- W1974106214 abstract "The aim of this study was to assess the influence of surface treatments on the surface characteristics of different zirconia cores and the adhesion of the zirconia-veneering ceramic systems by means of strain energy release rate (G-value, J/m(2)).Three types of zirconia cores (NANOZR (NZ), Vita In-Ceram YZ (VZ), and IPS e.max ZirCAD (IZ)) were used. The specimens were divided into four groups in each test according to the surface treatment used; Gr 1 (control; no treatment), Gr 2 (sandblasted), Gr 3 (CH2Cl2 for 60min), and Gr 4 (experimental hot etching solution for 60min). AFM, SEM, EDS, and XRD were carried out. Two types of veneering ceramics (Vita VM9 (V9) and IPS e.max Ceram (IC)) were used for testing the adhesion. The G-value (J/m(2)) was measured with a four-point bending configuration. Following fracture testing specimens were examined with SEM. Data were analyzed using ANOVA and Tukey's test.NZ treated with the experimental hot etching solution showed the highest Ra values (206.06±9.98nm) compared with the other groups (P<0.05). The greatest amount of monoclinic phase is measured after sandblasting (19.59%) for NZ, followed by VZ (9.3%) and IZ (6.6%). The NZ/V9 (etching for 60min) group showed the highest G-value (36.02±2.80J/m(2)) among the groups. Mode of failure was mostly cohesive failure within all the bonded veneering ceramic systems.The experimental hot etching solution could be considered as alternative treatment modality to sandblasting for zirconia cores to avoid phase transition at the surface from tetragonal to monoclinic that may be detrimental for the longevity of the zirconia-veneering ceramic restoration." @default.
- W1974106214 created "2016-06-24" @default.
- W1974106214 creator A5022742952 @default.
- W1974106214 date "2013-10-01" @default.
- W1974106214 modified "2023-10-18" @default.
- W1974106214 title "Influence of surface treatments on the surface properties of different zirconia cores and adhesion of zirconia-veneering ceramic systems" @default.
- W1974106214 cites W1955857136 @default.
- W1974106214 cites W1965414927 @default.
- W1974106214 cites W1972615372 @default.
- W1974106214 cites W1991204020 @default.
- W1974106214 cites W1998993695 @default.
- W1974106214 cites W2005468486 @default.
- W1974106214 cites W2014434166 @default.
- W1974106214 cites W2015558926 @default.
- W1974106214 cites W2018157405 @default.
- W1974106214 cites W2018329346 @default.
- W1974106214 cites W2019681230 @default.
- W1974106214 cites W2026442547 @default.
- W1974106214 cites W2027223120 @default.
- W1974106214 cites W2028272252 @default.
- W1974106214 cites W2028796069 @default.
- W1974106214 cites W2032820699 @default.
- W1974106214 cites W2032981902 @default.
- W1974106214 cites W2039516128 @default.
- W1974106214 cites W2052046330 @default.
- W1974106214 cites W2052893121 @default.
- W1974106214 cites W2054258711 @default.
- W1974106214 cites W2059279153 @default.
- W1974106214 cites W2065316785 @default.
- W1974106214 cites W2078356328 @default.
- W1974106214 cites W2085301003 @default.
- W1974106214 cites W2085348860 @default.
- W1974106214 cites W2087631993 @default.
- W1974106214 cites W2090435937 @default.
- W1974106214 cites W2094254683 @default.
- W1974106214 cites W2104419541 @default.
- W1974106214 cites W2109711875 @default.
- W1974106214 cites W2118268960 @default.
- W1974106214 cites W2119310097 @default.
- W1974106214 cites W2121419529 @default.
- W1974106214 cites W2124213131 @default.
- W1974106214 cites W2125555400 @default.
- W1974106214 cites W2125862839 @default.
- W1974106214 cites W2126252188 @default.
- W1974106214 cites W2129486998 @default.
- W1974106214 cites W2134449013 @default.
- W1974106214 cites W2134690201 @default.
- W1974106214 cites W2144442293 @default.
- W1974106214 cites W2156658924 @default.
- W1974106214 cites W2170180763 @default.
- W1974106214 cites W2332753550 @default.
- W1974106214 cites W4245056145 @default.
- W1974106214 cites W4361804434 @default.
- W1974106214 doi "https://doi.org/10.1016/j.dental.2013.07.003" @default.
- W1974106214 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/23899388" @default.
- W1974106214 hasPublicationYear "2013" @default.
- W1974106214 type Work @default.
- W1974106214 sameAs 1974106214 @default.
- W1974106214 citedByCount "43" @default.
- W1974106214 countsByYear W19741062142013 @default.
- W1974106214 countsByYear W19741062142014 @default.
- W1974106214 countsByYear W19741062142015 @default.
- W1974106214 countsByYear W19741062142016 @default.
- W1974106214 countsByYear W19741062142018 @default.
- W1974106214 countsByYear W19741062142019 @default.
- W1974106214 countsByYear W19741062142020 @default.
- W1974106214 countsByYear W19741062142021 @default.
- W1974106214 countsByYear W19741062142022 @default.
- W1974106214 countsByYear W19741062142023 @default.
- W1974106214 crossrefType "journal-article" @default.
- W1974106214 hasAuthorship W1974106214A5022742952 @default.
- W1974106214 hasConcept C100460472 @default.
- W1974106214 hasConcept C123609680 @default.
- W1974106214 hasConcept C127413603 @default.
- W1974106214 hasConcept C134132462 @default.
- W1974106214 hasConcept C159985019 @default.
- W1974106214 hasConcept C175708663 @default.
- W1974106214 hasConcept C178790620 @default.
- W1974106214 hasConcept C185592680 @default.
- W1974106214 hasConcept C192562407 @default.
- W1974106214 hasConcept C2779227376 @default.
- W1974106214 hasConcept C32909587 @default.
- W1974106214 hasConcept C42360764 @default.
- W1974106214 hasConcept C61276311 @default.
- W1974106214 hasConcept C84416704 @default.
- W1974106214 hasConceptScore W1974106214C100460472 @default.
- W1974106214 hasConceptScore W1974106214C123609680 @default.
- W1974106214 hasConceptScore W1974106214C127413603 @default.
- W1974106214 hasConceptScore W1974106214C134132462 @default.
- W1974106214 hasConceptScore W1974106214C159985019 @default.
- W1974106214 hasConceptScore W1974106214C175708663 @default.
- W1974106214 hasConceptScore W1974106214C178790620 @default.
- W1974106214 hasConceptScore W1974106214C185592680 @default.
- W1974106214 hasConceptScore W1974106214C192562407 @default.
- W1974106214 hasConceptScore W1974106214C2779227376 @default.
- W1974106214 hasConceptScore W1974106214C32909587 @default.
- W1974106214 hasConceptScore W1974106214C42360764 @default.
- W1974106214 hasConceptScore W1974106214C61276311 @default.