- W1981156647 abstract "Interfacial properties and microfailure modes of carbon, SiC, and glass fibers/bismaleimide (BMI) composites were evaluated using both tensile fragmentation and compressive Broutman tests with acoustic emission (AE). Since brittle BMI is a difficult matrix to apply for the conventional fragmentation test, dual matrix composites (DMC) were applied due to their too brittleness and high modulus. By curing further from two- to three-stage, the interfacial shear strength (IFSS) between the fiber and the BMI matrix increased under both tension and compression, whereas the number of the vertical crack spacings of the BMI matrix decreased under tension. It was considered that the IFSS increased due to further progressed curing at the three-stage. The typical microfailure modes including fiber break, matrix crack, and interfacial failure were observed in tension. Due to transverse tensile stress at the interface in compression, many overlapped diagonal slippages were observed only at the broken carbon fiber ends without a BMI vertical crack. In tension, SiC and glass fibers were never broken due to their rather longer elongation to failure than carbon fiber. AE amplitudes of the brittle BMI matrix fracture were even higher than those of carbon fiber fracture in tension because of high modulus of the BMI matrix to fracture and geometrical effect due to thick rod shape. The waveform of signals coming from BMI matrix fractures in tension was consistent with AE amplitude result." @default.
- W1981156647 created "2016-06-24" @default.
- W1981156647 creator A5025316925 @default.
- W1981156647 creator A5044969414 @default.
- W1981156647 creator A5087260536 @default.
- W1981156647 date "2002-05-01" @default.
- W1981156647 modified "2023-09-26" @default.
- W1981156647 title "Interfacial evaluation and microfailure mechanisms of single carbon fiber/bismaleimide (BMI) composites by tensile and compressive fragmentation tests and acoustic emission" @default.
- W1981156647 cites W1492838719 @default.
- W1981156647 cites W1970062218 @default.
- W1981156647 cites W1970817929 @default.
- W1981156647 cites W1980568191 @default.
- W1981156647 cites W1984854101 @default.
- W1981156647 cites W2001217642 @default.
- W1981156647 cites W2006861018 @default.
- W1981156647 cites W2014258714 @default.
- W1981156647 cites W2023227606 @default.
- W1981156647 cites W2025848046 @default.
- W1981156647 cites W2029276897 @default.
- W1981156647 cites W2034395501 @default.
- W1981156647 cites W2042873311 @default.
- W1981156647 cites W2051133347 @default.
- W1981156647 cites W2056599899 @default.
- W1981156647 cites W2067758005 @default.
- W1981156647 cites W2069142783 @default.
- W1981156647 cites W2070950567 @default.
- W1981156647 cites W2072728802 @default.
- W1981156647 cites W2074301379 @default.
- W1981156647 cites W2076249607 @default.
- W1981156647 cites W2079042426 @default.
- W1981156647 cites W2080211958 @default.
- W1981156647 cites W2115021039 @default.
- W1981156647 cites W2115752220 @default.
- W1981156647 cites W2127527558 @default.
- W1981156647 cites W2141974196 @default.
- W1981156647 cites W2167568497 @default.
- W1981156647 cites W4255221148 @default.
- W1981156647 cites W73461235 @default.
- W1981156647 doi "https://doi.org/10.1016/s0266-3538(02)00050-7" @default.
- W1981156647 hasPublicationYear "2002" @default.
- W1981156647 type Work @default.
- W1981156647 sameAs 1981156647 @default.
- W1981156647 citedByCount "39" @default.
- W1981156647 countsByYear W19811566472012 @default.
- W1981156647 countsByYear W19811566472013 @default.
- W1981156647 countsByYear W19811566472014 @default.
- W1981156647 countsByYear W19811566472015 @default.
- W1981156647 countsByYear W19811566472016 @default.
- W1981156647 countsByYear W19811566472018 @default.
- W1981156647 countsByYear W19811566472019 @default.
- W1981156647 countsByYear W19811566472020 @default.
- W1981156647 countsByYear W19811566472021 @default.
- W1981156647 countsByYear W19811566472022 @default.
- W1981156647 crossrefType "journal-article" @default.
- W1981156647 hasAuthorship W1981156647A5025316925 @default.
- W1981156647 hasAuthorship W1981156647A5044969414 @default.
- W1981156647 hasAuthorship W1981156647A5087260536 @default.
- W1981156647 hasConcept C112950240 @default.
- W1981156647 hasConcept C136478896 @default.
- W1981156647 hasConcept C159985019 @default.
- W1981156647 hasConcept C174598085 @default.
- W1981156647 hasConcept C192562407 @default.
- W1981156647 hasConcept C193867417 @default.
- W1981156647 hasConcept C30407753 @default.
- W1981156647 hasConceptScore W1981156647C112950240 @default.
- W1981156647 hasConceptScore W1981156647C136478896 @default.
- W1981156647 hasConceptScore W1981156647C159985019 @default.
- W1981156647 hasConceptScore W1981156647C174598085 @default.
- W1981156647 hasConceptScore W1981156647C192562407 @default.
- W1981156647 hasConceptScore W1981156647C193867417 @default.
- W1981156647 hasConceptScore W1981156647C30407753 @default.
- W1981156647 hasIssue "6" @default.
- W1981156647 hasLocation W19811566471 @default.
- W1981156647 hasOpenAccess W1981156647 @default.
- W1981156647 hasPrimaryLocation W19811566471 @default.
- W1981156647 hasRelatedWork W1512319868 @default.
- W1981156647 hasRelatedWork W1991133037 @default.
- W1981156647 hasRelatedWork W1994122271 @default.
- W1981156647 hasRelatedWork W1999239633 @default.
- W1981156647 hasRelatedWork W2089085266 @default.
- W1981156647 hasRelatedWork W2605431086 @default.
- W1981156647 hasRelatedWork W2729932191 @default.
- W1981156647 hasRelatedWork W2767788629 @default.
- W1981156647 hasRelatedWork W2795554382 @default.
- W1981156647 hasRelatedWork W3153296539 @default.
- W1981156647 hasVolume "62" @default.
- W1981156647 isParatext "false" @default.
- W1981156647 isRetracted "false" @default.
- W1981156647 magId "1981156647" @default.
- W1981156647 workType "article" @default.