• W1982667714 abstract "Waste supernate stored in Tank 11H was analyzed periodically from May 1973-August 1975 to determine the rate of nitrite ingrowth by radiolytic decomposition of nitrate. This waste was transferred to tank 33F in accordance with TA 2-892, Rev. 1, 'Use of Cracked Tank for Fresh High Level Waste,' during the week of November 10, 1975. This letter summarizes analytical and corrosion characterization which indicate that this transfer should not increase the risk of stress corrosion cracking in F Area non-stress-relieved tanks. An interpretation of the nitrite ingrowth data is presented and used as a basis for cokncluding that the crack in Tank 11H occurred early in 1974. The formation of nitrite in waste supernate was followed for 2 1/4 years during the last filling and storage cycle in 11H. The conversion of nitrate to nitrite in the 1 1/2 year period after filling was 4.9 x 10{sup -11} mol NO{sub 2}{sup -}/{ell} BTU of fission product heat. The energy released during the period was 1.15 x 10{sup 10} BTU with a corresponding increase in nitrite of 0.56 mol/{ell}. The crack that was first observed in Tank 11H in April 1974 probably made its final penetration through the wall in March 1974 based on nitrite in-growth calculations and analyses of supernate for the NO{sub 3}{sup -}/NO{sub 2}{sup -} ratio. Analyses for {sup 137}Cs/{sup 134}Cs in the dried salt crust did not yield a definite estimate of the time of penetration because waste from high-burnup, off-site fuel made up the last 20% of the present fill. Laboratory tests indicate that the OH{sup -} (1.5M) and NO{sub 2}{sup -}(1.2M) concentrations present in Tank 11H prior to transfer to F Area should sufficient for efficient inhibition of nitrate stress corrosion cracking. Electrochemically controlled tensile tests of A285-B steel specimens in synthetic 11H supernate at 100 C showed almost no loss of mechanical properties, and there was no visible evidence of crack propagation in precracked and stressed (45 kpsi/in.) wedge opening loaded specimens after 1000 hours exposure in synthetic supernate at 97 C. These tests are more severe than the actual tank conditions; 11H supernate was about 40 C when transferred." @default.
• W1982667714 created "2016-06-24" @default.
• W1982667714 creator A5069936485 @default.
• W1982667714 date "1975-11-25" @default.
• W1982667714 modified "2023-09-27" @default.
• W1982667714 title "NITRITE INGROWTH AND STRESS CORROSION CHARACTERIZATION OF TANK 11H SUPERNATE" @default.
• W1982667714 doi "https://doi.org/10.2172/1010268" @default.
• W1982667714 hasPublicationYear "1975" @default.
• W1982667714 type Work @default.
• W1982667714 sameAs 1982667714 @default.
• W1982667714 citedByCount "1" @default.
• W1982667714 crossrefType "report" @default.
• W1982667714 hasAuthorship W1982667714A5069936485 @default.
• W1982667714 hasBestOaLocation W19826677142 @default.
• W1982667714 hasConcept C13965031 @default.
• W1982667714 hasConcept C147789679 @default.
• W1982667714 hasConcept C178790620 @default.
• W1982667714 hasConcept C185592680 @default.
• W1982667714 hasConcept C191897082 @default.
• W1982667714 hasConcept C192562407 @default.
• W1982667714 hasConcept C20625102 @default.
• W1982667714 hasConcept C2776179834 @default.
• W1982667714 hasConcept C2776384668 @default.
• W1982667714 hasConcept C2778760603 @default.
• W1982667714 hasConcept C88380143 @default.
• W1982667714 hasConceptScore W1982667714C13965031 @default.
• W1982667714 hasConceptScore W1982667714C147789679 @default.
• W1982667714 hasConceptScore W1982667714C178790620 @default.
• W1982667714 hasConceptScore W1982667714C185592680 @default.
• W1982667714 hasConceptScore W1982667714C191897082 @default.
• W1982667714 hasConceptScore W1982667714C192562407 @default.
• W1982667714 hasConceptScore W1982667714C20625102 @default.
• W1982667714 hasConceptScore W1982667714C2776179834 @default.
• W1982667714 hasConceptScore W1982667714C2776384668 @default.
• W1982667714 hasConceptScore W1982667714C2778760603 @default.
• W1982667714 hasConceptScore W1982667714C88380143 @default.
• W1982667714 hasLocation W19826677141 @default.
• W1982667714 hasLocation W19826677142 @default.
• W1982667714 hasLocation W19826677143 @default.
• W1982667714 hasOpenAccess W1982667714 @default.
• W1982667714 hasPrimaryLocation W19826677141 @default.
• W1982667714 hasRelatedWork W12318693 @default.
• W1982667714 hasRelatedWork W125182315 @default.
• W1982667714 hasRelatedWork W1489071176 @default.
• W1982667714 hasRelatedWork W1515674321 @default.
• W1982667714 hasRelatedWork W1521698548 @default.
• W1982667714 hasRelatedWork W1540099879 @default.
• W1982667714 hasRelatedWork W1586276250 @default.
• W1982667714 hasRelatedWork W1586888068 @default.
• W1982667714 hasRelatedWork W1622545369 @default.
• W1982667714 hasRelatedWork W1895366584 @default.
• W1982667714 hasRelatedWork W1990285832 @default.
• W1982667714 hasRelatedWork W2028244765 @default.
• W1982667714 hasRelatedWork W2030715868 @default.
• W1982667714 hasRelatedWork W2039757694 @default.
• W1982667714 hasRelatedWork W2146408724 @default.
• W1982667714 hasRelatedWork W2181631765 @default.
• W1982667714 hasRelatedWork W2263355262 @default.
• W1982667714 hasRelatedWork W2271445045 @default.
• W1982667714 hasRelatedWork W275576537 @default.
• W1982667714 hasRelatedWork W50573051 @default.
• W1982667714 isParatext "false" @default.
• W1982667714 isRetracted "false" @default.
• W1982667714 magId "1982667714" @default.
• W1982667714 workType "report" @default.