- W1975977113 abstract "Abstract The interfacial microstructure of Sn–3.0Ag–0.5Cu solder with electroless Ni/immersion Au (ENIG) was studied using SEM, EPMA and TEM. (Cu,Ni)6Sn5 intermetallic compound layer was formed at the interface between the solder and Ni–P UBM upon reflow. However, after isothermal aging the AuSn4, with a certain amount of Ni dissolved in it, i.e. (Au,Ni)Sn4 appeared above the (Cu,Ni)6Sn5 layer. Two distinctive layers, P-rich and Ni–Sn–P, were additionally found from the TEM observation. The analytical studies using EDS in TEM revealed that the averaged composition of the P-rich layer is close to that of a mixture of Ni3P and Ni, while that of the Ni–Sn–P layer is analogous to the P-rich layer but containing a small amount of Sn in it. Shear force of the flip chip solder joints decreased during aging at various temperatures. The decrease in shear force was mainly caused by the coarsening of microstructure within the solder and increase of the interfacial intermetallic compound thickness. Nearly all of the test specimens showed ductile failure mode and this could be well explained with the results of FEM analyses." @default.
- W1975977113 created "2016-06-24" @default.
- W1975977113 creator A5008796299 @default.
- W1975977113 creator A5043267942 @default.
- W1975977113 creator A5088064594 @default.
- W1975977113 date "2005-08-01" @default.
- W1975977113 modified "2023-09-24" @default.
- W1975977113 title "Effect of aging conditions on interfacial reaction and mechanical joint strength between Sn–3.0Ag–0.5Cu solder and Ni–P UBM" @default.
- W1975977113 cites W146122384 @default.
- W1975977113 cites W1967164572 @default.
- W1975977113 cites W1975393842 @default.
- W1975977113 cites W1984231444 @default.
- W1975977113 cites W1989410536 @default.
- W1975977113 cites W1999298376 @default.
- W1975977113 cites W1999776108 @default.
- W1975977113 cites W2002407670 @default.
- W1975977113 cites W2008164206 @default.
- W1975977113 cites W2017241050 @default.
- W1975977113 cites W2024127384 @default.
- W1975977113 cites W2028628640 @default.
- W1975977113 cites W2030957321 @default.
- W1975977113 cites W2059523013 @default.
- W1975977113 cites W2060126518 @default.
- W1975977113 cites W2073909902 @default.
- W1975977113 cites W2078109311 @default.
- W1975977113 cites W2089129963 @default.
- W1975977113 cites W2090123060 @default.
- W1975977113 cites W2104148881 @default.
- W1975977113 cites W2133795729 @default.
- W1975977113 cites W2133895841 @default.
- W1975977113 cites W2140571583 @default.
- W1975977113 cites W4235094066 @default.
- W1975977113 doi "https://doi.org/10.1016/j.mseb.2005.03.033" @default.
- W1975977113 hasPublicationYear "2005" @default.
- W1975977113 type Work @default.
- W1975977113 sameAs 1975977113 @default.
- W1975977113 citedByCount "45" @default.
- W1975977113 countsByYear W19759771132012 @default.
- W1975977113 countsByYear W19759771132013 @default.
- W1975977113 countsByYear W19759771132015 @default.
- W1975977113 countsByYear W19759771132016 @default.
- W1975977113 countsByYear W19759771132017 @default.
- W1975977113 countsByYear W19759771132018 @default.
- W1975977113 countsByYear W19759771132019 @default.
- W1975977113 countsByYear W19759771132020 @default.
- W1975977113 crossrefType "journal-article" @default.
- W1975977113 hasAuthorship W1975977113A5008796299 @default.
- W1975977113 hasAuthorship W1975977113A5043267942 @default.
- W1975977113 hasAuthorship W1975977113A5088064594 @default.
- W1975977113 hasConcept C127413603 @default.
- W1975977113 hasConcept C159985019 @default.
- W1975977113 hasConcept C18555067 @default.
- W1975977113 hasConcept C191897082 @default.
- W1975977113 hasConcept C192562407 @default.
- W1975977113 hasConcept C2988076202 @default.
- W1975977113 hasConcept C50296614 @default.
- W1975977113 hasConcept C66938386 @default.
- W1975977113 hasConceptScore W1975977113C127413603 @default.
- W1975977113 hasConceptScore W1975977113C159985019 @default.
- W1975977113 hasConceptScore W1975977113C18555067 @default.
- W1975977113 hasConceptScore W1975977113C191897082 @default.
- W1975977113 hasConceptScore W1975977113C192562407 @default.
- W1975977113 hasConceptScore W1975977113C2988076202 @default.
- W1975977113 hasConceptScore W1975977113C50296614 @default.
- W1975977113 hasConceptScore W1975977113C66938386 @default.
- W1975977113 hasFunder F4320322348 @default.
- W1975977113 hasIssue "3" @default.
- W1975977113 hasLocation W19759771131 @default.
- W1975977113 hasOpenAccess W1975977113 @default.
- W1975977113 hasPrimaryLocation W19759771131 @default.
- W1975977113 hasRelatedWork W2017624938 @default.
- W1975977113 hasRelatedWork W2018615395 @default.
- W1975977113 hasRelatedWork W2082293200 @default.
- W1975977113 hasRelatedWork W2094849636 @default.
- W1975977113 hasRelatedWork W2137307547 @default.
- W1975977113 hasRelatedWork W2351679394 @default.
- W1975977113 hasRelatedWork W2366790477 @default.
- W1975977113 hasRelatedWork W2380293314 @default.
- W1975977113 hasRelatedWork W2980606179 @default.
- W1975977113 hasRelatedWork W4285802202 @default.
- W1975977113 hasVolume "121" @default.
- W1975977113 isParatext "false" @default.
- W1975977113 isRetracted "false" @default.
- W1975977113 magId "1975977113" @default.
- W1975977113 workType "article" @default.