- W1971192336 abstract "An Fe-2%Si alloy, which was designed for electromagnetic applications was submitted to a series of plane strain compression (PSC) tests with reductions of 25, 35 and 75% at temperatures varying from 800 to 1,100°C and at a constant engineering strain rate corresponding to a constant cross velocity of 20 mm/s. The initial structure of the material displayed nearly equi-axed grains with an average size of 80 μm. The as-received texture was characterised by a nearly random cube fibre (<100>//ND) with a relatively weak maximum on the rotated cube component ({001}<110>). After deformation the samples were water quenched in order to avoid post-process static recrystallization events. The microstructures were analysed by orientation imaging microscopy (OIM) revealing that the zone of PSC was restricted to the central layers of the sample but minimally covering 50% of the sample thickness. After deformation at 800°C the conventional lamellar deformation structures were observed on the sections perpendicular to the transverse direction of PSC. At higher deformation temperatures the structure was of a bimodal nature consisting of lamellar deformation bands and equi-axed small grains. The volume fraction of these small equi-axed grains increased from 19.9% after 75%reduction at 800°C to 67.8% after 75% reduction at 1.100°C. After 75% reduction the equi-axed grains exhibited an average size of 10 μm which represents a strong grain refinement with respect to the initial size of 80 μm prior to PSC. Ferrite Silicon steels undergo extensive dynamic recovery during hot working. Dynamic recrystallization (DRX), though, has not yet been reported for these alloys although the present data suggest that a DRX mechanism might be responsible for the remarkable grain refinement after relatively low amounts of strain applied at high temperatures." @default.
- W1971192336 created "2016-06-24" @default.
- W1971192336 creator A5026052966 @default.
- W1971192336 creator A5028029199 @default.
- W1971192336 creator A5076628692 @default.
- W1971192336 creator A5084732595 @default.
- W1971192336 date "2006-01-01" @default.
- W1971192336 modified "2023-09-27" @default.
- W1971192336 title "Grain Refinement by High Temperature Plane-Strain Compression of Fe-2%Si Steel" @default.
- W1971192336 cites W2003040775 @default.
- W1971192336 cites W2007208971 @default.
- W1971192336 cites W2036746969 @default.
- W1971192336 cites W3021741684 @default.
- W1971192336 cites W4235923276 @default.
- W1971192336 doi "https://doi.org/10.4028/www.scientific.net/msf.503-504.977" @default.
- W1971192336 hasPublicationYear "2006" @default.
- W1971192336 type Work @default.
- W1971192336 sameAs 1971192336 @default.
- W1971192336 citedByCount "0" @default.
- W1971192336 crossrefType "journal-article" @default.
- W1971192336 hasAuthorship W1971192336A5026052966 @default.
- W1971192336 hasAuthorship W1971192336A5028029199 @default.
- W1971192336 hasAuthorship W1971192336A5076628692 @default.
- W1971192336 hasAuthorship W1971192336A5084732595 @default.
- W1971192336 hasConcept C149342994 @default.
- W1971192336 hasConcept C151730666 @default.
- W1971192336 hasConcept C159985019 @default.
- W1971192336 hasConcept C169010117 @default.
- W1971192336 hasConcept C172658604 @default.
- W1971192336 hasConcept C191897082 @default.
- W1971192336 hasConcept C192191005 @default.
- W1971192336 hasConcept C192562407 @default.
- W1971192336 hasConcept C195702682 @default.
- W1971192336 hasConcept C204366326 @default.
- W1971192336 hasConcept C37210646 @default.
- W1971192336 hasConcept C77851909 @default.
- W1971192336 hasConcept C86803240 @default.
- W1971192336 hasConcept C87976508 @default.
- W1971192336 hasConceptScore W1971192336C149342994 @default.
- W1971192336 hasConceptScore W1971192336C151730666 @default.
- W1971192336 hasConceptScore W1971192336C159985019 @default.
- W1971192336 hasConceptScore W1971192336C169010117 @default.
- W1971192336 hasConceptScore W1971192336C172658604 @default.
- W1971192336 hasConceptScore W1971192336C191897082 @default.
- W1971192336 hasConceptScore W1971192336C192191005 @default.
- W1971192336 hasConceptScore W1971192336C192562407 @default.
- W1971192336 hasConceptScore W1971192336C195702682 @default.
- W1971192336 hasConceptScore W1971192336C204366326 @default.
- W1971192336 hasConceptScore W1971192336C37210646 @default.
- W1971192336 hasConceptScore W1971192336C77851909 @default.
- W1971192336 hasConceptScore W1971192336C86803240 @default.
- W1971192336 hasConceptScore W1971192336C87976508 @default.
- W1971192336 hasLocation W19711923361 @default.
- W1971192336 hasOpenAccess W1971192336 @default.
- W1971192336 hasPrimaryLocation W19711923361 @default.
- W1971192336 hasRelatedWork W2043318954 @default.
- W1971192336 hasRelatedWork W2045737480 @default.
- W1971192336 hasRelatedWork W2046993283 @default.
- W1971192336 hasRelatedWork W2067805255 @default.
- W1971192336 hasRelatedWork W2083472235 @default.
- W1971192336 hasRelatedWork W2124759670 @default.
- W1971192336 hasRelatedWork W2265262747 @default.
- W1971192336 hasRelatedWork W2318605593 @default.
- W1971192336 hasRelatedWork W2473373774 @default.
- W1971192336 hasRelatedWork W2742151284 @default.
- W1971192336 hasRelatedWork W2744681551 @default.
- W1971192336 hasRelatedWork W2807183190 @default.
- W1971192336 hasRelatedWork W2912211924 @default.
- W1971192336 hasRelatedWork W2969719859 @default.
- W1971192336 hasRelatedWork W2987027637 @default.
- W1971192336 hasRelatedWork W3024349180 @default.
- W1971192336 hasRelatedWork W3042919399 @default.
- W1971192336 hasRelatedWork W3045116657 @default.
- W1971192336 hasRelatedWork W3138385420 @default.
- W1971192336 hasRelatedWork W764772755 @default.
- W1971192336 isParatext "false" @default.
- W1971192336 isRetracted "false" @default.
- W1971192336 magId "1971192336" @default.
- W1971192336 workType "article" @default.