- W1972439966 abstract "The formation of stacking fault tetrahedra in quenched gold foils was observed by transmission electron microscopy. The density of tetrahedra was found to be about 6 × 1014 cm−3 for quenches from 890°C and independent of the annealing time and temperature beyond the early stage of annealing. The growth of the tetrahedra was confirmed; their nucleation was found to be completed in the very early stages of annealing. These results imply that condensation of vacancies occurs, to some extent, during quenching and that the binding energy of a divacancy is about 0.4 eV. La formation de fautes d'empilement tétrahedrales dans des feuilles d'or trempé a été observée par microscopie électronique de transmission la densité de tétrahedrales trouvée a été d'à peu près 6 × 1014 cm−3pour les trempes à 890°C et indépendante du temps de recuit et de la température. La croissance des tétrahedrales a été confirmée; on a trouvé que leur nucléation est terminée dans les tout premiers stades du recuit. Ces résultats impliquent que la condensation de lacunes a lieu, dans une certaine mesure, durant la trempe et que l'énergie de liaison d'une bilacune est d'environ 0.4 eV. Mit Hilfe von Durchstrahlungsaufnahmen im Elektronenmikroskop wurde die Bildung von Stapelfehlertetraedern in abgeschreckten Goldfolien beobachtet. Die Dichte der Tetraeder ergab sich zu etwa 6 × 1014 cm−3 bei einer Abschrecktemperatur von 890°C, unabhängig von der Anlaβzeit und der Anlaβtemperatur. Das Wachsen der Tetraeder wurde bestätigt. Die Keimbildung wurde in den Anfangsstadien des Anlassens bereits abgeschlossen. Diese Ergebnisse deuten an, daβ Leerstellenkondensation zu einem gewissen Grade schon während des Abschreckens erfolgt und daβ die Bindungsenergie einer Doppelleerstelle etwa 0.4 eV ist." @default.
- W1972439966 created "2016-06-24" @default.
- W1972439966 creator A5034758587 @default.
- W1972439966 creator A5060551151 @default.
- W1972439966 creator A5084730219 @default.
- W1972439966 date "1964-05-01" @default.
- W1972439966 modified "2023-10-16" @default.
- W1972439966 title "Nucleation and growth of stacking fault tetrahedra in gold" @default.
- W1972439966 cites W1969479054 @default.
- W1972439966 cites W1988643450 @default.
- W1972439966 cites W2007081601 @default.
- W1972439966 cites W2014030323 @default.
- W1972439966 cites W2022186869 @default.
- W1972439966 cites W2047808297 @default.
- W1972439966 cites W2066183455 @default.
- W1972439966 cites W2066365246 @default.
- W1972439966 cites W2071444547 @default.
- W1972439966 cites W2086577822 @default.
- W1972439966 cites W2089912120 @default.
- W1972439966 cites W2093195280 @default.
- W1972439966 doi "https://doi.org/10.1016/0001-6160(64)90021-5" @default.
- W1972439966 hasPublicationYear "1964" @default.
- W1972439966 type Work @default.
- W1972439966 sameAs 1972439966 @default.
- W1972439966 citedByCount "31" @default.
- W1972439966 countsByYear W19724399662013 @default.
- W1972439966 countsByYear W19724399662014 @default.
- W1972439966 countsByYear W19724399662017 @default.
- W1972439966 crossrefType "journal-article" @default.
- W1972439966 hasAuthorship W1972439966A5034758587 @default.
- W1972439966 hasAuthorship W1972439966A5060551151 @default.
- W1972439966 hasAuthorship W1972439966A5084730219 @default.
- W1972439966 hasConcept C105239961 @default.
- W1972439966 hasConcept C121332964 @default.
- W1972439966 hasConcept C159122135 @default.
- W1972439966 hasConcept C185592680 @default.
- W1972439966 hasConcept C191897082 @default.
- W1972439966 hasConcept C192562407 @default.
- W1972439966 hasConcept C2777855556 @default.
- W1972439966 hasConcept C2778536302 @default.
- W1972439966 hasConcept C61048295 @default.
- W1972439966 hasConcept C8010536 @default.
- W1972439966 hasConcept C97355855 @default.
- W1972439966 hasConceptScore W1972439966C105239961 @default.
- W1972439966 hasConceptScore W1972439966C121332964 @default.
- W1972439966 hasConceptScore W1972439966C159122135 @default.
- W1972439966 hasConceptScore W1972439966C185592680 @default.
- W1972439966 hasConceptScore W1972439966C191897082 @default.
- W1972439966 hasConceptScore W1972439966C192562407 @default.
- W1972439966 hasConceptScore W1972439966C2777855556 @default.
- W1972439966 hasConceptScore W1972439966C2778536302 @default.
- W1972439966 hasConceptScore W1972439966C61048295 @default.
- W1972439966 hasConceptScore W1972439966C8010536 @default.
- W1972439966 hasConceptScore W1972439966C97355855 @default.
- W1972439966 hasIssue "5" @default.
- W1972439966 hasLocation W19724399661 @default.
- W1972439966 hasOpenAccess W1972439966 @default.
- W1972439966 hasPrimaryLocation W19724399661 @default.
- W1972439966 hasRelatedWork W102219307 @default.
- W1972439966 hasRelatedWork W1973867812 @default.
- W1972439966 hasRelatedWork W1976592898 @default.
- W1972439966 hasRelatedWork W2018090826 @default.
- W1972439966 hasRelatedWork W2035803209 @default.
- W1972439966 hasRelatedWork W2056714355 @default.
- W1972439966 hasRelatedWork W2091865738 @default.
- W1972439966 hasRelatedWork W2558617580 @default.
- W1972439966 hasRelatedWork W2899084033 @default.
- W1972439966 hasRelatedWork W4205510562 @default.
- W1972439966 hasVolume "12" @default.
- W1972439966 isParatext "false" @default.
- W1972439966 isRetracted "false" @default.
- W1972439966 magId "1972439966" @default.
- W1972439966 workType "article" @default.