• W1979968960 endingPage "104" @default.
• W1979968960 startingPage "88" @default.
• W1979968960 abstract "STM, STS, LEED and XPS data for crystalline θ-Al2O3 and non-crystalline Al2O3 ultra-thin films grown on NiAl(0 0 1) at 1025 K and exposed to water vapour at low pressure (1 × 10−7–1 × 10−5 mbar) and room temperature are reported. Water dissociation is observed at low pressure. This reactivity is assigned to the presence of a high density of coordinatively unsaturated cationic sites at the surface of the oxide film. The hydroxyl/hydroxide groups cannot be directly identify by their XPS binding energy, which is interpreted as resulting from the high BE positions of the oxide anions (O1s signal at 532.5–532.8 eV). However the XPS intensities give evidence of an uptake of oxygen accompanied by an increase of the surface coverage by Al3+ cations, and a decrease of the concentration in metallic Al at the alloy interface. A value of ∼2 for the oxygen to aluminium ions surface concentration ratio indicates the formation of an oxy-hydroxide (AlOxOHy with x + y ∼ 2) hydroxylation product. STM and LEED show the amorphisation and roughening of the oxide film. At P(H2O) = 1 × 10−7 mbar, only the surface of the oxide film is modified, with formation of nodules of ∼2 nm lateral size covering homogeneously the surface. STS shows that essentially the valence band is modified with an increase of the density of states at the band edge. With increasing pressure, hydroxylation is amplified, leading to an increased coverage of the alloy by oxy-hydroxide products and to the formation of larger nodules (∼7 nm) of amorphous oxy-hydroxide. Roughening and loss of the nanostructure indicate a propagation of the reaction that modifies the bulk structure of the oxide film. Amorphisation can be reverted to crystallization by annealing under UHV at 1025 K when the surface of the oxide film has been modified, but not when the bulk structure has been modified." @default.
• W1979968960 created "2016-06-24" @default.
• W1979968960 creator A5040418305 @default.
• W1979968960 creator A5065860889 @default.
• W1979968960 creator A5085329915 @default.
• W1979968960 date "2005-04-01" @default.
• W1979968960 modified "2023-09-24" @default.
• W1979968960 title "Hydroxylation-induced modifications of the Al2O3/NiAl(001) surface at low water vapour pressure" @default.
• W1979968960 cites W1535813129 @default.
• W1979968960 cites W1548350703 @default.
• W1979968960 cites W1557824800 @default.
• W1979968960 cites W1969873911 @default.
• W1979968960 cites W1975916980 @default.
• W1979968960 cites W1992487204 @default.
• W1979968960 cites W1994035711 @default.
• W1979968960 cites W1995024272 @default.
• W1979968960 cites W2003780107 @default.
• W1979968960 cites W2006786575 @default.
• W1979968960 cites W2010464631 @default.
• W1979968960 cites W2014372435 @default.
• W1979968960 cites W2015047008 @default.
• W1979968960 cites W2016477811 @default.
• W1979968960 cites W2017204959 @default.
• W1979968960 cites W2020049665 @default.
• W1979968960 cites W2021215993 @default.
• W1979968960 cites W2023679097 @default.
• W1979968960 cites W2024277189 @default.
• W1979968960 cites W2035137700 @default.
• W1979968960 cites W2035919782 @default.
• W1979968960 cites W2039488425 @default.
• W1979968960 cites W2046066344 @default.
• W1979968960 cites W2047962693 @default.
• W1979968960 cites W2048817138 @default.
• W1979968960 cites W2051254617 @default.
• W1979968960 cites W2053109846 @default.
• W1979968960 cites W2060968334 @default.
• W1979968960 cites W2061742309 @default.
• W1979968960 cites W2062109368 @default.
• W1979968960 cites W2064002302 @default.
• W1979968960 cites W2064458873 @default.
• W1979968960 cites W2074554661 @default.
• W1979968960 cites W2074771153 @default.
• W1979968960 cites W2076085552 @default.
• W1979968960 cites W2081062947 @default.
• W1979968960 cites W2084185916 @default.
• W1979968960 cites W2085256702 @default.
• W1979968960 cites W2088398154 @default.
• W1979968960 cites W2088655506 @default.
• W1979968960 cites W2088952208 @default.
• W1979968960 cites W2314349287 @default.
• W1979968960 doi "https://doi.org/10.1016/j.susc.2005.02.034" @default.
• W1979968960 hasPublicationYear "2005" @default.
• W1979968960 type Work @default.
• W1979968960 sameAs 1979968960 @default.
• W1979968960 citedByCount "69" @default.
• W1979968960 countsByYear W19799689602012 @default.
• W1979968960 countsByYear W19799689602013 @default.
• W1979968960 countsByYear W19799689602014 @default.
• W1979968960 countsByYear W19799689602015 @default.
• W1979968960 countsByYear W19799689602016 @default.
• W1979968960 countsByYear W19799689602017 @default.
• W1979968960 countsByYear W19799689602018 @default.
• W1979968960 countsByYear W19799689602019 @default.
• W1979968960 countsByYear W19799689602020 @default.
• W1979968960 countsByYear W19799689602021 @default.
• W1979968960 countsByYear W19799689602022 @default.
• W1979968960 countsByYear W19799689602023 @default.
• W1979968960 crossrefType "journal-article" @default.
• W1979968960 hasAuthorship W1979968960A5040418305 @default.
• W1979968960 hasAuthorship W1979968960A5065860889 @default.
• W1979968960 hasAuthorship W1979968960A5085329915 @default.
• W1979968960 hasConcept C113196181 @default.
• W1979968960 hasConcept C127413603 @default.
• W1979968960 hasConcept C175708663 @default.
• W1979968960 hasConcept C178790620 @default.
• W1979968960 hasConcept C179104552 @default.
• W1979968960 hasConcept C185592680 @default.
• W1979968960 hasConcept C27501479 @default.
• W1979968960 hasConcept C2775896084 @default.
• W1979968960 hasConcept C2779851234 @default.
• W1979968960 hasConcept C2780026712 @default.
• W1979968960 hasConcept C2780289051 @default.
• W1979968960 hasConcept C2780700233 @default.
• W1979968960 hasConcept C42360764 @default.
• W1979968960 hasConceptScore W1979968960C113196181 @default.
• W1979968960 hasConceptScore W1979968960C127413603 @default.
• W1979968960 hasConceptScore W1979968960C175708663 @default.
• W1979968960 hasConceptScore W1979968960C178790620 @default.
• W1979968960 hasConceptScore W1979968960C179104552 @default.
• W1979968960 hasConceptScore W1979968960C185592680 @default.
• W1979968960 hasConceptScore W1979968960C27501479 @default.
• W1979968960 hasConceptScore W1979968960C2775896084 @default.
• W1979968960 hasConceptScore W1979968960C2779851234 @default.
• W1979968960 hasConceptScore W1979968960C2780026712 @default.
• W1979968960 hasConceptScore W1979968960C2780289051 @default.
• W1979968960 hasConceptScore W1979968960C2780700233 @default.
• W1979968960 hasConceptScore W1979968960C42360764 @default.
• W1979968960 hasIssue "1" @default.

• next