• W1980147157 abstract "The structural, morphological, and optical properties of zinc sulfide (ZnS) thin films deposited using chemical bath deposition method are reported. These films were deposited on soda lime glass substrates using Na2EDTA as a complexing agent, in acidic medium at 80 °C. The effect of the pH ranging from 5 to 6.5 on quality of ZnS thin films is investigated. Irrespective of the pH values used for the deposition all films are polycrystalline with a wurtzite (hexagonal) structure. Field emission scanning electron microscopy (FE-SEM) characterization shows that the surface of the sample deposited with pH 5 and 5.5 is compact and uniform. However, agglomerated clusters (∼100 nm) are observed in ZnS thin films grown with pH above 6. X-ray photoelectron spectroscopy results shows the presence of only Zn–S bonding for the ZnS thin film grown at pH = 5 while those films deposited with pH > 5.5, Zn–OH as well as Zn–S bonding have been observed. The composition is almost stoichiometric for a wide range of pH values of the solution (5–6.5). The transmission spectrum of ZnS thin films having thickness from 30 to 220 nm indicates a good transmission characteristic with an average transmittance of 70–85%. The absorption coefficient depends on the pH values of the solution used and are responsible to the changes observed in absorption edges. The band gap energy values of ZnS thin films decreased from 3.91 to 3.78 eV with increasing pH values of the solution." @default.
• W1980147157 created "2016-06-24" @default.
• W1980147157 creator A5014549788 @default.
• W1980147157 creator A5016176080 @default.
• W1980147157 creator A5022780804 @default.
• W1980147157 creator A5049617154 @default.
• W1980147157 creator A5064427633 @default.
• W1980147157 creator A5079554524 @default.
• W1980147157 date "2010-05-01" @default.
• W1980147157 modified "2023-09-23" @default.
• W1980147157 title "Effect of pH on the characteristics of nanocrystalline ZnS thin films prepared by CBD method in acidic medium" @default.
• W1980147157 cites W1965328534 @default.
• W1980147157 cites W1974409315 @default.
• W1980147157 cites W1978493289 @default.
• W1980147157 cites W1985634307 @default.
• W1980147157 cites W1987964835 @default.
• W1980147157 cites W2004326164 @default.
• W1980147157 cites W2016130603 @default.
• W1980147157 cites W2018184532 @default.
• W1980147157 cites W2019252718 @default.
• W1980147157 cites W2025200203 @default.
• W1980147157 cites W2027943811 @default.
• W1980147157 cites W2046708567 @default.
• W1980147157 cites W2064736241 @default.
• W1980147157 cites W2065658814 @default.
• W1980147157 cites W2072682208 @default.
• W1980147157 cites W2079703616 @default.
• W1980147157 cites W2080429732 @default.
• W1980147157 cites W2081487712 @default.
• W1980147157 cites W2083356676 @default.
• W1980147157 cites W2091334897 @default.
• W1980147157 cites W2093415110 @default.
• W1980147157 doi "https://doi.org/10.1016/j.cap.2010.02.052" @default.
• W1980147157 hasPublicationYear "2010" @default.
• W1980147157 type Work @default.
• W1980147157 sameAs 1980147157 @default.
• W1980147157 citedByCount "58" @default.
• W1980147157 countsByYear W19801471572012 @default.
• W1980147157 countsByYear W19801471572013 @default.
• W1980147157 countsByYear W19801471572014 @default.
• W1980147157 countsByYear W19801471572015 @default.
• W1980147157 countsByYear W19801471572016 @default.
• W1980147157 countsByYear W19801471572017 @default.
• W1980147157 countsByYear W19801471572018 @default.
• W1980147157 countsByYear W19801471572019 @default.
• W1980147157 countsByYear W19801471572020 @default.
• W1980147157 countsByYear W19801471572021 @default.
• W1980147157 countsByYear W19801471572022 @default.
• W1980147157 countsByYear W19801471572023 @default.
• W1980147157 crossrefType "journal-article" @default.
• W1980147157 hasAuthorship W1980147157A5014549788 @default.
• W1980147157 hasAuthorship W1980147157A5016176080 @default.
• W1980147157 hasAuthorship W1980147157A5022780804 @default.
• W1980147157 hasAuthorship W1980147157A5049617154 @default.
• W1980147157 hasAuthorship W1980147157A5064427633 @default.
• W1980147157 hasAuthorship W1980147157A5079554524 @default.
• W1980147157 hasConcept C113196181 @default.
• W1980147157 hasConcept C119824511 @default.
• W1980147157 hasConcept C120665830 @default.
• W1980147157 hasConcept C121332964 @default.
• W1980147157 hasConcept C127413603 @default.
• W1980147157 hasConcept C137637335 @default.
• W1980147157 hasConcept C140676511 @default.
• W1980147157 hasConcept C144082473 @default.
• W1980147157 hasConcept C171250308 @default.
• W1980147157 hasConcept C175708663 @default.
• W1980147157 hasConcept C178790620 @default.
• W1980147157 hasConcept C181966813 @default.
• W1980147157 hasConcept C185592680 @default.
• W1980147157 hasConcept C19067145 @default.
• W1980147157 hasConcept C191897082 @default.
• W1980147157 hasConcept C192562407 @default.
• W1980147157 hasConcept C2779219880 @default.
• W1980147157 hasConcept C2780228366 @default.
• W1980147157 hasConcept C3045981 @default.
• W1980147157 hasConcept C42360764 @default.
• W1980147157 hasConcept C43617362 @default.
• W1980147157 hasConcept C49040817 @default.
• W1980147157 hasConcept C535196362 @default.
• W1980147157 hasConceptScore W1980147157C113196181 @default.
• W1980147157 hasConceptScore W1980147157C119824511 @default.
• W1980147157 hasConceptScore W1980147157C120665830 @default.
• W1980147157 hasConceptScore W1980147157C121332964 @default.
• W1980147157 hasConceptScore W1980147157C127413603 @default.
• W1980147157 hasConceptScore W1980147157C137637335 @default.
• W1980147157 hasConceptScore W1980147157C140676511 @default.
• W1980147157 hasConceptScore W1980147157C144082473 @default.
• W1980147157 hasConceptScore W1980147157C171250308 @default.
• W1980147157 hasConceptScore W1980147157C175708663 @default.
• W1980147157 hasConceptScore W1980147157C178790620 @default.
• W1980147157 hasConceptScore W1980147157C181966813 @default.
• W1980147157 hasConceptScore W1980147157C185592680 @default.
• W1980147157 hasConceptScore W1980147157C19067145 @default.
• W1980147157 hasConceptScore W1980147157C191897082 @default.
• W1980147157 hasConceptScore W1980147157C192562407 @default.
• W1980147157 hasConceptScore W1980147157C2779219880 @default.
• W1980147157 hasConceptScore W1980147157C2780228366 @default.
• W1980147157 hasConceptScore W1980147157C3045981 @default.

• next