• W1970702905 abstract "The chemical durability of some selected glass-ceramic materials based on the Li2O- (MnO, CaO)MgOAl2O3SiO2 glass composition, has been determined by HCl, using the powder test. The leachability of the glass-ceramic was gradually increased by replacing MgO with MnO, while it was decreased by addition of MnO instead of CaO. Calcium oxide had a retarding effect on the durability of the material when it was added instead of MgO and/or MnO. However, on the addition of Al2O3 in replacing Li2O, the durability of the material was markedly improved. The leaching data were found to be dependent mainly on the proportion of the glass oxide constituents i.e. MgO/MnO, CaO/MnO and Li2O/Al2O3 ratios present in the glasses. The results were correlated to different views concerning the effect of various ions on the rate of interdiffusion between the crystalline-glass materials and leaching solution, the type, and proportions of the crystalline phases developed in glass-ceramics and residual glass phase. Die chemische Dauerhaftigkeit einiger ausgewählter Glaskeramikmaterialien, basierend auf einer Li2O-(MnO, CaO)MgOAl2O3SiO2-Glasverbindung, wurde mit Hilfe von HCl und des Pulvertests bestimmt. Die Auslaugfähigkeit der Glaskeramic konnte nach und nach erhöht werden, indem MgO durch MnO ersetzt wurde, während eine Abnahme beobachtet werden konnte, wenn MnO anstatt CaO zugegeben wurde. Kalziumoxyd erhöhte die Dauerhaftigkeit des Materials, wenn es anstelle von MgO und/oder MnO zugegeben wurde. Die Zugabe von Al2O3, um Li2O zu ersetzen, erhöhte die Dauerhaftigkeit des Materials beträchtlich. Es zeigte sich, daß die Auslaugdaten hauptsächlich von Anteil der Oxydbestandteile des Glases abhängen, d.h. von den MgO/MnO-, CaO/MnO- und Li2O/Al2O3-Verhältnissen. Die Ergebnisse wurden mit verschiedenen Betrachtungsweisen korreliert, die den Einfluß folgender Effekte beschreiben: den Einfluß unterschiedlicher Ionen auf die Interdiffusion zwischen den kristallinen Glasmaterialien und der Auslauglösung, den Effekt der Art und der Verhältnisse der sich entwickelnden kristallinen Phasen in der Glaskeramik und den Einfluß der Restglasphase. On a déterminé la résistance à l'attaque chimique de quelques vitrocéramiques ayant pour base le verre de composition Li2O- (MnO, CaO)MgOAl2O3SiO2, à l'aide du test de poudres dans HCl. Le lessivage de la vitrocéramique est augmenté lorsque l'on remplace MgO par MnO, il est par contre diminué si on remplace CaO par MnO. L'oxyde de calcium a un effet retardant sur la longévité du matériau lorsqu'il remplace MgO et/ou MnO. D'autre part, si l'on remplace Li2O par Al2O3 la longévité du matériau est sensiblement améliorée. On a constaté que les résultats des tests d'attaque dépendent surtout de la proportion des oxydes contenus dans le verre, i.e. MgO/MnO, CaO/MnO et Li2O/Al2O3. On a corrélé ces résultats aux différentes interprétations expliquant l'effet de certains ions sur la vitesse d'interdiffusion entre les verres et la solution d'attaque, et l'effet du type et de la proportion entre phases cristalline et verre amorphe présents dans ces vitrocéramiques." @default.
• W1970702905 created "2016-06-24" @default.
• W1970702905 creator A5015317937 @default.
• W1970702905 creator A5036443538 @default.
• W1970702905 date "1994-01-01" @default.
• W1970702905 modified "2023-10-18" @default.
• W1970702905 title "Characterization of glass-ceramic corrosion and durability" @default.
• W1970702905 cites W1977245303 @default.
• W1970702905 cites W1978465204 @default.
• W1970702905 cites W1990883562 @default.
• W1970702905 cites W2011492800 @default.
• W1970702905 cites W2061732296 @default.
• W1970702905 cites W2069501795 @default.
• W1970702905 cites W2077959455 @default.
• W1970702905 cites W2098229120 @default.
• W1970702905 cites W2322276021 @default.
• W1970702905 doi "https://doi.org/10.1016/0955-2219(94)90134-1" @default.
• W1970702905 hasPublicationYear "1994" @default.
• W1970702905 type Work @default.
• W1970702905 sameAs 1970702905 @default.
• W1970702905 citedByCount "5" @default.
• W1970702905 countsByYear W19707029052014 @default.
• W1970702905 crossrefType "journal-article" @default.
• W1970702905 hasAuthorship W1970702905A5015317937 @default.
• W1970702905 hasAuthorship W1970702905A5036443538 @default.
• W1970702905 hasConcept C104304963 @default.
• W1970702905 hasConcept C127413603 @default.
• W1970702905 hasConcept C134132462 @default.
• W1970702905 hasConcept C13965031 @default.
• W1970702905 hasConcept C159390177 @default.
• W1970702905 hasConcept C159750122 @default.
• W1970702905 hasConcept C159985019 @default.
• W1970702905 hasConcept C185592680 @default.
• W1970702905 hasConcept C191897082 @default.
• W1970702905 hasConcept C192562407 @default.
• W1970702905 hasConcept C199289684 @default.
• W1970702905 hasConcept C39432304 @default.
• W1970702905 hasConcept C42360764 @default.
• W1970702905 hasConcept C90982505 @default.
• W1970702905 hasConceptScore W1970702905C104304963 @default.
• W1970702905 hasConceptScore W1970702905C127413603 @default.
• W1970702905 hasConceptScore W1970702905C134132462 @default.
• W1970702905 hasConceptScore W1970702905C13965031 @default.
• W1970702905 hasConceptScore W1970702905C159390177 @default.
• W1970702905 hasConceptScore W1970702905C159750122 @default.
• W1970702905 hasConceptScore W1970702905C159985019 @default.
• W1970702905 hasConceptScore W1970702905C185592680 @default.
• W1970702905 hasConceptScore W1970702905C191897082 @default.
• W1970702905 hasConceptScore W1970702905C192562407 @default.
• W1970702905 hasConceptScore W1970702905C199289684 @default.
• W1970702905 hasConceptScore W1970702905C39432304 @default.
• W1970702905 hasConceptScore W1970702905C42360764 @default.
• W1970702905 hasConceptScore W1970702905C90982505 @default.
• W1970702905 hasIssue "6" @default.
• W1970702905 hasLocation W19707029051 @default.
• W1970702905 hasOpenAccess W1970702905 @default.
• W1970702905 hasPrimaryLocation W19707029051 @default.
• W1970702905 hasRelatedWork W1515141332 @default.
• W1970702905 hasRelatedWork W2026142536 @default.
• W1970702905 hasRelatedWork W2364319454 @default.
• W1970702905 hasRelatedWork W2367728600 @default.
• W1970702905 hasRelatedWork W2748952813 @default.
• W1970702905 hasRelatedWork W2768220118 @default.
• W1970702905 hasRelatedWork W2805770379 @default.
• W1970702905 hasRelatedWork W2899084033 @default.
• W1970702905 hasRelatedWork W4231943995 @default.
• W1970702905 hasRelatedWork W4306644717 @default.
• W1970702905 hasVolume "13" @default.
• W1970702905 isParatext "false" @default.
• W1970702905 isRetracted "false" @default.
• W1970702905 magId "1970702905" @default.
• W1970702905 workType "article" @default.