• W1978244889 abstract "The latent hardening in iron single crystals was studied as a function of Burgers' vector combination, amount of prestrain, deformation temperature, and strain rate. It was found that the latent hardening ratio varies between 1.2 and 1.4, relatively independent of the afore-mentioned variables. The temperature dependence of the flow stress is higher on the latent system than on the primary system down to 77°K; but the strain rate sensitivity is similar for both systems. It is concluded that at high temperatures (above 300°K), latent hardening in iron is due to either the elastic interaction between glide and forest dislocations or the lack of mobile dislocations in the latent system or both; while at low temperatures (below 300°K) latent hardening is due to the lack of mobile dislocations in the latent system. Les auteurs ont étudié les durcissements latents des monoeristaux de fer, en fonction des combinaisons du vecteur de Burgers, des températures de déformations antérieures, du taux et de la vitesse de celles-ci. Ils ont trouvé que le rapport du durcissement varie entre 1,2 et 1,4 ce qui le rend relativement indépendant des variables mentionnées ci-dessus. L'influence de la température sur la tension de glissement est plus importante vis à vis du système de glissement secondaire que vis à vis du système de glissement primaire; cette observation se vérifie jusqu'à une température de 77°K. La sensibilité des deux systèmes de glissement vis à vis de la vitesse de déformation est identique. Les auteurs concluent qu'aux températures élevées (au dessus de 300°K) le durcissement latent résulte soit des interactions élastiques entre les dislocations mobiles dans le système de glissement latent soit, enfin, des deux raisons précitées. A basse température (au dessous de 300°K) le durcissement latent résulte du nombre trop restreint de dislocations mobiles. Die latente Verfestigung in Eisen-Einkristallen wurde in Abhängigkeit von der Kombination der Burgersvektoren, dem Betrag der Vorspannung, der Verformungstemperatur und der Verformungsgeschwindigkeit untersucht. Es stellte sich heraus, dass das latente Verfestigungsverhältnis zwischen 1,2 und 1,4 variierte und zwar relativ unabhängig von den zuvor genannten Grossen. Die Temperaturabhängigkeit der Flieβspannung ist bis hinunter zu 77°K im latenten System grosser als im primären System; der Einfluss der Verformungsgeschwindigkeit jedoch ist in beiden Systemen ähnlich. Hieraus wird geschlossen, dass bei hohen Temperaturen (über 300°K) die latente Verfestigung in Eisen entweder durch die elastische Wechselwirkung zwischen Versetzungen im Gleitsystem und Waldversetzungen, oder durch die geringe Anzahl beweglicher Versetzungen im latenten System oder durch beides verursacht wird; bei tiefen Temperaturen (unterhalb 300°K) dagegen tritt die latente Verfestigung infolge des Mangels an beweglichen Versetzungen im latenten System auf." @default.
• W1978244889 created "2016-06-24" @default.
• W1978244889 creator A5057708003 @default.
• W1978244889 creator A5028109214 @default.
• W1978244889 date "1966-08-01" @default.
• W1978244889 modified "2023-10-09" @default.
• W1978244889 title "Latent hardening in iron single crystals" @default.
• W1978244889 cites W1969144720 @default.
• W1978244889 cites W1969753015 @default.
• W1978244889 cites W1971539422 @default.
• W1978244889 cites W1972650523 @default.
• W1978244889 cites W1978413381 @default.
• W1978244889 cites W1980534009 @default.
• W1978244889 cites W1981926718 @default.
• W1978244889 cites W1984828770 @default.
• W1978244889 cites W1986491517 @default.
• W1978244889 cites W1990333404 @default.
• W1978244889 cites W2004717889 @default.
• W1978244889 cites W2007445379 @default.
• W1978244889 cites W2008454981 @default.
• W1978244889 cites W2009000423 @default.
• W1978244889 cites W2024848162 @default.
• W1978244889 cites W2027290030 @default.
• W1978244889 cites W2041390860 @default.
• W1978244889 cites W2042784964 @default.
• W1978244889 cites W2045006368 @default.
