- W1974853693 abstract "The present investigation was undertaken to examine the effect of Ti undercoating on the corrosion fatigue properties of stainless steel bar coated with plasma-sprayed Al2O3. Corrosion fatigue tests were carried out under push-pull loading at a stress ratio R= -1 and at a frequency of 2 Hz. A physiological saline solution was used as corrosive environment. The fatigue strength of Ti undercoated specimen increased over the whole regime of S-N curve in comparison with that of the annealed substrate metal. Through the longitudinal section observation with a scanning electron microscope, it was revealed that Ti undercoating controlled the infiltration of a physiological saline solution to the substrate surface until 107 cycles. From the measurement of residual stress distribution by X-ray diffractometry along radial axis on the longitudinal section, it was found that the residual stress in the subsurface layer of substrate was changed from the tension to compression along radial axis and undercoat layer had compressive residual stresses in Ti undercoated specimen. In addition, it was clarified from the electrochemical experiments that Ti deposit was slightly nobler than annealed substrate metal. Consequently , it was concluded that the improvement of corrosion fatigue strength of Ti undercoated specimen was chiefly caused by both insulation effect by Ti undercoating and compressive residual stress in the subsurface layer of substrate and undercoat layer." @default.
- W1974853693 created "2016-06-24" @default.
- W1974853693 creator A5061433784 @default.
- W1974853693 creator A5070494674 @default.
- W1974853693 date "2009-01-01" @default.
- W1974853693 modified "2023-10-18" @default.
- W1974853693 title "Effect of Ti Undercoating on Fatigue Properties of Stainless Steel Coated with Plasma-sprayed Al2O3 in a Physiological Saline Solution" @default.
- W1974853693 cites W2011379752 @default.
- W1974853693 cites W2021055975 @default.
- W1974853693 cites W2049637901 @default.
- W1974853693 cites W2070099271 @default.
- W1974853693 cites W2070462534 @default.
- W1974853693 cites W2074518522 @default.
- W1974853693 cites W2081647297 @default.
- W1974853693 cites W2087250542 @default.
- W1974853693 cites W2315220483 @default.
- W1974853693 cites W2316254490 @default.
- W1974853693 cites W2316327058 @default.
- W1974853693 cites W2323973281 @default.
- W1974853693 cites W2331950625 @default.
- W1974853693 doi "https://doi.org/10.7791/jhts.35.215" @default.
- W1974853693 hasPublicationYear "2009" @default.
- W1974853693 type Work @default.
- W1974853693 sameAs 1974853693 @default.
- W1974853693 citedByCount "0" @default.
- W1974853693 crossrefType "journal-article" @default.
- W1974853693 hasAuthorship W1974853693A5061433784 @default.
- W1974853693 hasAuthorship W1974853693A5070494674 @default.
- W1974853693 hasBestOaLocation W19748536931 @default.
- W1974853693 hasConcept C111368507 @default.
- W1974853693 hasConcept C127313418 @default.
- W1974853693 hasConcept C131850400 @default.
- W1974853693 hasConcept C159985019 @default.
- W1974853693 hasConcept C191897082 @default.
- W1974853693 hasConcept C192562407 @default.
- W1974853693 hasConcept C20625102 @default.
- W1974853693 hasConcept C26771246 @default.
- W1974853693 hasConcept C2777289219 @default.
- W1974853693 hasConcept C2779227376 @default.
- W1974853693 hasConcept C30407753 @default.
- W1974853693 hasConcept C37292000 @default.
- W1974853693 hasConceptScore W1974853693C111368507 @default.
- W1974853693 hasConceptScore W1974853693C127313418 @default.
- W1974853693 hasConceptScore W1974853693C131850400 @default.
- W1974853693 hasConceptScore W1974853693C159985019 @default.
- W1974853693 hasConceptScore W1974853693C191897082 @default.
- W1974853693 hasConceptScore W1974853693C192562407 @default.
- W1974853693 hasConceptScore W1974853693C20625102 @default.
- W1974853693 hasConceptScore W1974853693C26771246 @default.
- W1974853693 hasConceptScore W1974853693C2777289219 @default.
- W1974853693 hasConceptScore W1974853693C2779227376 @default.
- W1974853693 hasConceptScore W1974853693C30407753 @default.
- W1974853693 hasConceptScore W1974853693C37292000 @default.
- W1974853693 hasIssue "4" @default.
- W1974853693 hasLocation W19748536931 @default.
- W1974853693 hasOpenAccess W1974853693 @default.
- W1974853693 hasPrimaryLocation W19748536931 @default.
- W1974853693 hasRelatedWork W1512319868 @default.
- W1974853693 hasRelatedWork W1983622139 @default.
- W1974853693 hasRelatedWork W2004362670 @default.
- W1974853693 hasRelatedWork W2351696714 @default.
- W1974853693 hasRelatedWork W2387616028 @default.
- W1974853693 hasRelatedWork W2746738132 @default.
- W1974853693 hasRelatedWork W2911369907 @default.
- W1974853693 hasRelatedWork W3097783663 @default.
- W1974853693 hasRelatedWork W4211076237 @default.
- W1974853693 hasRelatedWork W4245667518 @default.
- W1974853693 hasVolume "35" @default.
- W1974853693 isParatext "false" @default.
- W1974853693 isRetracted "false" @default.
- W1974853693 magId "1974853693" @default.
- W1974853693 workType "article" @default.