967339556 hasConceptScore W1967339556C68044625 @default.
- W1967339556 hasConceptScore W1967339556C87976508 @default.
- W1967339556 hasFunder F4320321106 @default.
- W1967339556 hasFunder F4320335773 @default.
- W1967339556 hasLocation W19673395561 @default.
- W1967339556 hasOpenAccess W1967339556 @default.
- W1967339556 hasPrimaryLocation W19673395561 @default.
- W1967339556 hasRelatedWork W2029621844 @default.
- W1967339556 hasRelatedWork W2070306449 @default.
- W1967339556 hasRelatedWork W2085626160 @default.
- W1967339556 hasRelatedWork W2089251307 @default.
- W1967339556 hasRelatedWork W2123155170 @default.
- W1967339556 hasRelatedWork W2379115426 @default.
- W1967339556 hasRelatedWork W2379855728 @default.
- W1967339556 hasRelatedWork W2380476493 @default.
- W1967339556 hasRelatedWork W2393443368 @default.
- W1967339556 hasRelatedWork W4303926928 @default.
- W1967339556 hasVolume "636" @default.
- W1967339556 isParatext "false" @default.
- W1967339556 isRetracted "false" @default.
- W1967339556 magId "1967339556" @default.
- W1967339556 workType "article" @default.