- W1971028528 abstract "Presents the results of a study of the effects of solder ball pad metallurgy, intermetallic compound (IMC) thickness and thermal cycling on the shear strengths of PBGA package solder balls. The study of the microstructures of solder balls revealed that only a very thin layer of intermetallic compound existed between solder balls and Ni or Ni alloy barrier layers immediately after ball placement and reflow. The protective Au layer was dissolved completely and a needle like AuSn 4 intermetallic compound was then formed and dispersed evenly in the solder balls. The overall thickness of the IMC layers was thicker than 15μm after storage at 150°C for 1,000 hours. During the shear tests failure occurred at the interface of the two IMC layers. The fracture surfaces of solder balls with electrolytic Ni and thick Au layers were smooth and brittle fracture was observed. The ball shear strength decreased dramatically with the formation of IMC layers. For the solder balls with electroless Ni and thin Au layers, only a single IMC layer was formed at the interface and its thickness was only 2.5 μm after storage at 150°C for 1,000 hours." @default.
- W1971028528 created "2016-06-24" @default.
- W1971028528 creator A5002933586 @default.
- W1971028528 creator A5030540135 @default.
- W1971028528 date "1999-04-01" @default.
- W1971028528 modified "2023-09-27" @default.
- W1971028528 title "Solder joint reliability of plastic ball grid array packages" @default.
- W1971028528 cites W2101602749 @default.
- W1971028528 cites W2159080175 @default.
- W1971028528 doi "https://doi.org/10.1108/09540919910254930" @default.
- W1971028528 hasPublicationYear "1999" @default.
- W1971028528 type Work @default.
- W1971028528 sameAs 1971028528 @default.
- W1971028528 citedByCount "57" @default.
- W1971028528 countsByYear W19710285282012 @default.
- W1971028528 countsByYear W19710285282013 @default.
- W1971028528 countsByYear W19710285282014 @default.
- W1971028528 countsByYear W19710285282015 @default.
- W1971028528 countsByYear W19710285282016 @default.
- W1971028528 countsByYear W19710285282018 @default.
- W1971028528 countsByYear W19710285282019 @default.
- W1971028528 crossrefType "journal-article" @default.
- W1971028528 hasAuthorship W1971028528A5002933586 @default.
- W1971028528 hasAuthorship W1971028528A5030540135 @default.
- W1971028528 hasConcept C121332964 @default.
- W1971028528 hasConcept C127893833 @default.
- W1971028528 hasConcept C136478896 @default.
- W1971028528 hasConcept C153294291 @default.
- W1971028528 hasConcept C159390177 @default.
- W1971028528 hasConcept C159750122 @default.
- W1971028528 hasConcept C159985019 @default.
- W1971028528 hasConcept C177564732 @default.
- W1971028528 hasConcept C191281628 @default.
- W1971028528 hasConcept C191897082 @default.
- W1971028528 hasConcept C192562407 @default.
- W1971028528 hasConcept C204530211 @default.
- W1971028528 hasConcept C27501479 @default.
- W1971028528 hasConcept C2780026712 @default.
- W1971028528 hasConcept C39432304 @default.
- W1971028528 hasConcept C50296614 @default.
- W1971028528 hasConcept C87976508 @default.
- W1971028528 hasConcept C94709252 @default.
- W1971028528 hasConceptScore W1971028528C121332964 @default.
- W1971028528 hasConceptScore W1971028528C127893833 @default.
- W1971028528 hasConceptScore W1971028528C136478896 @default.
- W1971028528 hasConceptScore W1971028528C153294291 @default.
- W1971028528 hasConceptScore W1971028528C159390177 @default.
- W1971028528 hasConceptScore W1971028528C159750122 @default.
- W1971028528 hasConceptScore W1971028528C159985019 @default.
- W1971028528 hasConceptScore W1971028528C177564732 @default.
- W1971028528 hasConceptScore W1971028528C191281628 @default.
- W1971028528 hasConceptScore W1971028528C191897082 @default.
- W1971028528 hasConceptScore W1971028528C192562407 @default.
- W1971028528 hasConceptScore W1971028528C204530211 @default.
- W1971028528 hasConceptScore W1971028528C27501479 @default.
- W1971028528 hasConceptScore W1971028528C2780026712 @default.
- W1971028528 hasConceptScore W1971028528C39432304 @default.
- W1971028528 hasConceptScore W1971028528C50296614 @default.
- W1971028528 hasConceptScore W1971028528C87976508 @default.
- W1971028528 hasConceptScore W1971028528C94709252 @default.
- W1971028528 hasIssue "1" @default.
- W1971028528 hasLocation W19710285281 @default.
- W1971028528 hasOpenAccess W1971028528 @default.
- W1971028528 hasPrimaryLocation W19710285281 @default.
- W1971028528 hasRelatedWork W1971659822 @default.
- W1971028528 hasRelatedWork W1988327836 @default.
- W1971028528 hasRelatedWork W1988536889 @default.
- W1971028528 hasRelatedWork W2023616436 @default.
- W1971028528 hasRelatedWork W2099142685 @default.
- W1971028528 hasRelatedWork W2290530404 @default.
- W1971028528 hasRelatedWork W2360487249 @default.
- W1971028528 hasRelatedWork W2980606179 @default.
- W1971028528 hasRelatedWork W4206915007 @default.
- W1971028528 hasRelatedWork W2556229382 @default.
- W1971028528 hasVolume "11" @default.
- W1971028528 isParatext "false" @default.
- W1971028528 isRetracted "false" @default.
- W1971028528 magId "1971028528" @default.
- W1971028528 workType "article" @default.