- W1969883975 abstract "Amorphous ribbons of the composition Prx(Fe0.8B0.2)1–, 0?x?0.30, have been produced by meltspinning onto a copper wheel under argon atmosphere. The alloys were characterized thermally using a DuPont 1090 Thermal Analysis System. The crystallization onset temperature Tx, measured at a heating rate of 20 K/min, has a maximum of 899 K at x = 0.10. Tx equals 696 and 729 K for x = 0 and x = 0.30, respectively. The activation energy of crystallization of 5.4 eV for x = 0.05, dropping to 4.3 eV at x = 0.10, remaining approximately constant betwen x = 0.10 and 0.20, then dropping to 2.7 eV for x = 0.30. There is evidence that the alloys phase-separate slowly at room temperature, rapidly at elevated temperature. The magnetic moment was measured as a function of applied field at room temperature and at 4.2 K. The saturation moment decreased from 142 to 50.2 emu/gm at room temperature, and from 171.5 to 93.5 emu/gm at 4.2 K. The low temperature moments were strongly time dependent. The room temperature coercive force was too small to measure (<5 Oe)." @default.
- W1969883975 created "2016-06-24" @default.
- W1969883975 creator A5015126712 @default.
- W1969883975 creator A5015429915 @default.
- W1969883975 creator A5026403095 @default.
- W1969883975 creator A5037382486 @default.
- W1969883975 date "1982-03-01" @default.
- W1969883975 modified "2023-10-16" @default.
- W1969883975 title "Thermal and magnetic properties of amorphous Pr<sub>x</sub>(Fe<sub>0.8</sub>B<sub>0.2</sub>)<sub>1−x</sub>" @default.
- W1969883975 cites W1977831462 @default.
- W1969883975 cites W2016913493 @default.
- W1969883975 cites W2079285132 @default.
- W1969883975 doi "https://doi.org/10.1063/1.330791" @default.
- W1969883975 hasPublicationYear "1982" @default.
- W1969883975 type Work @default.
- W1969883975 sameAs 1969883975 @default.
- W1969883975 citedByCount "8" @default.
- W1969883975 crossrefType "journal-article" @default.
- W1969883975 hasAuthorship W1969883975A5015126712 @default.
- W1969883975 hasAuthorship W1969883975A5015429915 @default.
- W1969883975 hasAuthorship W1969883975A5026403095 @default.
- W1969883975 hasAuthorship W1969883975A5037382486 @default.
- W1969883975 hasConcept C113196181 @default.
- W1969883975 hasConcept C114614502 @default.
- W1969883975 hasConcept C121332964 @default.
- W1969883975 hasConcept C123266363 @default.
- W1969883975 hasConcept C126530901 @default.
- W1969883975 hasConcept C147789679 @default.
- W1969883975 hasConcept C185592680 @default.
- W1969883975 hasConcept C192562407 @default.
- W1969883975 hasConcept C203036418 @default.
- W1969883975 hasConcept C26873012 @default.
- W1969883975 hasConcept C33923547 @default.
- W1969883975 hasConcept C43617362 @default.
- W1969883975 hasConcept C54553102 @default.
- W1969883975 hasConcept C56052488 @default.
- W1969883975 hasConcept C63648874 @default.
- W1969883975 hasConcept C8010536 @default.
- W1969883975 hasConcept C82217956 @default.
- W1969883975 hasConcept C95121573 @default.
- W1969883975 hasConcept C97355855 @default.
- W1969883975 hasConcept C9930424 @default.
- W1969883975 hasConceptScore W1969883975C113196181 @default.
- W1969883975 hasConceptScore W1969883975C114614502 @default.
- W1969883975 hasConceptScore W1969883975C121332964 @default.
- W1969883975 hasConceptScore W1969883975C123266363 @default.
- W1969883975 hasConceptScore W1969883975C126530901 @default.
- W1969883975 hasConceptScore W1969883975C147789679 @default.
- W1969883975 hasConceptScore W1969883975C185592680 @default.
- W1969883975 hasConceptScore W1969883975C192562407 @default.
- W1969883975 hasConceptScore W1969883975C203036418 @default.
- W1969883975 hasConceptScore W1969883975C26873012 @default.
- W1969883975 hasConceptScore W1969883975C33923547 @default.
- W1969883975 hasConceptScore W1969883975C43617362 @default.
- W1969883975 hasConceptScore W1969883975C54553102 @default.
- W1969883975 hasConceptScore W1969883975C56052488 @default.
- W1969883975 hasConceptScore W1969883975C63648874 @default.
- W1969883975 hasConceptScore W1969883975C8010536 @default.
- W1969883975 hasConceptScore W1969883975C82217956 @default.
- W1969883975 hasConceptScore W1969883975C95121573 @default.
- W1969883975 hasConceptScore W1969883975C97355855 @default.
- W1969883975 hasConceptScore W1969883975C9930424 @default.
- W1969883975 hasIssue "3" @default.
- W1969883975 hasLocation W19698839751 @default.
- W1969883975 hasOpenAccess W1969883975 @default.
- W1969883975 hasPrimaryLocation W19698839751 @default.
- W1969883975 hasRelatedWork W1585643147 @default.
- W1969883975 hasRelatedWork W2055842878 @default.
- W1969883975 hasRelatedWork W2067250293 @default.
- W1969883975 hasRelatedWork W2075777996 @default.
- W1969883975 hasRelatedWork W2347557507 @default.
- W1969883975 hasRelatedWork W2378351669 @default.
- W1969883975 hasRelatedWork W2384695235 @default.
- W1969883975 hasRelatedWork W250751874 @default.
- W1969883975 hasRelatedWork W3137208073 @default.
- W1969883975 hasRelatedWork W292496791 @default.
- W1969883975 hasVolume "53" @default.
- W1969883975 isParatext "false" @default.
- W1969883975 isRetracted "false" @default.
- W1969883975 magId "1969883975" @default.
- W1969883975 workType "article" @default.