- W1976988491 abstract "Accumulative roll-bonding process is the only severe plastic deformation (SPD) process using rolling deformation itself, and has been used for 70/30 brass up to 6 cycles at ambient temperature under unlubricated conditions. Microstructural characterizations were done by transmission electron microscopy (TEM). After 6 cycles it was found that continuous recrystallization occurred and the microstructure covered with small recrystallized grains with an average diameter below 100 nm. The tensile tests and Vickers macro- and microhardness were conducted on the ARBed 70/30 brass. A scanning electron microscopy (SEM) study was performed in order to observe the shear bands and also to clarify the failure mechanism. The tensile strength and hardness became two and three times greater than the initial value respectively. However, the elongation dropped abruptly at the first cycle, then increased slightly. Strengthening in ARBed 70/30 brass explained by strain hardening in the first step and grain refinement at high strains. Observations revealed that the failure mode in ARBed 70/30 brass was a shearing ductile rupture with elongated shallow shear dimples." @default.
- W1976988491 created "2016-06-24" @default.
- W1976988491 creator A5025045535 @default.
- W1976988491 creator A5029594559 @default.
- W1976988491 date "2010-01-01" @default.
- W1976988491 modified "2023-10-18" @default.
- W1976988491 title "Nano-grained 70/30 brass strip produced by accumulative roll-bonding (ARB) process" @default.
- W1976988491 cites W1974653847 @default.
- W1976988491 cites W1990757323 @default.
- W1976988491 cites W2007575254 @default.
- W1976988491 cites W2019883675 @default.
- W1976988491 cites W2020527961 @default.
- W1976988491 cites W2023427068 @default.
- W1976988491 cites W2032448565 @default.
- W1976988491 cites W2048909348 @default.
- W1976988491 cites W2053420827 @default.
- W1976988491 cites W2069778172 @default.
- W1976988491 cites W2070887165 @default.
- W1976988491 cites W2074046222 @default.
- W1976988491 cites W2087806948 @default.
- W1976988491 cites W2145159443 @default.
- W1976988491 cites W2169503974 @default.
- W1976988491 cites W37608986 @default.
- W1976988491 doi "https://doi.org/10.1016/j.msea.2009.09.029" @default.
- W1976988491 hasPublicationYear "2010" @default.
- W1976988491 type Work @default.
- W1976988491 sameAs 1976988491 @default.
- W1976988491 citedByCount "93" @default.
- W1976988491 countsByYear W19769884912012 @default.
- W1976988491 countsByYear W19769884912013 @default.
- W1976988491 countsByYear W19769884912014 @default.
- W1976988491 countsByYear W19769884912015 @default.
- W1976988491 countsByYear W19769884912016 @default.
- W1976988491 countsByYear W19769884912017 @default.
- W1976988491 countsByYear W19769884912018 @default.
- W1976988491 countsByYear W19769884912019 @default.
- W1976988491 countsByYear W19769884912020 @default.
- W1976988491 countsByYear W19769884912021 @default.
- W1976988491 countsByYear W19769884912022 @default.
- W1976988491 countsByYear W19769884912023 @default.
- W1976988491 crossrefType "journal-article" @default.
- W1976988491 hasAuthorship W1976988491A5025045535 @default.
- W1976988491 hasAuthorship W1976988491A5029594559 @default.
- W1976988491 hasConcept C111919701 @default.
- W1976988491 hasConcept C159985019 @default.
- W1976988491 hasConcept C191897082 @default.
- W1976988491 hasConcept C192562407 @default.
- W1976988491 hasConcept C2777777420 @default.
- W1976988491 hasConcept C2780033417 @default.
- W1976988491 hasConcept C2780357685 @default.
- W1976988491 hasConcept C41008148 @default.
- W1976988491 hasConcept C544778455 @default.
- W1976988491 hasConcept C87976508 @default.
- W1976988491 hasConcept C98045186 @default.
- W1976988491 hasConceptScore W1976988491C111919701 @default.
- W1976988491 hasConceptScore W1976988491C159985019 @default.
- W1976988491 hasConceptScore W1976988491C191897082 @default.
- W1976988491 hasConceptScore W1976988491C192562407 @default.
- W1976988491 hasConceptScore W1976988491C2777777420 @default.
- W1976988491 hasConceptScore W1976988491C2780033417 @default.
- W1976988491 hasConceptScore W1976988491C2780357685 @default.
- W1976988491 hasConceptScore W1976988491C41008148 @default.
- W1976988491 hasConceptScore W1976988491C544778455 @default.
- W1976988491 hasConceptScore W1976988491C87976508 @default.
- W1976988491 hasConceptScore W1976988491C98045186 @default.
- W1976988491 hasIssue "3" @default.
- W1976988491 hasLocation W19769884911 @default.
- W1976988491 hasOpenAccess W1976988491 @default.
- W1976988491 hasPrimaryLocation W19769884911 @default.
- W1976988491 hasRelatedWork W1964325525 @default.
- W1976988491 hasRelatedWork W1976988491 @default.
- W1976988491 hasRelatedWork W2001338098 @default.
- W1976988491 hasRelatedWork W2016304719 @default.
- W1976988491 hasRelatedWork W2314188148 @default.
- W1976988491 hasRelatedWork W2594730997 @default.
- W1976988491 hasRelatedWork W2770018496 @default.
- W1976988491 hasRelatedWork W2789346047 @default.
- W1976988491 hasRelatedWork W4297422938 @default.
- W1976988491 hasRelatedWork W4308346666 @default.
- W1976988491 hasVolume "527" @default.
- W1976988491 isParatext "false" @default.
- W1976988491 isRetracted "false" @default.
- W1976988491 magId "1976988491" @default.
- W1976988491 workType "article" @default.