- W1978730207 abstract "This research investigates the influence of high temperature on the properties of bricks containing non-ground granulated blast-furnace slag (GBFS) as fine aggregate replacement. Replacement percentages were 0%, 25% and 50% by dry weight of fine aggregates. The manufactured bricks were exposed to 200°С, 400°С, 600°С, and 800°С for a constant duration of two hours after 28 days of curing. Tests were conducted according to both Egyptian Standard Specifications (ESS) and American Society for Testing and Materials (ASTM) in order to determine compressive strength, absorption percentage, oven-dry weight, and ultrasound pulse velocity. Also, loss in weight was performed. Compressive strength limit regarding load-bearing units was met by mix 1 at all tested temperatures. Mixes 2 and 3, resulted in compressive strength that satisfied the requirement for load-bearing units at temperatures ranging from room temperature to 600°С.Compressive strength obtained regarding mixes 2 and 3 met the requirements of non-load bearing units at 800°С. The control mix resulted in normal weight bricks when tested at the various temperatures till 600°С. At 800°С, mixes 2 and 3 yielded light weight and medium weight bricks, respectively. There was a significant reduction in mass when comparing the mass at 800°С with the corresponding mass at room temperature concerning the three mixes. Results showed that it is feasible to partially replace fine aggregate with GBFS even when bricks are subjected to elevated temperature." @default.
- W1978730207 created "2016-06-24" @default.
- W1978730207 creator A5064583052 @default.
- W1978730207 creator A5065742422 @default.
- W1978730207 date "2014-03-01" @default.
- W1978730207 modified "2023-09-27" @default.
- W1978730207 title "Effect of High Temperature on Properties of Bricks Using Granulated Blast-Furnace Slag as Aggregate Replacement" @default.
- W1978730207 cites W1592955211 @default.
- W1978730207 cites W1977415345 @default.
- W1978730207 cites W1995443807 @default.
- W1978730207 cites W2003615651 @default.
- W1978730207 cites W2027291516 @default.
- W1978730207 cites W2039415884 @default.
- W1978730207 cites W2056945748 @default.
- W1978730207 cites W2070285478 @default.
- W1978730207 cites W2076766597 @default.
- W1978730207 cites W2088010141 @default.
- W1978730207 cites W2165547997 @default.
- W1978730207 cites W4238944084 @default.
- W1978730207 doi "https://doi.org/10.4028/www.scientific.net/kem.600.227" @default.
- W1978730207 hasPublicationYear "2014" @default.
- W1978730207 type Work @default.
- W1978730207 sameAs 1978730207 @default.
- W1978730207 citedByCount "2" @default.
- W1978730207 countsByYear W19787302072020 @default.
- W1978730207 countsByYear W19787302072022 @default.
- W1978730207 crossrefType "journal-article" @default.
- W1978730207 hasAuthorship W1978730207A5064583052 @default.
- W1978730207 hasAuthorship W1978730207A5065742422 @default.
- W1978730207 hasConcept C116628846 @default.
- W1978730207 hasConcept C132976073 @default.
- W1978730207 hasConcept C159985019 @default.
- W1978730207 hasConcept C168314062 @default.
- W1978730207 hasConcept C191897082 @default.
- W1978730207 hasConcept C192562407 @default.
- W1978730207 hasConcept C30407753 @default.
- W1978730207 hasConcept C33819350 @default.
- W1978730207 hasConcept C4679612 @default.
- W1978730207 hasConcept C523993062 @default.
- W1978730207 hasConceptScore W1978730207C116628846 @default.
- W1978730207 hasConceptScore W1978730207C132976073 @default.
- W1978730207 hasConceptScore W1978730207C159985019 @default.
- W1978730207 hasConceptScore W1978730207C168314062 @default.
- W1978730207 hasConceptScore W1978730207C191897082 @default.
- W1978730207 hasConceptScore W1978730207C192562407 @default.
- W1978730207 hasConceptScore W1978730207C30407753 @default.
- W1978730207 hasConceptScore W1978730207C33819350 @default.
- W1978730207 hasConceptScore W1978730207C4679612 @default.
- W1978730207 hasConceptScore W1978730207C523993062 @default.
- W1978730207 hasLocation W19787302071 @default.
- W1978730207 hasOpenAccess W1978730207 @default.
- W1978730207 hasPrimaryLocation W19787302071 @default.
- W1978730207 hasRelatedWork W1976627846 @default.
- W1978730207 hasRelatedWork W1980259934 @default.
- W1978730207 hasRelatedWork W2003615651 @default.
- W1978730207 hasRelatedWork W2010424955 @default.
- W1978730207 hasRelatedWork W2145916218 @default.
- W1978730207 hasRelatedWork W2203049705 @default.
- W1978730207 hasRelatedWork W2285818438 @default.
- W1978730207 hasRelatedWork W2533761395 @default.
- W1978730207 hasRelatedWork W2534790296 @default.
- W1978730207 hasRelatedWork W2602648543 @default.
- W1978730207 hasRelatedWork W2734942174 @default.
- W1978730207 hasRelatedWork W2736650369 @default.
- W1978730207 hasRelatedWork W2740544653 @default.
- W1978730207 hasRelatedWork W2776940741 @default.
- W1978730207 hasRelatedWork W2801367402 @default.
- W1978730207 hasRelatedWork W2936327519 @default.
- W1978730207 hasRelatedWork W2994040502 @default.
- W1978730207 hasRelatedWork W3006363968 @default.
- W1978730207 hasRelatedWork W3007854808 @default.
- W1978730207 hasRelatedWork W2750062608 @default.
- W1978730207 isParatext "false" @default.
- W1978730207 isRetracted "false" @default.
- W1978730207 magId "1978730207" @default.
- W1978730207 workType "article" @default.