• W1978244889 cites W2055071027 @default.
• W1978244889 cites W2064049997 @default.
• W1978244889 cites W2072034838 @default.
• W1978244889 cites W2073742401 @default.
• W1978244889 cites W2074271970 @default.
• W1978244889 cites W2090080275 @default.
• W1978244889 cites W2094717561 @default.
• W1978244889 cites W2143318599 @default.
• W1978244889 cites W2314495126 @default.
• W1978244889 doi "https://doi.org/10.1016/0001-6160(66)90217-3" @default.
• W1978244889 hasPublicationYear "1966" @default.
• W1978244889 type Work @default.
• W1978244889 sameAs 1978244889 @default.
• W1978244889 citedByCount "83" @default.
• W1978244889 countsByYear W19782448892013 @default.
• W1978244889 countsByYear W19782448892014 @default.
• W1978244889 countsByYear W19782448892015 @default.
• W1978244889 countsByYear W19782448892017 @default.
• W1978244889 countsByYear W19782448892018 @default.
• W1978244889 countsByYear W19782448892019 @default.
• W1978244889 countsByYear W19782448892023 @default.
• W1978244889 crossrefType "journal-article" @default.
• W1978244889 hasAuthorship W1978244889A5028109214 @default.
• W1978244889 hasAuthorship W1978244889A5057708003 @default.
• W1978244889 hasConcept C121332964 @default.
• W1978244889 hasConcept C149342994 @default.
• W1978244889 hasConcept C156413551 @default.
• W1978244889 hasConcept C159985019 @default.
• W1978244889 hasConcept C162611839 @default.
• W1978244889 hasConcept C185592680 @default.
• W1978244889 hasConcept C191897082 @default.
• W1978244889 hasConcept C192562407 @default.
• W1978244889 hasConcept C199289684 @default.
• W1978244889 hasConcept C2779227376 @default.
• W1978244889 hasConcept C44255700 @default.
• W1978244889 hasConcept C8010536 @default.
• W1978244889 hasConcept C97355855 @default.
• W1978244889 hasConceptScore W1978244889C121332964 @default.
• W1978244889 hasConceptScore W1978244889C149342994 @default.
• W1978244889 hasConceptScore W1978244889C156413551 @default.
• W1978244889 hasConceptScore W1978244889C159985019 @default.
• W1978244889 hasConceptScore W1978244889C162611839 @default.
• W1978244889 hasConceptScore W1978244889C185592680 @default.
• W1978244889 hasConceptScore W1978244889C191897082 @default.
• W1978244889 hasConceptScore W1978244889C192562407 @default.
• W1978244889 hasConceptScore W1978244889C199289684 @default.
• W1978244889 hasConceptScore W1978244889C2779227376 @default.
• W1978244889 hasConceptScore W1978244889C44255700 @default.
• W1978244889 hasConceptScore W1978244889C8010536 @default.
• W1978244889 hasConceptScore W1978244889C97355855 @default.
• W1978244889 hasIssue "8" @default.
• W1978244889 hasLocation W19782448891 @default.
• W1978244889 hasOpenAccess W1978244889 @default.
• W1978244889 hasPrimaryLocation W19782448891 @default.
• W1978244889 hasRelatedWork W2000044286 @default.
• W1978244889 hasRelatedWork W2068728794 @default.
• W1978244889 hasRelatedWork W2159581289 @default.
• W1978244889 hasRelatedWork W2335212083 @default.
• W1978244889 hasRelatedWork W2336385494 @default.
• W1978244889 hasRelatedWork W2342500646 @default.
• W1978244889 hasRelatedWork W2362212451 @default.
• W1978244889 hasRelatedWork W2744433168 @default.
• W1978244889 hasRelatedWork W2780800405 @default.
• W1978244889 hasRelatedWork W2958985340 @default.
• W1978244889 hasVolume "14" @default.
• W1978244889 isParatext "false" @default.
• W1978244889 isRetracted "false" @default.
• W1978244889 magId "1978244889" @default.
• W1978244889 workType "article" @default.