- W1986153909 abstract "Abstract The microstructures and tensile properties of Ti-44Al-6V-3Nb-0.3Y (at. %) alloy before and after hot rolling were investigated systematically. SEM results indicated that the as-rolled TiAl sheet was characterized by completely dynamically recrystallizated microstructures, except some refined lamellar colonies in the back end, which are primarily caused by the temperature drop during canned forging and subsequent pack rolling. By TEM analysis, the coarsening of γ lamellae by α lath decomposition during hot rolling are found. Meanwhile, by EBSD measurements, the phase composition and grain features of the as-forged and the as-rolled conditions were characterized and compared. Additionally, the tensile properties were tested to find that the room temperature tensile strength decreased obviously after hot rolling, with yield strength decreasing from 620 MPa to 520 MPa along transverse direction (TD) and to 485 MPa in rolling direction (RD), and the UTS from 680 MPa to 598 MPa and 556 MPa respectively. The reason for the degradation of the tensile strength is interpreted detailedly. After being heat-treated in single α phase field, beta phase was eliminated from current deformed TiAl alloy and the tensile properties were enhanced obviously." @default.
- W1986153909 created "2016-06-24" @default.
- W1986153909 creator A5011724802 @default.
- W1986153909 creator A5012677697 @default.
- W1986153909 creator A5036371686 @default.
- W1986153909 creator A5058288764 @default.
- W1986153909 creator A5086808716 @default.
- W1986153909 date "2012-02-01" @default.
- W1986153909 modified "2023-09-26" @default.
- W1986153909 title "Effect of pack rolling on microstructures and tensile properties of as-forged Ti-44Al-6V-3Nb-0.3Y alloy" @default.
- W1986153909 cites W1967348466 @default.
- W1986153909 cites W1976808023 @default.
- W1986153909 cites W1978483550 @default.
- W1986153909 cites W1981705479 @default.
- W1986153909 cites W1982663340 @default.
- W1986153909 cites W1986041052 @default.
- W1986153909 cites W1989884278 @default.
- W1986153909 cites W2004260220 @default.
- W1986153909 cites W2016778914 @default.
- W1986153909 cites W2022342935 @default.
- W1986153909 cites W2029900740 @default.
- W1986153909 cites W2030279526 @default.
- W1986153909 cites W2036851190 @default.
- W1986153909 cites W2037828360 @default.
- W1986153909 cites W2042081712 @default.
- W1986153909 cites W2050422257 @default.
- W1986153909 cites W2059785154 @default.
- W1986153909 cites W2062017515 @default.
- W1986153909 cites W2064650372 @default.
- W1986153909 cites W2067436926 @default.
- W1986153909 cites W2076964931 @default.
- W1986153909 cites W2078325607 @default.
- W1986153909 cites W2087692010 @default.
- W1986153909 cites W2095053704 @default.
- W1986153909 cites W2136042805 @default.
- W1986153909 cites W2315556162 @default.
- W1986153909 cites W4236840542 @default.
- W1986153909 cites W71933283 @default.
- W1986153909 doi "https://doi.org/10.1016/j.intermet.2011.10.003" @default.
- W1986153909 hasPublicationYear "2012" @default.
- W1986153909 type Work @default.
- W1986153909 sameAs 1986153909 @default.
- W1986153909 citedByCount "46" @default.
- W1986153909 countsByYear W19861539092012 @default.
- W1986153909 countsByYear W19861539092013 @default.
- W1986153909 countsByYear W19861539092014 @default.
- W1986153909 countsByYear W19861539092015 @default.
- W1986153909 countsByYear W19861539092016 @default.
- W1986153909 countsByYear W19861539092017 @default.
- W1986153909 countsByYear W19861539092018 @default.
- W1986153909 countsByYear W19861539092019 @default.
- W1986153909 countsByYear W19861539092020 @default.
- W1986153909 countsByYear W19861539092021 @default.
- W1986153909 countsByYear W19861539092022 @default.
- W1986153909 countsByYear W19861539092023 @default.
- W1986153909 crossrefType "journal-article" @default.
- W1986153909 hasAuthorship W1986153909A5011724802 @default.
- W1986153909 hasAuthorship W1986153909A5012677697 @default.
- W1986153909 hasAuthorship W1986153909A5036371686 @default.
- W1986153909 hasAuthorship W1986153909A5058288764 @default.
- W1986153909 hasAuthorship W1986153909A5086808716 @default.
- W1986153909 hasConcept C112950240 @default.
- W1986153909 hasConcept C159985019 @default.
- W1986153909 hasConcept C191897082 @default.
- W1986153909 hasConcept C192562407 @default.
- W1986153909 hasConcept C2780026712 @default.
- W1986153909 hasConcept C87976508 @default.
- W1986153909 hasConceptScore W1986153909C112950240 @default.
- W1986153909 hasConceptScore W1986153909C159985019 @default.
- W1986153909 hasConceptScore W1986153909C191897082 @default.
- W1986153909 hasConceptScore W1986153909C192562407 @default.
- W1986153909 hasConceptScore W1986153909C2780026712 @default.
- W1986153909 hasConceptScore W1986153909C87976508 @default.
- W1986153909 hasIssue "1" @default.
- W1986153909 hasLocation W19861539091 @default.
- W1986153909 hasOpenAccess W1986153909 @default.
- W1986153909 hasPrimaryLocation W19861539091 @default.
- W1986153909 hasRelatedWork W1987487801 @default.
- W1986153909 hasRelatedWork W2010733322 @default.
- W1986153909 hasRelatedWork W2058945371 @default.
- W1986153909 hasRelatedWork W2089251307 @default.
- W1986153909 hasRelatedWork W2123155170 @default.
- W1986153909 hasRelatedWork W2371235204 @default.
- W1986153909 hasRelatedWork W2379855728 @default.
- W1986153909 hasRelatedWork W4205648827 @default.
- W1986153909 hasRelatedWork W4240267549 @default.
- W1986153909 hasRelatedWork W4303926928 @default.
- W1986153909 hasVolume "21" @default.
- W1986153909 isParatext "false" @default.
- W1986153909 isRetracted "false" @default.
- W1986153909 magId "1986153909" @default.
- W1986153909 workType "article" @default.