- W1976545161 abstract "Purpose The results of a study of friction welding of ductile cast iron using stainless steel interlayer are presented. Based on the microstructure evolution at the region close to the ductile cast iron‐stainless steel interface, the phenomena accompanying the process of joining were evaluated. Therefore, the purpose of this paper is to take a closer look into metallurgical phenomena accompanying the friction welding of ductile cast iron. Design/methodology/approach In this paper, ductile cast iron and austenitic‐stainless steel are welded using the friction welding method. The tensile strength of the joints was determined using a conventional tensile test machine. Moreover, the hardness across the interface ductile cast iron‐stainless steel interface was measured on a metallographic specimen. The microstructure of the joints was examined using light metallography as well as electron microscopy. In this case, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were applied. Energy Dispersive X‐ray analysis (EDS) was carried out across the section of friction welded ductile iron‐stainless steel interface. Findings On the basis of careful analysis of experimental data it was concluded that the process of friction welding was accompanied with diffusion of Cr, Ni and C atoms across the ductile cast iron‐stainless steel interface. This leads to an increase of carbon concentration in stainless steel where chromium carbides were formed, the size and distribution of which was dependent on the distance from the interface. Originality/value The main value of this paper is to contribute to the literature on friction welding of ductile cast iron." @default.
- W1976545161 created "2016-06-24" @default.
- W1976545161 creator A5019424127 @default.
- W1976545161 creator A5043316747 @default.
- W1976545161 date "2013-06-14" @default.
- W1976545161 modified "2023-10-18" @default.
- W1976545161 title "The microstructure and mass transport during friction welding of ductile cast iron" @default.
- W1976545161 cites W1729692515 @default.
- W1976545161 cites W1974309051 @default.
- W1976545161 cites W1983310999 @default.
- W1976545161 cites W1986379466 @default.
- W1976545161 cites W2004927522 @default.
- W1976545161 cites W2012252764 @default.
- W1976545161 cites W2018803699 @default.
- W1976545161 cites W2021004437 @default.
- W1976545161 cites W2036384310 @default.
- W1976545161 cites W2084987775 @default.
- W1976545161 cites W2089428552 @default.
- W1976545161 cites W4231216239 @default.
- W1976545161 cites W4246003403 @default.
- W1976545161 doi "https://doi.org/10.1108/00368791311331248" @default.
- W1976545161 hasPublicationYear "2013" @default.
- W1976545161 type Work @default.
- W1976545161 sameAs 1976545161 @default.
- W1976545161 citedByCount "9" @default.
- W1976545161 countsByYear W19765451612013 @default.
- W1976545161 countsByYear W19765451612014 @default.
- W1976545161 countsByYear W19765451612016 @default.
- W1976545161 countsByYear W19765451612017 @default.
- W1976545161 countsByYear W19765451612018 @default.
- W1976545161 countsByYear W19765451612021 @default.
- W1976545161 countsByYear W19765451612022 @default.
- W1976545161 crossrefType "journal-article" @default.
- W1976545161 hasAuthorship W1976545161A5019424127 @default.
- W1976545161 hasAuthorship W1976545161A5043316747 @default.
- W1976545161 hasConcept C112950240 @default.
- W1976545161 hasConcept C159985019 @default.
- W1976545161 hasConcept C191897082 @default.
- W1976545161 hasConcept C192562407 @default.
- W1976545161 hasConcept C19474535 @default.
- W1976545161 hasConcept C2776735967 @default.
- W1976545161 hasConcept C2779260511 @default.
- W1976545161 hasConcept C5335593 @default.
- W1976545161 hasConcept C62352918 @default.
- W1976545161 hasConcept C87976508 @default.
- W1976545161 hasConcept C96288455 @default.
- W1976545161 hasConceptScore W1976545161C112950240 @default.
- W1976545161 hasConceptScore W1976545161C159985019 @default.
- W1976545161 hasConceptScore W1976545161C191897082 @default.
- W1976545161 hasConceptScore W1976545161C192562407 @default.
- W1976545161 hasConceptScore W1976545161C19474535 @default.
- W1976545161 hasConceptScore W1976545161C2776735967 @default.
- W1976545161 hasConceptScore W1976545161C2779260511 @default.
- W1976545161 hasConceptScore W1976545161C5335593 @default.
- W1976545161 hasConceptScore W1976545161C62352918 @default.
- W1976545161 hasConceptScore W1976545161C87976508 @default.
- W1976545161 hasConceptScore W1976545161C96288455 @default.
- W1976545161 hasIssue "4" @default.
- W1976545161 hasLocation W19765451611 @default.
- W1976545161 hasOpenAccess W1976545161 @default.
- W1976545161 hasPrimaryLocation W19765451611 @default.
- W1976545161 hasRelatedWork W1983614295 @default.
- W1976545161 hasRelatedWork W2045842386 @default.
- W1976545161 hasRelatedWork W2358099038 @default.
- W1976545161 hasRelatedWork W2391620287 @default.
- W1976545161 hasRelatedWork W2493380318 @default.
- W1976545161 hasRelatedWork W2978677870 @default.
- W1976545161 hasRelatedWork W4239900904 @default.
- W1976545161 hasRelatedWork W4386397061 @default.
- W1976545161 hasRelatedWork W575189868 @default.
- W1976545161 hasRelatedWork W863272090 @default.
- W1976545161 hasVolume "65" @default.
- W1976545161 isParatext "false" @default.
- W1976545161 isRetracted "false" @default.
- W1976545161 magId "1976545161" @default.
- W1976545161 workType "article" @default.